Strained c(4 × 2) CoO(1 0 0)-like monolayer on Pd(1 0 0): Experiment and theory

We report on an interface-stabilized strained c(4 × 2) phase formed by cobalt oxide on Pd(1 0 0). The structural details and electronic properties of this oxide monolayer are elucidated by combination of scanning tunneling microscopy data, high resolution electron energy loss spectroscopy measurements and density functional theory. The c(4 × 2) periodicity is shown to arise from a rhombic array of Co vacancies, which form in a pseudomorphic CoO(1 0 0) monolayer to partially compensate for the compressive strain associated with the large lattice mismatch (～9.5%) between cobalt monoxide and the substrate. Deviation from the perfect 1:1 stoichiometry thus appears to offer a common and stable mechanism for strain release in Pd(1 0 0) supported monolayers of transition metal rocksalt monoxides of the first transition series, as very similar metal-deficient c(4 × 2) structures have been previously found for nickel and manganese oxides on the same substrate.     

Atomic and nanostructures of monolayer c(2 × 2)NiN on Cu(0 0 1)

Structures of monolayer nickel nitride (NiN) on Cu(0 0 1) surface are studied by X-ray photoelectron spectroscopy (XPS), low energy electron diffraction (LEED) and scanning tunneling microscopy (STM). Formations of Ni–N chemical bonds and NiN monolayer at the surface are confirmed by XPS on the N-adsorbed Cu(0 0 1) surfaces after Ni deposition and subsequent annealing to 670 K. A c(2 × 2) structure is always observed in the LEED patterns, which is a quite contrast to the (2 × 2)p4g structure observed usually at the N-adsorbed Ni(0 0 1) surface. Atomic images by STM indicate the mixture of Ni–N and Cu–N structures at the surface. Density of the trenches on the N-saturated surface decreases and the grid pattern on partially N-covered surfaces becomes disordered with increasing the Ni coverage. These results are attributed to the decrease of the surface compressive stress at the N-adsorbed Cu surface by mixing Ni atoms.     

Structure determination of the Cu(0 0 1)–c(4 × 4)-Sn surface by low-energy electron diffraction

Low-energy electron diffraction (LEED) have been used to determine the Cu(0 0 1)–c(4 × 4)-Sn structure formed at 300 K. It is demonstrated that a structural model suggested by scanning tunneling microscopy observations is correct: The model consists of one substitutional Sn atom and four Sn adatoms in the unit cell. Optimum parameters of the determined c(4 × 4) structure reveal that Sn adatoms laterally are displaced by 0.30 Å away from ideal fourfold-hollow sites along the 〈100〉 directions. It is proposed that such displacements of the Sn adatoms cause the formation of a network of octagonal rings on Cu(0 0 1). The substitutional Sn atom is located at each center of the octagonal rings. The formation conditions of the network are discussed.     

Chemical properties of structurally well-defined PdRu/Ru(0 0 0 1) surface alloys – Interaction with CO

The chemical properties of structurally well-defined PdRu/Ru(0 0 0 1) monolayer surface alloys [H. Hartmann, T. Diemant, A. Bergbeiter, J. Bansmann, H.E. Hoster, R.J. Behm, Surf. Sci. in press, doi:10.1016/j.sucs.2008.10.055.] and a Pd monolayer on Ru(0 0 0 1) were studied by temperature programmed desorption and infrared reflection absorption spectroscopy using CO as probe molecule. IR experiments on the PdRu/Ru(0 0 0 1) surface alloys demonstrate that CO adsorption on Ru sites resembles that on pure Ru(0 0 0 1) (on-top adsorption), while adsorption on the Pd sites occurs on both multifold coordinated and on-top sites, similar to CO on Pd(1 1 1). A significant destabilization of CO adsorption on Pd sites for both, surface alloys and the Pd monolayer film, compared to pure Pd(1 1 1) surfaces is attributed to a combination of geometric strain and vertical electronic ligand effects; an additional variation in the CO adsorption bond strength in the surface alloys is attributed to changes in the neighboring surface atom shell (lateral ligand effects). The chemical modifications introduced by PdRu surface alloy formation are compared with findings for deuterium adsorption on the same surface alloys; effects of the two-dimensional (2D) distribution of surface atoms are illustrated by comparison with CO adsorption on PtRu/Ru(0 0 0 1) surface alloys, where in contrast to the pronounced 2D phase segregation in PdRu/Ru(0 0 0 1) the surface atoms are essentially randomly distributed.     

Reversible and irreversible reactions of three oxygen precursors on InAs(0 0 1)-(4 × 2)/c(8 × 2)

The substrate reactions of three common oxygen sources for gate oxide deposition on the group III rich InAs(0 0 1)-(4 × 2)/c(8 × 2) surface are compared: water, hydrogen peroxide (HOOH), and isopropyl alcohol (IPA). Scanning tunneling microscopy reveals that surface atom displacement occurs in all cases, but via different mechanisms for each oxygen precursor. The reactions are examined as a function of post-deposition annealing temperature. Water reaction shows displacement of surface As atoms, but it does not fully oxidize the As; the reaction is reversed by high temperature (450 °C) annealing. Exposure to IPA and subsequent low-temperature annealing (100 °C) show the preferential reaction on the row features of InAs(0 0 1)-(4 × 2)/c(8 × 2), but higher temperature anneals result in permanent surface atom displacement/etching. Etching of the substrate is observed with HOOH exposure for all annealing temperatures. While nearly all oxidation reactions on group IV semiconductors are irreversible, the group III rich surface of InAs(0 0 1) shows that oxidation displacement reactions can be reversible at low temperature, thereby providing a mechanism of self-healing during oxidation reactions.     

Topmost-surface-sensitive Si-2p photoelectron spectra of clean Si(1 0 0)-2 × 1 measured with photoelectron Auger coincidence spectroscopy

Topmost-surface-sensitive Si-2p photoelectron spectra of a clean Si(1 0 0)-2 × 1 surface have been measured using Si-2p photoelectron Si-L₂₃VV Auger coincidence spectroscopy (Si-2p–Si-L₂₃VV PEACS). The escape depth of the PEACS electrons is estimated to be ～1.2 Å. The results support the assignments of the Si up-atoms, the Si down-atoms, the Si 2nd-layer, and the Si bulk proposed in previous researches. The Si-2p component with a binding energy of ?0.23 eV relative to the bulk Si-2p_3/2 peak, is shown to originate mainly from the topmost surface. Site selectivity of PEACS is indicated to be achieved to some degree by carefully selecting the kinetic energy of the Auger electrons. Since PEACS can be applied to any surface, the present study opens a new approach to identify PES components.     

Selective adsorption of coronene on Si(1 1 1)-(7 × 7)

The adsorption of coronene (C₂₄H₁₂) on the Si(1 1 1)-(7 × 7) surface is studied using scanning tunneling microscopy (STM). Upon room temperature submonolayer deposition, we find that the coronene molecules preferentially adsorb on the unfaulted half of the 7 × 7 unit cell. Molecules adsorbed on different sites can be induced to move to the preferential sites by the action of the tip in repeated image scans. Imaging of the molecules is strongly bias dependent, and also critically depends on the adsorption site. We analyze the results in terms of differential bonding strength for the different adsorption sites and we identify those substrate atoms which participate in the bonding with the molecule.     

Structural,electronic and energetic properties of water adsorbed on β-Si3N4 (0 0 0 1) surface: First-principles calculations

Structural, energetic and electronic properties of water molecules adsorbed on β-Si₃N₄ (0 0 0 1) surface, at various coverages, are investigated using density functional theory. At low coverages (θ ? 0.5), it is found that all H₂O molecules undergo spontaneous dissociation forming hydroxyl (OH) and imino (NH) groups where the reactive sites are identified, a result shown for the first time using ab initio theory. For higher coverages (θ > 0.5), only partial dissociation takes place where some of the molecules stay intact being bound via H-bond in good agreement with experimental findings. The driving force for the water dissociation has been identified to be dangling bonds on lower coordinated N and Si surface atoms showing that not all surface atoms are reactive corroborating with previous experimental findings.     

Ferromagnetism in Zn1−xCrxTe (x = 0.05, 0.15) films grown on GaAs(1 0 0) substrate

Zn_1−xCr_xTe (x = 0.05, 0.15) films were grown on GaAs(1 0 0) substrate by thermal evaporation method. X-ray diffraction analysis showed the presence of ZnCrTe phase without any secondary phase. The surface was analyzed by high resolution magnetic force microscope and profile measurements showed orientation of magnetic domains in the range of 0.5–2 nm with increase of Cr content. Magnetic moment–magnetic field measurements showed a characteristic hysteresis loop even at room temperature. The Curie temperature was estimated to be greater than 300 K. From the electron spin resonance spectra, the valence state of Cr in ZnTe was found to be +2 with d² electronic configuration. Hall effect study was done at room temperature and the result showed the presence of p-type charge carriers and hole concentration was found to increase from 5.95 × 10¹² to 6.7 × 10¹² m⁻³ when Cr content increases. We deduce the origin of ferromagnetic behavior based on the observed experimental results.     

NMR and electric impedance study of lithium mobility in fast ion conductors LiTi2 − xZrx(PO4)3 (0 ≤ x ≤ 2)

Materials of the LiTi_2 − xZr_x(PO₄)₃ series (0 ≤ x ≤ 2) were prepared and characterized by powder X-ray (XRD) and neutron diffraction (ND), ⁷Li and ³¹P Nuclear Magnetic Resonance (NMR) and Electric Impedance techniques. In samples with x < 1.8, XRD patterns were indexed with the rhombohedral R3̅c space group, but in samples with x ≥ 1.8, XRD patterns display the presence of rhombohedral and triclinic phases. The Rietveld analysis of the LiTi_1.4Zr_0.6(PO₄)₃ neutron diffraction (ND) pattern provided structural information about intermediate compositions. For low Zr contents, compositions deduced from ³¹P MAS-NMR spectra are similar to nominal ones, indicating that Zr⁴⁺ and Ti⁴⁺ cations are randomly distributed in the NASICON structure. At increasing Zr contents, differences between nominal and deduced compositions become significant, indicating some Zr segregation in the triclinic phase. The substitution of Ti⁴⁺ by Zr⁴⁺ stabilizes the rhombohedral phase; however, electrical performances are not improved in expanded networks of Zr-rich samples. Below 300 K, activation energy of all samples is near 0.36 eV; however, above 300 K, activation energy is near 0.23 eV in Ti-rich samples and close to 0.36 eV in Zr-rich samples. The analysis of electrical data suggests that the amount of charge carriers and entropic terms are higher in Zr-rich samples; however, the increment of both parameters does not compensate lower activation energy terms of these samples. As a consequence of different contributions, the bulk conductivity of Zr-rich samples, measured at room temperature, is one order of magnitude lower than that measured in Ti-rich samples.     

Growth of 〈1 0 0〉 directed ADP crystal with slotted ampoule

Good quality ammonium dihydrogen phosphate single crystals have been grown by: (i) Sankaranarayanan–Ramasamy (SR) method and (ii) SR method with slotted ampoule. The grown crystals were subjected to UV–Vis spectroscopy, high-resolution X-ray diffractometer, dielectric, piezoelectric and laser damage threshold studies. Compared to the (1 0 0) plane of the conventional method grown ADP crystal and 〈1 0 0〉 directed SR method grown ADP crystal, the crystal grown by SR method with slotted ampoule has higher growth rate, higher optical transparency, high crystalline perfection, low dielectric loss, high piezoelectric charge coefficient and high laser damage threshold due to diffusion of segregated impurities away from the growing crystal in the slotted ampoule growth.     

Atomic structure of the (3 × 2) Si–GaAs (0 0 1) reconstructed surface: A clue to δ doping mechanism derived from in situ grazing incidence X-ray diffraction data

In view of understanding silicon incorporation in the δ doping process of GaAs (0 0 1), Si atoms have been deposited, under UHV, on a α(2 × 4) arsenic terminated substrate. In the low coverage regime, a transition to a less As rich (3 × 2) reconstructed Si–GaAs (0 0 1) surface was observed whose atomic structure has been investigated by grazing incidence X-ray diffraction performed in situ. Silicon is found to occupy not only a Ga substitutional site, precursor of a donor dopant but also to form nuclei for neutral clusters, on a template made by the (3 × 2) GaAs (0 0 1) reconstructed surface observed by Martrou et al. [Phys. Rev. B 72 (2005) 241307®]. The maximum surface concentration of donor-like silicon is estimated at 1.04 × 10¹⁴ cm^?2 (1/6th monolayer).     

Adsorption of small molecules on a (2 × 1) PdZn surface alloy on Pd(1 1 1)

The adsorption of methanol, formaldehyde, methoxy, carbon monoxide and water on a (2 × 1) PdZn surface alloy on Pd(1 1 1) has been studied using DFT calculations. The most stable adsorption structures of all species have been investigated with respect to the structure and the electronic properties. It was found that methanol is only weakly bound to the surface. The adsorption energy only increases with higher methanol coverage, where chain structures with hydrogen bonds between the methanol molecules are formed. The highest adsorption energy was found for the formate species followed by the methoxy species. The formaldehyde species shows quite some electronic interaction with the surface, however the stable η₂ formaldehyde has only an adsorption energy of about 0.49 eV. The calculated IR spectra of the different species fit quite well to the experimental values available in the literature.     

Raman scattering study of IrxRu1−xO2 mixed metal oxide nanowires (0 ≤ x ≤ 1)

Recent interests in mixed metal oxide nanostructured materials especially Ir_xRu_1−xO₂ compounds have been mainly driven by the technological application as electrocatalyst and electrode materials. We present room temperature Raman scattering results of single crystalline Ir_xRu_1−xO₂ (0 ≤ x ≤ 1) nanowires grown by atmospheric pressure chemical vapor deposition. We observed that the E_g, the A_1g, and the B_2g phonon modes of a single Ir_xRu_1−xO₂ nanowire are blue-shifted linearly with respect to the Ir contents from which we could get stoichiometry information. We also observed that the asymmetric lineshape and the broadening of the full width at half maximum of the E_g mode that involves the out-of-plane oxygen vibration. The unusual asymmetric broadening of the E_g phonon can be explained by the activation of the non-zone-center phonons due to substitutional disorder present in the system. We also found that there is a mixed mode of the A_1g and the B_2g phonons due to the substitutional disorder, in the range of 630–750 cm⁻¹.     

Ab initio study of Yb on the Ge(111)–(3 × 2) and Si(111)–(3 × 2) surfaces

The surface reconstruction, 3 × 2, induced by Yb adsorption on a Ge (Si)(111) surface has been studied using first principles density-functional calculation within the generalized gradient approximation. The two different possible adsorption sites have been considered: (i) H₃ (this site is directly above a fourth-layer Ge (Si) atom) and (ii) T₄ (directly above a second-layer Ge (Si) atom). We have found that the total energies corresponding to these binding sites are nearly the same, indeed for the Yb/Ge (Si)(111)–(3 × 2) structure the T₄ model is slightly energetic by about 0.01 (0.08) eV/unitcell compared with the H₃ model. In particular for the Ge sublayer, the energy difference is small, and therefore it is possible that the T₄, H₃, or T₄H₃ (half of the adatoms occupy the T₄ adsorption site and the rest of the adatoms are located at the H₃ site) binding sites can coexist with REM/Ge(111)–(3 × 2). In contrast to the proposed model, we have not determined any buckling in the Ge = Ge double bond. The electronic band structures of the surfaces and the corresponding natures of their orbitals have also been calculated. Our results for both substrates are seen to be in agreement with the recent experimental data, especially that of the Yb/Si(111)–(3 × 2) surface.     

Scanning tunneling microscope study of nanosized metal–semiconductor contacts between ErSi2 nanoislands and Si(0 0 1) substrate

The current–voltage (I–V) characteristics of the nanosized metal–semiconductor contacts formed between the epitaxially grown ErSi₂ islands and p-Si(0 0 1) substrate are measured in situ by the scanning tunneling microscope. Experimental results show that the current densities passing through the nanocontacts are five orders of magnitude larger than that of the macroscopic ones and have an obvious dependence on the contact area. Especially, it is found that I–V characteristics of the contacts are sensitive to the sample surface adsorption. Our investigations indicate that surface conduction plays an important role in the electrical transport process from ErSi₂ islands to the Si(0 0 1) substrate. Furthermore, for the nanocontacts with surface currents suppressed effectively, the ideality factor and the effective Schottky barrier height are estimated by using the standard thermionic emission model. Our analysis suggests that the current through the interface between ErSi₂ nanoislands and the p-Si(0 0 1) substrate is enhanced due to the effects of tunneling and image force lowering.     

Theoretical investigation of the inversion parameter in Co3 − sAlsO4 (s = 0–3) spinel structures

The structural, energetic, and thermodynamic properties of the Co_3 ? sAl_sO₄ (s = 0, 1, 2, and 3) crystal family are studied using periodic DFT calculations. We provide a quantitative discussion of the cation distribution effect on the cell parameter, the oxygen Wyckoff position, the interatomic distances and the energies of the structures. It is demonstrated that the low cobalt containing CoAl₂O₄ spinel is the most stable structure of the Co_3 ? sAl_sO₄ (s = 0, 1, 2, and 3) crystal family.