Preparation,properties, and Li-ion battery application of EC + PC-modified PVdF-HFP gel polymer electrolyte films

Based on poly(vinylidene fluoride-co-hexafluoropropylene) (PVdF-HFP) and lithium tetrafluoroborate (LiBF₄) salt along with blending plasticizers, ethylene carbonate (EC) and propylene carbonate (PC), high Li-ion-conducting gel polymer electrolyte films are developed. Their properties are characterized by various techniques. The ambient temperature ionic conductivity of the 85PVdF-HFP:15LiBF₄ + 150(EC + PC) electrolyte film has a high value of 8.1 × 10^?4 S cm^?1. Its crystallinity, melting point, and electrochemical stability window are 9.5%, 115 °C, and 4.6 V, respectively. The mechanical testing shows that the Young’s modulus, yield strength, and breaking strain of this electrolyte film are 36.8 MPa, 3.4 MPa, and 320%, respectively. Lithium-ion batteries based on the gel polymer electrolyte film exhibit remarkable charge–discharge and cycling performances. The initial discharge capacity of this battery is as high as 165.1 mAh g^?1 at 0.1 C and just shows a small capacity fading of 4.8% after 120 cycles, indicating that the 85PVdF-HFP:15LiBF₄ + 150(EC + PC) system is an excellent electrolyte candidate for lithium-ion battery applications. The charge–discharge performance of the Li-ion cell fabricated with this gel polymer electrolyte film is apparently better than that of the previously reported Li-ion cells fabricated with other PVdF-HFP-based gel polymer electrolyte films.     

Field enhanced Li ion conduction in nanoferroelectric modified polymer electrolyte systems

Nanocomposite polymer electrolyte (NCPE) films based on polyethylene oxide (PEO) complexed with lithium perchlorate (LiClO₄) and nanosized ferroelectric ceramic fillers such as BaTiO₃, SrTiO3 have been prepared using solution cast technique. The films showed very good mechanical stability when exposed to ambient atmospheres for prolonged periods. Lithium ion transport studies revealed that the conductivity is predominantly ionic. The effect of electric field on ionic conductivity of NCPE films was investigated. One order enhancement in conductivity due to the field was observed at 323 K. NCPE films exhibited conductivity of 3.46?×?10^?5 Scm^?1 at 323 K. NCPE films were characterized using differential scanning calorimetry (DSC) and X-ray diffraction (XRD) technique. The DSC and XRD studies revealed reduced crystallinity which confirmed the higher amorphous phase and hence the improved ionic conductivity.     

Structural,thermal and electrical properties of polyvinyl alcohol/poly(vinyl pyrrolidone)–sodium nitrate solid polymer blend electrolyte

Sodium ion conducting solid polymer blend electrolyte thin films have been prepared by using polyvinyl alcohol (PVA)/poly(vinyl pyrrolidone) (PVP) with NaNO₃ by solution cast technique. The prepared films were characterized by various methods. The complexation of the salt with the polymer blend was identified by X-ray diffraction (XRD) and Fourier transforms infrared spectroscopy (FTIR), Differential scanning calorimetry was used to analyze the thermal behavior of the samples, and the glass transition temperature is low for the highest conducting polymer material. The scanning electron microscopy gives the surface morphology of the polymer electrolytes. The frequency and temperature dependent of electrical conductivities of the films were studied using impedance analyzer in the frequency range of 1 Hz to 1 MHz. The highest electrical conductivity of 50PVA/50PVP/2 wt% NaNO₃ concentration has been found to be 1.25 × 10^?5 S cm^?1 at room temperature. The electrical permittivity of the polymer films have been studied for various temperatures. The transference number measurements showed that the charge transport is mainly due to ions than electrons. Using this highest conducting polymer electrolyte, an electrochemical cell is fabricated and the parameters of the cells are tabulated.     

Preparation and characterization of blend polymer electrolyte film based on poly(vinyl alcohol)-poly(acrylonitrile)/MgCl<Subscript>2</Subscript> for energy storage devices

The development of magnesium electrolytes for battery applications has been the demand for electrochemical devices. To meet such demand, in this work solid blend polymer electrolytes were prepared using polyvinyl alcohol (PVA) and polyacrylonitrile (PAN) (92.5PVA:7.5PAN) as host polymer, magnesium chloride (MgCl₂) of different molar mass percentage (m.m.%) (0.1, 0.2, 0.3, 0.4, 0.5, and 0.6%) as salt and dimethylformamide (DMF) as solvent. Structural, vibrational, thermal, electrical, and electrochemical properties of the prepared electrolytes were investigated using different techniques such as X-ray diffraction pattern, FTIR spectroscopy analysis, differential scanning calorimetry (DSC), AC impedance measurement, and transference number measurement. X-ray diffraction studies confirm the minimum volume fraction of crystalline phase for the polymer electrolyte with 0.5 m.m.% of MgCl₂. FTIR confirms the complex formation between host polymer and salt. DSC analysis proves the thermal transition of the prepared films are affected by salt concentration. The optimized material with 0.5 m.m.% of MgCl₂ offers a maximum electrical conductivity of 1.01 × 10^?3 S cm^?1 at room temperature. The Mg²⁺ ion conduction in the blend polymer electrolyte is confirmed from transference number measurement. Electrochemical analysis demonstrates the promising characteristic of these polymer films suitable as electrolytes for primary magnesium batteries. Output potential and discharge characteristics have been analyzed for primary magnesium battery which is constructed using optimized conducting electrolyte.     

Preparation and characterization of biodegradable poly(ε-caprolactone)-based gel polymer electrolyte films

Biodegradable polymer electrolyte films based on poly(ε-caprolactone) (PCL) in conjunction with lithium tetrafluoroborate (LiBF₄) salt and 1-ethyl-3-methylimidazolium tetrafluoroborate (EMIMBF₄) ionic liquid were prepared by solution cast technique. The structural, morphological, thermal, and electrical properties of these films were examined using X-ray diffraction (XRD), optical microscopy (OM), differential scanning calorimetry (DSC), and impedance spectroscopy. The XRD and OM results reveal that the pure PCL possesses a semi-crystalline nature and its degree of crystallinity decreases with the addition of LiBF₄ salt and EMIMBF₄ ionic liquid. DSC analysis indicates that the melting temperature and enthalpy are apparently lower for the 40 wt% EMIMBF₄ gel polymer electrolyte as compared with the others. The ambient temperature electrical conductivity increases with increasing EMIMBF₄ concentration and reaches a high value of ～2.83?×?10^?4 S cm^?1 for the 85 PCL:15 LiBF₄ + 40 wt% EMIMBF₄ gel polymer electrolyte. The dielectric constant and ionic conductivity follow the same trend with increasing EMIMBF₄ concentration. The dominant conducting species in the 40 wt% EMIMBF₄ gel polymer electrolyte determined by Wagner’s polarization technique are ions. The ionic conductivity of this polymer electrolyte (～2.83?×?10^?4 S cm^?1) should be high enough for practical applications.     

Impedance and dielectric studies of nanocomposite polymer electrolyte systems using MMT and ferroelectric fillers

Impedance and dielectric properties of nanocomposite polymer electrolyte systems modified with nano size MMT and ferroelectric fillers have been investigated for varying lithium to oxygen ratios. The changes in the structural properties of the electrolyte samples were characterized by X-ray diffraction (XRD) and differential scanning calorimetric (DSC) technique. The ion transport number estimated by DC polarization technique is found to be between 0.86 and 0.95. The bulk conductivities of nanocomposite polymer electrolyte films were studied using impedance spectroscopic technique. The impedance plot shows high frequency semicircle, due to the bulk effect of sample and maximum ionic conductivity of 2.15 × 10⁻⁴ Scm⁻¹ was observed for (PEO)₄LiCBSM at 323 K with lithium to oxygen ratio 1: 4. The complex impedance data was used to evaluate ionic conductivity and dielectric relaxation process, to understand the ion transport mechanism in these systems.

     

Enhancement of Electrical and Optical Properties of Sodium Bromide Doped Carboxymethyl Cellulose Biopolymer Electrolyte Films

Abstract

Biodegradable ion conducting solid polymer electrolyte films of carboxymethyl cellulose (CMC) doped with sodium bromide (NaBr) with various weight percentages were prepared by a solution casting technique. Their structural, optical and electrical properties were studied by various experimental techniques in order to understand the impact of the sodium metal salt on the biopolymer CMC’s properties. The optical parameters namely the optical bandgap energy and the refractive index, showed a significant variable variation with the metal salt concentration. The maximum dc conductivity was found to be ～5.15?×?10^?4 S cm^?1 at room temperature for the sample with 20?wt% of NaBr content in the CMC matrix. The ionic conductivity and dielectric constant in general, increased with increase in metal salt content, affirming the increase in ion concentration. The calculated transference number showed that the conductivity was mainly due to ions. The increase in conductivity was due to an increase in degree of amorphousness of the polymer upon doping, as analyzed by their XRD spectra.     

Enhancement of the electrochemical properties with the effect of alkali metal systems on PEO/PVdF-HFP complex polymer electrolytes

Polymer blend electrolytes based on poly(ethylene oxide) (PEO) and poly(vinylidene fluoride-hexafluoropropylene) (PVdF-HFP) were prepared by using different lithium salts LiX (X = ClO₄, BF₄, CF₃SO₃, and N [CF₃SO₂]₂) using solution casting technique. To confirm the structure and complexation of the electrolyte films, the prepared electrolytes were subjected to X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) analysis. Alternating current (AC) impedance analysis was performed for all the electrolyte samples at various temperatures from 303 to 343 K. The result suggests that among the various lithium salts, LiN[CF₃SO₂]₂-based electrolytes exhibited the highest ionic conductivity at 8.20 × 10^?4 S/cm. The linear variation of the ionic conductivity of the polymer electrolytes with increasing temperature suggests the Arrhenius-type thermally activated process. Activation energies were found to decrease when doping with lithium imide salt. The dielectric behavior has been analyzed using dielectric permittivity (ε*), electric modulus (M*), and dissipation factor (tanδ) of the samples. Cyclic voltammetry has been performed for the electrolyte films to study their cyclability and reversibility. Thermogravimetric and differential thermal analysis (TG/DTA) was used to ascertain the thermal stability of the electrolytes, and the porous nature of the electrolytes was identified using scanning electron microscopy via ion hopping conduction. Surface morphology of the sample having maximum conductivity was studied by an atomic force microscope (AFM).     

Vibrational,electrical, and ion transport properties of PVA-LiClO<Subscript>4</Subscript>-sulfolane electrolyte with high cationic conductivity

Novel solid polymer electrolytes, poly(vinylalcohol)-lithium perchlorate (PVA-LiClO₄) and PVA-LiClO₄-sulfolane are prepared by solvent casting method. The experimental results show that sulfolane addition enhances the ionic conductivity of PVA-LiClO₄ complex by three orders. The maximum ionic conductivity of 1.14 ± 0.20 × 10^?2 S cm^?1 is achieved for 10 mol% sulfolane-added electrolyte at ambient temperature. Polymer-salt-plasticizer interactions are analyzed through attenuated total reflectance-Fourier transform infrared (ATR-FTIR) spectroscopy. Lithium ion transference number is found by AC impedance spectroscopy combined with DC potentiostatic measurements. The results confirm that sulfolane improves the Li⁺ transference number of PVA-LiClO₄ complex to 0.77 from 0.40. The electrochemical stability window of electrolytes is determined by cyclic voltammetry (CV). The broad electrochemical stability window of 5.45 V vs. lithium is obtained for maximum conducting electrolyte. All-solid-state cell is fabricated using maximum conducting electrolyte, and electrochemical impedance study is carried out. It reveals that electrolyte interfacial resistance with Li electrode is very low. The use of PVA-LiClO₄-sulfolane as a viable electrolyte material for high-voltage lithium ion batteries is ensured.     

Preparation and characterizations of PVAc/P(VdF-HFP)-based polymer blend electrolytes

A novel group of polymer blend electrolytes based on the mixture of poly(vinyl acetate) (PVAc), poly(vinylidene fluoride-hexafluoropropylene) (PVdF-HFP), and the lithium salt (LiClO₄) are prepared by solvent casting technique. Ionic conductivity of the polymer blend electrolytes has been investigated by varying the PVAc and PVdF-HFP content in the polymer matrix. The maximum ionic conductivity has been obtained as 0.527 × 10⁻⁴ Scm⁻¹ at 303 K for PVAc/PVdF-HFP ((25/75) wt.%)/LiClO₄ (8 wt.%). The complex formations ascertained from XRD and FTIR spectroscopic techniques and the thermal behavior of the prepared samples has been performed by DSC analysis. The surface morphology and the surface roughness are studied using SEM and AFM scanning techniques respectively.     

Preparation and characterization of cellulose acetate and lithium nitrate for advanced electrochemical devices

Environmental research has the objective of finding solutions to environmental degradation. To this aim, an optimized solid bio-polymer electrolyte (BPE) based on cellulose acetate (CA) with lithium nitrate (LiNO₃) has been developed to achieve the possible energy storage Li-ion batteries. CA is one of the natural polymers with very good film forming capacity. The widespread use of CA is attributed to the availability of renewable resources, non-toxic nature, low cost, and bio-compatible material. Here, we demonstrate an extremely simplest process of solution-casting technique for the development of BPE by incorporating various LiNO₃ compositions (wt.%) with bio-polymer material CA. The crystalline nature of the CA with LiNO₃ has been analyzed by X-ray diffraction (XRD) measurement. The bio-polymer-salt complex formation and the biopolymer-proton interactions have been investigated through Fourier transform infrared (FTIR) spectroscopy. Electrochemical impedance spectroscopy has been used to examine the ionic conductivity of the BPEs at room temperature (303 K). The highest ionic conductivity of 1.93 × 10^?3S/cm has been achieved for 50CA/50LiNO₃ polymer electrolyte. Electrochemical studies show that highest BPE has high electrochemical stability windows. The conducting species is found to be Li⁺ ion, which has been confirmed by transference number measurement (TNM). Primary lithium battery with discharge profile has been constructed for 50CA/50LiNO₃. This research will help to identify a new lithium ion membrane for battery technology and other electrochemical device applications.     

Conduction mechanism of lithium bis(oxalato)borate–cellulose acetate polymer gel electrolytes

Polymer gel electrolytes (PGE) belonging to salt–solvent–polymer hybrid systems are prepared using a mixture of lithium bis(oxalato)borate (LiBOB), γ-butyrolactone (γ-BL), and cellulose acetate (CA). The increase in ionic conductivity of PGE is due to the dissociation of ion aggregates, as confirmed by Fourier transform infrared analysis. The highest conductivity attained by the PGE is 7.05 mS cm^?1 at 2.4 wt.% CA. The plots of conductivity–temperature show a classical Arrhenius relationship. The electrical properties of the sample with the highest conductivity are analyzed using electrical permittivity and electric modulus formalism studies. Meanwhile, the frequency-dependent conductivity of the polymer gel electrolyte adheres to Jonscher’s power law. Conduction mechanism study also shows that the 2.4 wt.% CA PGE is in agreement with the small polaron hopping model.     

Conductivity studies of plasticized proton conducting PVA–PVIM blend doped with NH4BF4

The proton conducting solid-state polymer electrolyte comprising blend of poly(vinyl alcohol) (PVA) and poly(N-vinylimidazole) (PVIM), ammonium tetrafluoroborate (NH₄BF₄) as salt, and polyethylene glycol (PEG) (molecular weight 300 and 600) as plasticizer is prepared at various compositions by solution cast technique. The prepared films are characterized by Fourier transform infrared spectroscopy, differential scanning calorimetry, X-ray diffraction, and scanning electron microscopy analysis. The conductivity–temperature plots are found to follow an Arrhenius nature. The conductivity of solid polymer electrolytes is found to depend on salt and plasticizer content and also on the dielectric constant value and molecular weight of the plasticizer. Maximum ionic conductivity values of 2.20?×?10^?4 and 1.28?×?10^?4?S?cm^?1 at 30 °C are obtained for the system (PVA–PVIM)?+?20 wt.% NH₄BF₄?+?150 wt.% PEG300 and (PVA–PVIM)?+?20 wt.% NH₄BF₄?+?150 wt.% PEG300, respectively. The blended polymer, complexed with salt and plasticizer, is shown to be a predominantly ionic conductor. The proton transport in the system may be expected to follow Grotthuss-type mechanism.     

Lithium ion conductivity and dielectric properties of P(VdCl-co-AN-co-MMA)-LiCl-EC triblock co-polymer electrolytes

Lithium ion conducting polymer electrolytes based on triblock polymer P(VdCl-co-AN-co-MMA)–LiCl were prepared using a solution casting technique. XRD studies show that the amorphous nature of the polymer electrolyte has been increased due to the addition of LiCl. The maximum amorphous nature has been observed for 40 m% P(VdCl-co-AN-co-MMA)/60 m% LiCl samples. The FTIR study of the lithium ion conducting polymer membrane confirms the complex formation between the polymer P(VdCl-co-AN-co-MMA) and LiCl. The lithium ion conductivity is found to be 1.6 × 10^?5 Scm^?1 for the 40 m% P(VdCl-co-AN-co-MMA)/60 m% LiCl sample at room temperature. This value is found to be greater than that of pure polymer whose conductivity is found to be 1.5 × 10^?8 Scm^?1. To improve ionic conductivity, ethylene carbonate has been added as a plasticizer to the 40 m% P(VdCl-co-AN-co-MMA)/60 m% LiCl sample. When we add 0.6 m% of ethylene carbonate, it has been observed that the lithium ion conductivity has increased to 1.3 × 10^?3 Scm ^?1 . This value is two orders of magnitude greater than the 40 m% P(VdCl-co-AN-co-MMA)/60 m% LiCl sample. It is also observed from XRD patterns of 40 m% P(VdCl-co-AN-co-MMA)/60 m % LiCl/0.6 m % EC that the amorphous nature has been increased further. A dielectric study has been performed for the above membranes.     

Electrochemical performance of plasticized PEO-LiTf complex-based composite gel polymer electrolytes with the addition of barium titanate

Gel electrolytes and solid electrolytes have been reported as a potential element to slow down the polysulfide shuttle by reducing its mobility in the electrolytes. The preparation of sulfur-conductive polymer composites, or sulfur-carbon composites, has been reported as softening the impact of the shuttle effects. Unlike Li-ion batteries so far, no electrolyte is found to be optimal for Li–S batteries at all conditions. Taking into account all these factors, in the present study, an attempt has been made to develop solid polymer electrolytes in conjunction with non-aqueous liquid electrolytes along with inert fillers for Li–S batteries. Poly-ethylene oxide (PEO)-based composite gel polymer electrolytes (CGPE) comprising a combination of plasticizers, namely 1,3-dioxolane (DIOX)/tetraethylene glycol dimethylether (TEGDME) and a lithium salt (LiTf) with the addition of ceramic filler, barium titanate (BaTiO₃) have been prepared using a simple solution casting technique in an argon atmosphere. The as-prepared polymer electrolyte films were subjected to SEM, ionic conductivity, TG/DTA, and FTIR analyses. A symmetric cell composed of Li/CGPE/Li was assembled, and the variation of interfacial resistance as a function of time was also measured. The ionic conductivity was found to be increased as a function of temperature. The lithium transference number (Li_t ⁺) was measured, and the value was calculated as 0.7 which is sufficient for battery applications. The electrochemical stability window of the sample was studied by linear sweep voltammetry, and the polymer electrolyte film was found to be stable up to 5.7 V. The TG/DTA analysis reveals that this CGPE is thermally stable up to 350 °C. The compatibility studies exhibited that CGPE has better interracial properties with lithium metal anode. The interaction between the PEO and salt has been identified by an FTIR analysis.     

Tamarind seed polysaccharide biopolymer membrane for lithium-ion conducting battery

Solid biopolymers have gained much attention in the development of polymer electrolytes due to its biocompatibility, film-forming nature, and non-toxicity. In the present work, biopolymer membrane has been prepared using tamarind seed polysaccharide (TSP) as host polymer and various concentrations of lithium chloride (LiCl) salt as dopant by solution casting technique. The prepared biopolymer electrolyte has been characterized by XRD, FTIR, differential scanning calorimetry (DSC) analysis, AC impedance spectroscopy analysis, and transference number measurement. XRD analysis has been done to investigate the amorphous/crystalline nature of the polymer membrane. The highest amorphous nature has been found for 1 g of TSP with 0.4 g LiCl. FTIR spectrum analysis confirms the complex formation between TSP biopolymer with LiCl. From AC impedance conductivity analysis, the maximum ionic conductivity is of the order of 6.7?×?10^?3 S cm^?1 at room temperature for 1 g TSP with 0.4 g LiCl, whereas for pure TSP biopolymer membrane, the ionic conductivity is of the order of 5.48?×?10^?7 S cm^?1. The glass transition temperature for the highest conducting biopolymer membrane for the composition of 1 g TSP: 0.4 g LiCl has been found to be 44.25 °C using the DSC technique. Employing the maximum conducting biopolymer membrane, a lithium-ion conducting battery has been fabricated and its discharge characteristics have been studied.     

Incorporation of NH<Subscript>4</Subscript>NO<Subscript>3</Subscript> into MC-PVA blend-based polymer to prepare proton-conducting polymer electrolyte films

Proton-conducting solid polymer blend electrolytes based on methylcellulose-polyvinyl alcohol:ammonium nitrate (MC-PVA:NH₄NO₃) were prepared by the solution cast technique. The structural and electrical properties of the samples were examined by X-ray diffraction (XRD), Fourier transform infrared (FTIR), and electrical impedance (EI) spectroscopy. The shifting and change in the intensity of FTIR bands of the electrolyte samples confirm the complex formation between the MC-PVA polymer blend and the NH₄NO₃ added salt. The observed broadening in the XRD pattern of the doped samples reveals the increase of the amorphous fraction of polymer electrolyte samples. The increase in electrical conductivity of polymer electrolyte samples with increasing salt concentration attributed to the formation of charge-transfer complexes, and to increase in the amorphous domains. A maximum ionic conductivity of about 7.39 × 10^?5 S cm^?1 was achieved at room temperature for the sample incorporating 20 wt% of NH₄NO₃. The DC conductivity of the present polymer system exhibits Arrhenius-type dependence with temperature. The decrease in the values of activation energies with increasing salt concentration indicates the ease mobility of ions. The decrease in dielectric constant with increasing frequency was observed at all temperatures. Optical properties such as absorption edge, optical band gap, and tail of localized state were estimated for polymer blend and their electrolyte films. It was found that the optical band gap values shifted towards lower photon energy from 6.06 to 4.75 eV by altering the NH₄NO₃ salt content.     

AC impedance studies on proton-conducting PAN : NH4SCN polymer electrolytes

Solid polymer electrolytes based on polyacrylonitrile (PAN) doped with ammonium thiocyanate (NH₄SCN) in different molar ratios of polymer and salt have been prepared by solution-casting method using DMF as solvent. The increase in amorphous nature of the polymer electrolytes has been confirmed by XRD analysis. A shift in glass transition temperature (T _g) of the PAN?:?NH₄SCN electrolytes has been observed from the DSC thermograms which indicates the interaction between the polymer and the salt. From the AC impedance spectroscopic analysis, the ionic conductivity has been found to increase with increasing salt concentration up to 30 mol% of NH₄SCN beyond which the conductivity decreases and the highest ambient temperature conductivity has been found to be 5.79?×?10^?3 S cm^?1. The temperature-dependent conductivity of the polymer electrolyte follows an Arrhenius relationship which shows hopping of ions in the polymer matrix. The dielectric loss curves for the sample 70 mol% PAN?:?30 mol% NH₄SCN reveal the low-frequency β-relaxation peak pronounced at high temperature, and it may be caused by side group dipoles. The ionic transference number of polymer electrolyte has been estimated by Wagner’s polarization method, and the results reveal that the conductivity species are predominantly ions.     

Structural, conductivity, and dielectric characterization of PEO–PEG blend composite polymer electrolyte dispersed with TiO2 nanoparticles

A solid polymer electrolyte (SPE) composites consisting blend of poly(ethylene oxide) (PEO) and poly(ethylene glycol) (PEG) as the polymer host with LiCF₃SO₃ as a Li⁺ cation salt and TiO₂ nanoparticle which acts as a filler were prepared using solution-casting technique. The SPE films were characterized by X-ray diffraction and Fourier transform infrared analysis to ensure complexation of the polymer composites. Frequency-dependent impedance spectroscopy observation was used to determine ionic conductivity and dielectric parameters. Ionic conductivity was found to vary with increasing salt and filler particle concentrations in the polymer blend complexes. The optimum ambient temperature conductivity achieved was 2.66?×?10^?4?S?cm^?1 for PEO (65 %), PEG (15 %), LiCF₃SO₃ (15 %), ethylene carbonate (5 %), and TiO₂ (3 %) using weight percentage. The dielectric relaxation time obtained from a loss tangent plot is fairly consistent with the conductivity studies. Both Arrhenius and VTF behaviors of all the composites confirm that the conductivity mechanism of the solid polymer electrolyte is thermally activated.     

Poly(ethylene oxide)-lithium difluoro(oxalato)borate new solid polymer electrolytes: ion–polymer interaction,structural, thermal,and ionic conductivity studies

Solid polymer electrolytes based on high molecular weight poly(ethylene oxide) (PEO) complexed with lithium difluoro(oxalato)borate (LiDFOB) salt in various EO:Li molar ratios from 30:1 to 8:1 were prepared by using solution casting technique. Ion–polymer interaction, structural, thermal, and ionic conductivity studies have been reported by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), polarized optical microscopy (POM), differential scanning calorimeter (DSC), and impedance analysis. FTIR spectral studies suggested that the interaction of Li⁺ cations with the ether oxygen of PEO, where a triple peak broad band centered at 1105 cm^?1, corresponds to C–O–C stretching and extreme deformation occurs. XRD, POM, and DSC indicated that the inclusion of LiDFOB salt could reduce the crystallinity of PEO. The melting temperature of PEO shifted to lower temperature side by the addition of LiDFOB. The glass transition temperature obtained for the system 10:1 was ?38.2 °C. An increase in the ionic conductivity from 3.95?×?10^?9 to 3.18?×?10^?5 S/cm at room temperature (23 °C) was obtained through the addition of LiDFOB to a high molecular weight PEO. In addition, the ionic conductivity of the polymer electrolyte films followed an Arrhenius relation, and the activation energy decreased with increasing LiDFOB concentration.