Synthesis of TiO2 thin film by a modified sol-gel method and properties of the prepared films for photocatalyst

PTA (peroxo titanic acid) gel was prepared by a modified sol-gel method from peroxo titanic acid using TiCl₄/ethanol/water solution as the starting material at room temperature. Physicochemical properties of heat-treated gel were characterized by IR, XRD, TG-DTA and SEM. Optimal preparing conditions were chosen to prepare anatase film for the photocatalytic degradation of methyl orange. The dip-coating technique was used to synthesis the supported anatase film on quartz glass. Photocatalytic efficiency for the degradation of methyl orange under UV irradiation was also examined. It was found that the degradation efficiency of the anatase film synthesized in this paper is higher than commercial titania P25.     

The influence of titanium dioxide phase composition on dyes photocatalysis

A comparative study of TiO₂ powders prepared by sol–gel methods is presented. Titanium tetraisopropoxide was used as the precursor for the sol–gel processes. The effects of the annealing treatment on phase, crystallite size, porosity and photodegradation of dyes (methyl orange and methylene blue) were studied. The phase structure, microstructure and surface properties of the films were characterized by using X-ray diffraction (XRD) and Atomic Force Microscopy (AFM). The X-ray diffraction was used for crystal phase identification, for the accurate estimation of the anatase–rutile ratio and for the crystallite size evaluation of each polymorph in the samples. It was found that the only TiO₂ anatase phase of the synthesized TiO₂ develops below 500 °C, between 600 and 800 °C the anatase coexist with rutile and above 800 °C only the rutile phase was found in the samples. Attention has been paid not only to crystal structures, but also to the porosity, the particle size and the photocatalytic properties. However, the annealing temperature was found to have significant influence on the photocatalytic properties. Different TiO₂ doctor blade thin films were obtained mixing the sol gel powder (100% anatase) and TiO₂ Aldrich with TiO₂ Degussa P25. The surfactant (Triton X100 or sodium dodecyl sulfate) affects the packing density of the particles during deposition and the photocatalytic degradation efficiency of the dyes. The photocatalytic degradation kinetics of methyl orange and methylene blue using TiO₂ thin film were investigated.     

Synthesis and characterization of novel InVO<Subscript>4</Subscript>–TiO<Subscript>2</Subscript> thin films using the low temperature sol

The InVO₄ sol was obtained by a mild hydrothermal treatment (the precursor precipitation solution at 423 K, for 4 h). Novel visible-light activated photocatalytic InVO₄–TiO₂ thin films were synthesized through a sol–gel dipping method from the composite sol, which was obtained by mixing the low temperature InVO₄ sol and TiO₂ sol. The photocatalytic activities of the new InVO₄–TiO₂ thin films under visible light irradiation were investigated by the photocatalytic discoloration of methyl orange aqueous solution. The thin films were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM) and UV–Vis absorption spectroscopy (UV–Vis). The results revealed that the InVO₄ doped thin films enhanced the methyl orange degradation rate under visible light irradiation, 3.0 wt% InVO₄–TiO₂ thin films reaching 80.1% after irradiated for 15 h.     

Role of ammonium ions on the stability of TiO2 sol

In this paper, the role of the trace ammonium ions on the stability of TiO₂ sol prepared by peroxo titanic acid (PTA) sol was investigated. The results showed that the removal of ammonium ions in PTA sol is beneficial to reduce agglomeration and increase the negative charge on the surface of TiO₂ colloidal particles, contributing to the higher stability and longer storage time of the TiO₂ sol. It was also approved by the increase of interaction energy calculated by classical DLVO theory. In addition, the photocatalytic performance of TiO₂ sol was improved due to the decrease of aggregation of TiO₂ colloidal particles.     

Fabrication of Ordered TiO2 Porous Thin Films by Sol-Dipping PS Template Method

Monolayer polystyrene spheres (∼400 nm) array templates were assembled orderly on clean glass substrates by dip-drawing method from emulsion of PS and porous TiO₂ thin films were prepared by using sol-dipping template method to fill TiO₂ sol into the interstices among the close-packed PS templates and then annealing to remove the PS templates. The effects of TiO₂ precursor sol concentration and dipping time in sol on the porous structure of the thin films were studied. The results showed pore size of the ordered TiO₂ porous thin film depended mainly on PS size and partly on TiO₂ sol concentration. The shrinkage of pore diameter was about 10% for 0.2 M and 20% for 0.4 M TiO₂ sol concentrations. X-ray diffraction (XRD) spectra indicated the porous thin film was anatase structure. The transmittance spectrum showed that optical transmittance of the porous thin film kept above 70% beyond the wavelength of 430 nm. Optical band-gap of the porous TiO₂ thin film (fired at 550^∘;C) was 3.12 eV.     

How room-humidity during the coating affects the structural,optical and photocatalytic properties of TiO<Subscript>2</Subscript> films

TiO₂ thin films were obtained on glass slide substrates by the sol–gel technique. The substrates were coated by the immersion-removal method, at a constant withdrawal speed. The TiO₂ precursor solution and the substrate were maintained in a closed box with a controlled relative humidity (RH) during the removal of the substrate. The RH was varied in the 30–90% range in steps of 20%. The films were dried and after that sintered in an open atmosphere. The effect of the RH was studied on the structural, optical and photocatalytic properties. The films are polycrystalline with an anatase phase and show a high optical transmission in the UV–Vis range. The photocatalytic activity was evaluated by the photobleaching of methylene blue in an aqueous solution. The best photocatalytic activity was obtained for the films with 90% RH, this fact is mainly attributed to the highest porosity value obtained for these films.     

Photocatalytic activity of (sulfur,nitrogen)-codoped mesoporous TiO<Subscript>2</Subscript> thin films

Nitrogen and sulfur co-doped mesoporous TiO₂ thin films were fabricated using thiourea as a doping resource by the combination of the sol–gel and evaporation-induced self-assembly (EISA) processes. Scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), N₂ adsorption–desorption, and UV–vis spectra were performed to characterize the as-synthesized mesoporous TiO₂ materials. The XPS result shows that O–Ti–N and O–Ti–S bonds in the (S, N)-codoped mesoporous TiO₂ were formed. The resultant mesoporous (S, N)-codoped TiO₂ exhibited anatase framework with a high porosity and a narrow pore distribution. After being illuminated for 3 h, methyl orange (MO) could be degraded completely by the co-doped sample under the ultraviolet irradiation, whereas mesoporous TiO₂ film without doping could only degrade 60% MO. After being illuminated by visible light, the water contact angles of the mesoporous co-doped TiO₂ samples decreased slightly, but the pure TiO₂ mesoporous film exhibited no change in the hydrophilicity.     

Hydrothermal synthesis and enhanced photocatalytic activity of mixed-phase TiO2 powders with controllable anatase/rutile ratio

In this study, mixed-phase TiO₂ powders were novelly synthesized via a facile and mild hydrothermal method without any post-heat treatment. TiOSO₄ and peroxide titanic acid (PTA) were used as inorganic titanium sources, while no special solvent or additive were introduced. The XRD and TEM results showed the mixed-phase TiO₂ powders were composed of anatase and rutile phases, and the PTA sol played an important role on forming the rutile nucleus. The proportion of rutile in the mixed-phase TiO₂ could be easily controlled in the range of 0%–70.5% by changing the amount of PTA sol used in the synthesis process. The UV-Visible absorption spectra indicated the prepared mixed-phase TiO₂ showed enhanced visible light absorption with the increase of rutile ratio. The photodegradation experiments revealed the mixed-phase TiO₂ exhibited the best photocatalytic activity at the rutile ratio of 41.5%, while a higher or lower rutile ratio both resulted in the decrease of photocatalytic activity.     

Low-temperature synthesis of photocatalytic TiO2 thin film from aqueous anatase precursor sols

Anatase TiO₂ sols (RS) were synthesized by peptizing the hydrolysis of titanyl sulfate in abundant hydrogen peroxide solution and subsequent reflux to enhance crystallization. The influences of various reflux time on crystallinity, morphology, and size of the obtained TiO₂ sol and dried TiO₂ film particles were investigated. At room temperature, crystalline TiO₂ thin film was deposited on glass silde from the as prepared TiO₂ sol by dip-coating method. No further thermal posttreatment was required to eliminate organics from the film or to induce titania crystallization. TiO₂ thin film on substrates could be thickened by means of consecutive dip-coating process. Titania film thus obtained was transparent and showed proper adherence. The photocatalytic activities of the TiO₂ thin film was assessed by the degradation of methyl orange in aqueous solution. The preparation process of photocatalytic TiO₂ thin film was quite simple and a low-temperature route.     

Characterization and activity of visible light–driven TiO<Subscript>2</Subscript> photocatalysts co<Emphasis Type="Bold">-</Emphasis>doped with nitrogen and lanthanum

Nitrogen and lanthanum co-doped titania photocatalysts were prepared by a modified sol–gel process with urea and lanthanum nitrate doping precursors and characterized by various techniques including XRD, FTIR, TEM, EDS, and UV–Vis DRS. The average crystallite size was ca. 12–15 nm as calculated from XRD patterns, and anatase was the dominant crystalline type in the as-prepared samples. The UV–Vis DRS of the samples revealed significant absorption within the range of 400–500 nm. The optimum composition of N(0.020)La(0.012)TiO₂ exhibited the highest photocatalytic activity for degradation of methyl orange (MO) aqueous solution under simulated sunlight. The percent degradation of MO was ca. 97% for N(0.020)La(0.012)TiO₂ under simulated sunlight irradiation for 9 h. The enhanced photocatalytic activity was ascribed to the synergistic effects of the nitrogen and lanthanum co-doping.     

Photocatalytic degradation of methyl orange on arrayed porous iron-doped anatase TiO2

Arrayed porous iron-doped TiO₂ was prepared by sol–gel with polystyrene spheres as template and used as photocatalyst for the degradation of methyl orange. The structure and performances of the prepared photocatalyst were characterized with X-ray diffractometer, inductively coupled plasma-atomic emission spectrometer, scanning electron microscope, UV-visible spectrometer, and methyl orange degradation tests. It is found that the iron dopant does not change the crystal phase of TiO₂ but affects its lattice constant, optical absorption, electronic conductivity, charge-transfer resistance, and activity toward the degradation of methyl orange. The sample doped with 0.01 wt.% Fe (based on Ti) and with smaller pore size exhibits the better photocatalytic activity. The degradation rate of methyl orange on the sample with a pore size of 190 nm is 2.3 times that on the undoped sample with the same pore size.     

锐钛矿型多孔TiO2薄膜的溶解法制备及性能表征

在具有锐钛矿晶粒的TiO₂溶胶中加入苯丙乳液粒子，使用该混合液浸渍提拉涂膜，然后利用甲苯将薄膜中的苯丙乳液粒子溶解去除，并通过重复涂膜，在室温下获得了具有良好多孔性的锐钛矿型TiO₂薄膜。考察了多孔薄膜的表面形貌、光学性能、吸附性能和光催化性能。结果表明：随薄膜涂膜次数的增加，TiO₂多孔薄膜的吸光度增大，透光率减小，光吸收边波长向长波方向移动。罗丹明B在TiO₂多孔薄膜上的吸附量随涂膜次数的增加先升高，后降低；多次涂膜会在薄膜中产生半封闭的孔洞，经过长时间的毛细渗透等作用能进一步增加薄膜对罗丹明B的吸附。TiO₂多孔薄膜通过吸附+光催化氧化的模式快速分解罗丹明B，其活性主要受到薄膜在光催化反应初期的吸附能力的影响。此外，TiO₂的负载量、光的利用效率、以及光生电荷迁移及其分离等也是影响薄膜光催化活性的因素。     

Photocatalytic TiO2 Coatings: Effect of Substrate and Template

Summary. Transparent TiO₂ films with a high photodegradation activity towards an azo dye in aqueous solution were prepared by sol–gel processing. Films on soda–lime glass supports protected with a thin silica barrier layer exhibited better crystallization and monodisperse nanoparticles, higher absorption of light below 370 nm, and higher photocatalytic activity than those films deposited on bare glass supports proving the detrimental effect of interdiffused sodium ions on the development of the anatase nanostructure. The effect of substrate was more pronounced in thinner films (300 nm) than in thicker ones (1200 nm), which were achieved by adding a template (i.e. Pluronic F127) to the sol.     

Enhanced photocatalytic activity for titanium dioxide by co-modification with copper and iron

A copper(II) and iron(III) co-modified titanium dioxide nano material was prepared by a simple sol–gel process using titanium(IV) isopropoxide plus copper(II) and iron(III) nitrates as raw materials. The as-prepared nanocomposites were characterized by X-ray diffraction (XRD), diffuse reflectance spectroscopy and photoluminescence spectra. The XRD results showed that the undoped TiO₂ nanoparticles mainly include anatase phase while the Cu, Fe-codoped TiO₂ nanoparticles showed a mixture of anatase phase with a small fraction of rutile phase displaying higher activity than the pure anatase phase. Optical characterization showed that the codoping with copper(II) and iron(III) resulted in a red shift of adsorption and lower recombination probability between electrons and holes, which were associated with high photocatalytic activity of the Cu, Fe-codoped TiO₂ nanoparticles under visible light (λ > 400 nm). The photocatalytic activity of the samples was tested by aqueous methyl orange degradation. The capability of the codoped catalyst was much higher than that of the pure TiO₂ catalyst under visible irradiation. A mechanism is proposed in order to account for the enhanced catalytic activity.     

Photocatalytic TiO2 Coatings: Effect of Substrate and Template

Transparent TiO₂ films with a high photodegradation activity towards an azo dye in aqueous solution were prepared by sol–gel processing. Films on soda–lime glass supports protected with a thin silica barrier layer exhibited better crystallization and monodisperse nanoparticles, higher absorption of light below 370 nm, and higher photocatalytic activity than those films deposited on bare glass supports proving the detrimental effect of interdiffused sodium ions on the development of the anatase nanostructure. The effect of substrate was more pronounced in thinner films (300 nm) than in thicker ones (1200 nm), which were achieved by adding a template (i.e. Pluronic F127) to the sol.     

Preparation and Characterization of Bismuth Doped TiO2 Thin Films

A series of Bismuth-doped titanium oxide (Bi-doped TiO₂) thin films on glass substrates have been prepared by sol-gel dip coating process. The prepared catalysts were characterized by XRD and XPS. The photocatlytic activity of the thin film catalysts was evaluated through the photodegradation of aqueous methyl orange under UV illumination. The experiments demonstrated that the Bi-doped TiO₂ prepared was anatase phase. The doped bismuth was in the 3⁺ oxidation state. The presence of Bi significantly enhanced the photocatalytic activity of TiO₂ films. At calcination temperature of 500°C, with doping concentration of 2 wt %, Bi-doped TiO₂ thin film showed the highest photocatalyic activity.     

Tribological performance of fluoroalkylsilane modification of sol–gel TiO<Subscript>2</Subscript> coating

This paper explores the possibility of making coatings with super friction-reducing and wear protection properties by using both sol–gel and self-assembling techniques. The thin film of TiO₂ was firstly prepared on glass substrates via a sol–gel method, followed by sintering at 480°C. The self-assembled monolayer of Fluoroalkylsilane (FAS) were then prepared on TiO₂ thin film to obtain TiO₂–FAS dual-layer film. The contact angle measurement and X-ray photoelectron spectroscopy were used to determine the wetting behavior and chemical structure of films, respectively. The friction behavior of films sliding against a steel ball was examined on a macro friction and wear tester. It is shown that FAS is strongly adsorbed on sol–gel derived TiO₂ thin film, making it strongly hydrophobic. Good friction-reducing and wear protection behavior is observed for the glass substrate after duplex surface-modification with sol–gel TiO₂ and top layer of FAS.     

Preparation and photocatalytic activity of TiO<Subscript>2</Subscript> films with Ni nanoparticles

Titania thin films were synthesized by sol–gel dip-coating method with metallic Ni nanoparticles synthesized separately from an organometallic precursor Ni(COD)₂ (COD = cycloocta-1,5-diene) in presence of 1,3-diaminopropane as a stabilizer. Titania was obtained from a titanium isopropoxide precursor solution in presence of acetic acid. A Ni/TiO₂ sol system was used to coat glass substrate spheres (6, 4 and 3 mm diameter sizes), and further heat treatment at 400 °C was carried out to promote the crystallization of titania. XRD analysis of the TiO₂ films revealed the crystallization of the anatase phase. Transmission Electron Microscopy (TEM) and High Resolution TEM studies of Ni nanoparticles before mixing with the TiO₂ solution revealed the formation of Ni nanostructures with an average size of 5–10 nm. High-angle annular dark-field images of the Ni/TiO₂ system revealed well-dispersed Ni nanoparticles supported on TiO₂ and confirmed by AFM analysis. The photocatalytic activity of the Ni/TiO₂ films was evaluated in hydrogen evolution from the decomposition of ethanol using a mercury lamp for UV light irradiation. Titania films in presence of Ni nanoparticles show higher efficiency in their photocatalytic properties in comparison with TiO₂.     

Chemical synthesis of Ni/TiO<Subscript>2</Subscript> nanophotocatalyst for UV/visible light assisted degradation of organic dye in aqueous solution

The Ni/TiO₂ nanoparticles with different Ni dopant content were prepared by a modified sol–gel method. The structure and photoinduced charge properties of the as-prepared catalysts were determined using X-ray diffraction, transmission electron microscopy, UV–vis diffuse reflectance spectroscopy and surface photovoltage spectroscopy techniques, and the photocatalytic efficiency of these catalysts was tested using an organic dye. It was shown that Ni modification could greatly enhance the photocatalytic efficiency of these nanocomposite catalysts by taking the photodegradation of methyl orange as a model reaction. With appropriate ratio of Ni and TiO₂, Ni/TiO₂ nanocomposites showed the superior photocatalytic activity than the single TiO₂ nanoparticles. Surface photovoltage spectra demonstrated that Ni modification could effectively inhibit the recombination of the photoinduced electron and holes of TiO₂. This electron–hole pair separation conditions are responsible for the higher photocatalytic performance of Ni/TiO₂ nanocomposites in the visible region of electromagnetic spectrum.     

Synergistic effect between TiO2 sol–gel and Degussa P25 in dye photodegradation

The TiO₂ powders were synthesized by versatile and low cost sol–gel process using HNO₃ and titanium tetra-isopropoxide (volumetric ratio of 4:1) following by the hydrolysis reaction. The powders show the two polymorphs of TiO₂: 96 % anatase and 4 % brookite, due to acidic condition (pH = 3). Thin films of titanium oxide were obtained by dip-coating, using the sol–gel of titanium oxide mixed with commercial Degussa P25 into a weight ratio 1:1 or 1:1.5, to enhance the synergistic effect of anatase/rutile ratio aiming at increasing the efficiency of the TiO₂ photocatalyst in dyes degradation. The thin film surface (charge and morphology) was controlled by polymer (poly-ethylene glycol) and surfactant (Sodium dodecyl sulphate, Triton X100) addition. The titanium oxide was characterized by particle size analyzer, contact angle measurements, X-ray diffraction, scanning electron microscopy, and atomic force microscopy. The photocatalytic properties of powders and coatings were evaluated based on the degradation efficiency of two reference dyes (methyl orange and methylene blue). The results outline that poly(ethylene glycol) and films morphologies are the most influential factors that affecting the photocatalytic activity.