Growth and optical properties of Hf,Ce co-doped lithium niobate crystals

In this paper, a series of Hf,Ce co-doped lithium niobate crystals with various HfO₂ concentrations were grown by Czochralski method. The ultraviolet-visible absorption spectra and the infrared transmittance spectra were measured to study defect structure of the crystals. The optical damage resistance was measured by the transmitted facula distortion method. The results showed that the optical damage resistance of Hf:Ce:LiNbO₃ was greatly improved when the Hf-doping concentration was above 4 mol%.     

Defect structure and nonvolatile hologram storage properties in Hf:Fe:Mn:LiNbO3 crystals

A series of Hf:Fe:Mn:LiNbO₃ crystals with various levels of HfO₂ doping were grown by Czochralski technique. The infrared spectra and ultraviolet spectra were measured and discussed to investigate their structure and defects. The optical damage resistance was characterized by the transmitted beam pattern distortion method. The nonvolatile two-color holographic recording experimental results showed that the recording speed was faster with the increase of HfO₂ doping concentration and at the same time little loss of nonvolatile diffraction efficiencies could be achieved.     

Defect structure and optical damage resistance of Zn:Fe:LiNbO<Subscript>3</Subscript> crystals

A series of Zn:Fe:LiNbO₃ crystals were prepared by the Czochralski technique with 0.015 wt. % Fe₂O₃ content and various concentrations of ZnO. The ultraviolet-visible absorption spectra and the infrared absorption spectra of the Zn:Fe:LiNbO₃ crystals were detected in order to investigate their defect structure. Their optical damage resistance was characterized by the photoinduced birefringence change and transmission facula distortion method. The optical damage resistance of the Zn:Fe:LiNbO₃ crystals increases remarkably when the concentration of ZnO is over its threshold concentration (more than 6.0 mol. %). The effects of defects on the optical damage resistance of the Zn:Fe:LiNbO₃ crystals are discussed in detail. Received: 25 October 2002 / Revised version: 6 January 2003 / Published online: 22 May 2003 RID="*" ID="*"Corresponding author. Fax: +86-451/2300-926, E-mail: zzxxhhdoctor@sina.com     

Structure and optical damage resistance of Zn:Mn:Fe:LiNbO3 crystals

The new non-volatile holographic storage materials, Zn:Mn:Fe:LiNbO₃ crystals, were prepared by Czochralski technique. Their microstructure was measured and analyzed by infrared (IR) transmission spectra. The optical damage resistance of Zn:Mn:Fe:LiNbO₃ crystals was characterized by the transmitted beam pattern distortion method. It increases remarkably when the concentration of ZnO is over a threshold concentration. Its value in Zn(7.0 mol%):Mn:Fe:LiNbO₃ crystal is about three orders of magnitude higher that in Mn:Fe:LiNbO₃ crystal. The photoinduced birefringence change was measured by the Sénarmont's method. It decreased with ZnO concentration increasing. The dependence of the defects on the optical damage resistance was discussed.     

The effect of In doping on optical properties of Fe:LiNBO3 crystals

Fe:LiNbO₃ and In:Fe:LiNbO₃ crystals were grown by Czochralski method. The absorption spectra were measured to investigate their defect structure. The photo damage resistance and photorefractive properties were measured. The photo damage resistance of the In:Fe:LiNbO₃ crystal in which the In concentration is above the threshold value is one order of magnitude higher than that of the Fe:LiNbO₃ crystal. The mechanisms of the violet shift of the absorption edge and the enhancement of the photorefractive effect of In:Fe:LiNbO₃ crystals were investigated.     

锂铌比对铪铁铌酸锂晶体全息存储性能的影响

以掺杂4 mol%Hf⁴⁺的LiNbO₃:Fe:Hf系列晶体（[Li]/[Nb]比变化）为研究对象,研究了系列晶体的可见吸收光谱,在632.8nm的写入光下晶体的衍射效率、灵敏度和抗光散射能力在不同[Li]/[Nb]下的变化规律.研究发现Hf⁴⁺的浓度达到阈值浓度后,随着[Li]/[Nb]比的增大,晶体的可见吸收边会发生红移,而且晶格中[Fe²⁺]/[Fe³⁺]也会增加,这就导致随着[Li]/[Nb]比的增加,样品的衍射效率逐渐减小,写入时间缩短,灵敏度增大.同时,在晶体中,随着[Li]/[Nb]的增大,陷阱中心Fe²⁺Li数量增大会使得晶体抗光散射能力减弱.     

Investigation of optical photorefractive properties of Zr:Fe:LiNbO3 crystals

A series of Zr:Fe:LiNbO₃ crystals with various levels of ZrO₂ doping were grown by Czochraski technique. The optical damage resistance and photorefractive properties were deeply explored. The results showed that the ability optical damage resistance increased remarkably when the concentration of ZrO₂ is over threshold concentration, but which is lower than that of traditional damage resistant additive MgO. While, the holographic storage properties can be greatly enhanced by proper level of ZrO₂ doping in Fe:LiNbO₃. In terms of ions' site occupation model, the photo-damage resistant ability enhancement and the change of the photorefractive properties were discussed.     

Optical damage resistance of Ce:Fe:LiNbO3 crystals with various Li/Nb ratios

Ce:Fe:LiNbO₃ crystals were grown by the Czochralski technique with various ratios of Li/Nb = 0.94, 1.05, 1.20 and 1.38 in the melt. Their UV–Vis absorption spectra were measured in order to investigate their defect structures and their optical damage resistance was characterized by the photoinduced birefringence change and transmission facual distortion method. The optical damage resistance of Ce:Fe:LiNbO₃ crystals improves with the Li/Nb ratio increases. The dependence of the optical damage resistance on the defect structure of Ce:Fe:LiNbO₃ crystals is discussed in detail.     

Preparation and holographic storage properties of tri-doped Mg:Mn:Fe:LiNbO3 crystals

Doping MgO, MnO and Fe₂O₃ in LiNbO₃ crystals, tri-doped Mg:Mn:Fe:LiNbO₃ single crystals were prepared by the conventional Czochralski method. The UV-vis absorption spectra were measured and the shift mechanism of absorption edge was also investigated in this paper. In Mg:Mn:Fe:LiNbO₃ crystal, Mn and Fe locate at the deep level and the shallow level, respectively. The two-photon holographic storage is realized in Mg:Mn:Fe:LiNbO₃ crystals by using He-Ne laser as the light source and ultraviolet as the gating light. The results indicated that the recording time can be significantly reduced for introducing Mg²⁺ in the Mg:Mn:Fe:LiNbO₃ crystal.     

Mg:Fe:LiNbO3晶体的生长及光学性能研究

在Fe:LiNbO₃中掺进MgO和Fe₂O₃以提拉技术生长Mg:Fe:LiNbO₃晶体.对晶体进行极化和还原处理.测试晶体的吸收光谱,Mg:Fe:LiNbO₃晶体吸收边相对Fe:LiNbO₃晶体发生紫移.测试晶体的红外光谱,Mg:(5 mol%)Fe:LiNbO₃晶体OH^-吸收峰由Fe:LiNbO₃晶体的3482 cm^-1移到3534 cm^-1.采用锂空位模型阐述Mg:Fe:LiNbO₃晶体,吸收边和OH-吸收峰移动的机理.测试晶体的抗光致散射能力.Mg:(5 mol%)Fe:LiNbO₃晶体抗光致散射能力比Fe:LiNbO₃晶体提高一个数量级以上.测试晶体的衍射效率和响应时间.Mg:Fe:LiNbO₃晶体响应速度比Fe:LiNbO₃晶体提高四倍.     

Mg2+对Fe:LiNbO3晶体光折变响应时间的影响

在Fe:LiNbO₃中掺进3mol%和6mol%MgO,生长了Mg:Fe:LiNbO₃晶体.测试了Mg:Fe:LiNbO₃晶体抗光致散射能力、衍射效率、响应时间和光电导.推导响应时间与光电导之间的关系.在Fe:LiNbO₃晶体中掺进6mol%的Mg²⁺,它的抗光致散射能力比Fe:LiNbO₃晶体提高一个数量级,响应速度比Fe:LiNbO₃晶体提高四倍.     

Influence of post-growth treatment on the optical properties of In:Ce:Cu:LiNbO3 crystals

Congruent In (3 mol%):Ce:Cu:LiNbO₃ crystals have been grown by the Czochralski method in air. Some crystal samples were reduced in Li₂CO₃ power, and others were oxidized in Nb₂O₅ power. The structure of crystals was studied by an infrared transmittance spectrum. The resistance ability to optical damage and the photorefractive properties were measured by light-induced scattering experiments and two-beam coupling, respectively. It has been found that the reduction treatment increased the photoconductivity , which resulted in decreased erasure time and diffraction efficiency, but higher light-induced scattering resistance ability. The oxidation treatment caused the inverse affect. Finally, the nonvolatile holographic recording in In:Ce:Cu:LiNbO3 crystals is realized.     

Spectroscopic properties of Er<Superscript>3+</Superscript> ions in LiNbO<Subscript>3</Subscript> crystals codoped with HfO<Subscript>2</Subscript>

The results of the spectroscopic analysis of transition strengths for Er³⁺ ions in a series of Hf:Er:LiNbO₃ crystals with variable Hf content and fixed Er content are reported. Unpolarized UV-VIS-NIR absorption spectra, upconversion fluorescence spectra excited at 800 nm, and microsecond time-resolved spectra excited at 400 nm and 800 nm by 800 nm femtosecond laser were measured at room temperature. The HfO₂ incorporation has influence on Er³⁺ radiative lifetimes, and fluorescence branching ratios. For Hf(4 mol %):Er(1 mol %):LiNbO₃, Ω₂=2.63×10^-20 cm², Ω₄=2.86×10^-20 cm², and Ω₆=0.72×10^-20 cm². Ω₂<Ω₄ is contrary to the Er³⁺ general trend of Ω₂>Ω₄>Ω₆ when the Hf content is below its threshold concentration. In addition, the sum of Ω increases with the Hf content when the HfO₂ content below 6 mol % is unfamiliar. The upconversion mechanism is discussed in this work. PACS 71.20.Eh; 77.84.Dy; 42.62.Fi; 42.65.Ky     

Improvement of photorefractive properties in Hf:Fe:LiNbO3 crystals with various [Li]/[Nb] ratios

Photorefractive properties of Hf:Fe:LiNbO3 crystals with various [Li]/[Nb] ratios have been investigated at 488 nm wavelength based on the two-wave coupling experiment. High diffraction efficiency and large recording sensitivity are observed and explained. The decrease in Li vacancies is suggested to be the main contributor to the increase in the photoconductivity and subsequently to the induction of the improvement of recording sensitivity. The saturation diffraction efficiency is measured up to 80.2%, and simultaneously the recording sensitivity of 0.91 cm/J is achieved to in the Hf:Fe:LiNbO3 crystal grown from the melt with the [Li]/[Nb] ratio of 1.20, which is significantly enhanced as compared with those of the Hf:Fe:LiNbO3 crystal with the [Li]/[Nb] ratio of 0.94 in melt under the same experimental conditions. Experimental results definitely show that increasing the [Li]/[Nb] ratio in crystal is an effective method for Hf:Fe:LiNbO3 crystal to improve its photorefractive properties.     

Growth and optical properties of In:Nd:LiNbO3 crystals

In, Nd double-doped LiNbO₃ (LN) crystals have been grown for the first time. Their infrared (IR) transmission spectra were measured and discussed to investigate their structure and defects. The optical damage resistance of Nd:In:LiNbO₃ crystals were characterized by straightly observing transmission facula distortion method. The optical damage resistance of In (4.0 mol%):Nd:LiNbO₃ was much higher than that of Nd:LiNbO₃. The defects were discussed in this paper to explain the optical damage resistance in the In:Nd:LiNbO₃ crystals.     

Growth and photorefractive properties of near-stoichiometric In:Fe:Cu:LiNbO3 crystals

The near-stoichiometric LiNbO₃ crystal co-doped with In₂O₃, Fe₂O₃, and CuO has been grown from a Li-rich melt (Li/Nb = 1.38, atomic ratio) by the Czochralski method in air atmosphere for the first time. The OH⁻ absorption spectra were characterized to investigate the structure defects of the crystals. The appearance of the 3506 cm⁻¹ absorption peak manifests that the composition of the grown crystal is close to the stoichiometric ratio. The photorefractive properties were also measured by the two-wave coupling experiments. The results show that the near-stoichiometric In:Fe:Cu:LiNbO₃ crystal has a larger refractive index change, higher recording sensitivity and larger two-wave coupling gain coefficient than those obtained in the congruent In:Fe:Cu:LiNbO₃ crystal under the same experimental conditions. The material of near-stoichiometric In:Fe:Cu:LiNbO₃ crystal is a promising candidate for blue photorefractive holographic recording.     

掺锌LiNbO3晶体的生长及其光学性能

在LiNbO₃中掺进3mol%、5mol%、7mol%ZnO生长Zn:LiNbO₃晶体.测试Zn:LiNbO₃晶体的吸收光谱,研究Zn:LiNbO₃晶体吸收边紫移的机制.测试Zn:LiNbO₃晶体的红外光谱,研究Zn(7mol%):LiNbO₃晶体OH 吸收峰由3484cm^-1移到3530cm^-1的机制.测试Zn:LiNbO₃晶体倍频转换效率和相位匹配温度,研究Zn:LiNbO₃晶体倍频转换效率增强的机制.     

Structure and optical damage resistance of near-stoichiometric Zn:Fe:LiNbO3 crystals

A series of near-stoichiometric Zn:Fe:LiNbO₃ crystals were grown by the high-temperature top-seed solution growth (HTTSSG) method from stoichiometric melts doped with 6 mol% K₂O. Infrared (IR) transmission spectra were measured and discussed in terms of the defect structure of the near-stoichiometric Zn:Fe:LiNbO₃ crystals. The results of the transmitted beam pattern distortion method show that the optical damage resistance of the near-stoichiometric Zn:Fe:LiNbO₃ crystals increases rapidly when the ZnO concentration exceeds a threshold value. The threshold value concentration of ZnO of the near-stoichiometric Zn:Fe:LiNbO₃ crystals is much lower than that of the congruent LiNbO₃ crystals. The dependence of the optical damage resistance on the defect structure of the near-stoichiometric Zn:Fe:LiNbO₃ crystals are discussed, and the holographic recording properties of the near-stoichiometric Zn:Fe:LiNbO₃ crystals are investigated.     

Structure and nonvolatile holographic recording of Mg:Ce:Cu:LiNbO3 crystals

A series of Mg:Ce:Cu:LiNbO₃ crystals has been grown by Czochralski method. Their infrared transmittance spectra and ultraviolet-visible absorption spectra were measured and discussed to investigate their defect structure. The nonvolatile holographic recording of Mg:Ce:Cu:LiNbO₃ crystals was characterized by the two-photon fixed method. We found that the recording time of Mg:Ce:Cu:LiNbO₃ crystals became shorter and nonvolatile diffraction efficiency decreases with the increase of Mg doping concentration, especially doping with Mg approaches and exceeds the so-called threshold. And the nonvolatility vanishes when the concentration of MgO exceeds 4 mol%. The intrinsic and extrinsic defects were discussed to explain the nonvolatile holographic properties in the Mg:Ce:Cu:LiNbO₃ crystals.     

Nonvolatile photorefractive holographic recording in Sc:Ce:Cu:LiNbO3

In this paper experimental studies of nonvolatile photorefractive holographic recording in Ce:Cu:LiNbO₃ crystals doped with Sc(0,1,2,3 mol%) were carried out. The Sc:Ce:Cu:LiNbO₃ crystals were grown by the Czochralski method and oxidized in Nb₂O₅ powders. The nonvolatile holographic recording in Sc:Ce:Cu:LiNbO₃ crystals was realized by the two-photon fixed method. We found that the recording time of Sc:Ce:Cu:LiNbO₃ crystal became shorter with the increase of Sc doping concentration, especially doping with Sc(3 mol%), which exceeds the so-called threshold, and there was little loss of nonvolatile diffraction efficiencies between Sc(3 mol%):Ce:Cu:LiNbO₃ and Ce:Cu:LiNbO₃ crystals.