Upconverted VUV luminescence of Nd and Er doped into LiYF4 crystals under XeF-laser excitation

The upconverted VUV (185 nm) and UV (230 and 260 nm) luminescence due to 5d-4f radiative transitions in Nd³⁺ ions doped into a LiYF₄ crystal has been obtained under excitation by 351/353 nm radiation from a XeF excimer laser. The maximum upconversion efficiency, defined as the ratio of intensity for 5d-4f luminescence to overall intensity for 5d-4f and 4f-4f luminescence from the ⁴D_3/2 Nd³⁺ level, has been estimated to be about 70% under optimal focusing conditions for XeF laser radiation. A redistribution of intensity between three main components of 5d-4f Nd³⁺ luminescence is observed under changing the excitation power density, which favors the most long-wavelength band (260 nm) at higher excitation density level. The effect is interpreted as being due to excited state absorption of radiation emitted. The upconverted VUV and UV luminescence from the high-lying ²F(2)_7/2 4f level of Er³⁺ doped into a LiYF₄ crystal has also been obtained under XeF-laser excitation the most intense line being at 280 nm from the spin-allowed transition to the ²H(2)_11/2 4f level of Er³⁺, but the efficiency of upconversion for Er³⁺ emission is low, less than 5%.     

Optical character of Er/Yb co-doped P2O5-CaO-Na2O-Al2O3-AgO phosphate glass

The up-conversion (UC) and near infrared (NIR) luminescence of Er³⁺/Yb³⁺ co-doped phosphate glass are investigated. In the UC emission range, the 523 nm, 546 nm green emissions and the 659 nm red emission are observed. With the increasing pump power, the intensity ratios of I₅₂₃/I₆₅₉, I₅₄₆/I₆₅₉ and I₅₂₃/I₅₄₆ increase gradually. The phenomenon is reasonably interpreted by theoretical analysis based on steady state rate equations. The emission cross section of the infrared emission at 1546 nm is larger (about 6.7 × 10^− 21 cm²), which is suitable for making fiber amplifier.     

Infrared and visible emission of Er in combustion-synthesized CaAl2O4 phosphors

New near-infrared luminescent, monoclinic CaAl₂O₄:Er³⁺ phosphor was prepared by using the combustion route at furnace temperatures as low as 500 °C in a few minutes. Combustion synthesized phosphor has been well characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy-dispersive analysis of X-ray (EDAX) mapping studies. The luminescence spectra of Er³⁺-doped calcium aluminate were studied at UV (380 nm), vis (488 nm) and IR (980 nm) excitation. Upon UV and vis excitation, the CaAl₂O₄:Er³⁺ phosphor exhibits emission bands at ~523 nm and at ~547 nm, corresponding to transitions from the ²H_11/2 and ⁴S_3/2 erbium levels to the ⁴I_15/2 ground state. A strong luminescence at 1.55 μm in the infrared (IR) region due to ⁴I_13/2→⁴I_15/2 transition has been observed in CaAl₂O₄:Er³⁺ phosphor upon 980 nm CW pumping. In the spectrum of IR-excited up-conversion luminescence, green (~523 and ~547 nm) and red (662 nm) luminescence bands were present, the latter associated with the ⁴F_9/2→⁴I_15/2 transitions of Er³⁺ ions. Both excited state absorption and energy transfer may be proposed as processes responsible for the population of the ⁴S_3/2 and ⁴F_9/2 erbium levels upon IR excitation. The mechanisms responsible for the up-conversion luminescence are discussed.     

Effect of Ce on the spectroscopic properties in Er doped TeO2-GeO2-Nb2O5-Li2O glasses

The Ce³⁺ ion was introduced into Er³⁺ doped TeO₂-GeO₂-Nb₂O₅-Li₂O (TGNL) glass to improve the 1.5 μm fluorescence characteristics. As increasing of Ce³⁺ concentration, the lifetime of Er³⁺:⁴I_11/2 level is shortened form 360 to 225 μs, while the Er³⁺:⁴I_13/2 level remains unchanged. Accordingly, the upconversion fluorescence (blue, green and red) was quenched. Improved 1.5 μm emission is obtained and the reason is ascribed to the increase of nonradiative rate between the ⁴I_11/2 and ⁴I_13/2 level of the Er³⁺ ions.     

Upconversion properties of Er^3＋/Yb^3＋ co-doped TeO2-Nb2O5-Li2O glasses

The Er^3＋/Yb^3＋ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser diode is observed with the naked eyes. The dependence of luminescence intensity on the ratio of Yb^3＋/Er^3＋ is discussed in detail, and the relationship between the ratio of green luminescence intensity to red luminescence intensity and the ratio of Yb^3＋/Er^3＋ is also studied, The luminescence intensity increases with the ratio of Yb^3＋/Er^3＋ increasing. The ratio of Yb^3＋/Er^3＋ plays a more important role than the concentration of Er^3＋ in determining the upconversion luminescence intensity. The ratio of green luminescence intensity to red luminescence intensity reaches a maximum when ratio of Yb^3＋/Er^3＋ is 3. Thus the glass could be one of the potential candidates for LD pumping solid-state lasers.     

980 nm激发下Er3+/Yb3+共掺杂ZrO2-Al2O3粉末的上转换发光特性

通过固相反应法制备了Er³⁺/Yb³⁺共掺杂ZrO₂-Al₂O₃粉末的样品，并对样品在980nm激光激发下的上转换发光特性进行了研究.从发射光谱可以发现，在可见光范围内有3个强的发光带，一个位于654nm附近的红光带和两个分别位于545nm、525nm附近的绿光带，分别对应于Er³⁺离子的以下辐射跃迁：⁴F_9/2→⁴I_15/2、⁴S_3/2→⁴I_15/2、 ²H_11/2→⁴I_15/2.其中又以Er³⁺离子的⁴F_9/2→⁴I_15/2跃迁产生的红色荧光辐射最强.对其上转换发光机制进行了分析，发现这三个发光过程都是双光子过程.对样品粉末进行了XRD检测，发现ZrO₂主要以立方相为主，并且计算得到了这种立方结构的晶格常数.Al₂O₃固溶于ZrO₂中，Al³⁺嵌入ZrO₂后产生氧空位，导致ZrO₂晶体的对称性降低，这种结构变化更有利于提高上转换效率，即上转换发光强度增强. 关键词： 3+/Yb³⁺')" href="#">Er³⁺/Yb³⁺ 上转换 2-Al₂O₃')" href="#">ZrO₂-Al₂O₃ 荧光 稀土     

Enhancement of upconversion luminescence in Tm/Er/Yb-codoped glass ceramic containing LiYF4 nanocrystals

A transparent Er³⁺–Tm³⁺–Yb³⁺ tri-doped oxyfluoride glass ceramics containing LiYF₄ nanocrystals were prepared. Under 980 nm laser diode (LD) pumping, intensive red, green and blue upconversion (UC) was obtained. The blue, green, and red UC radiations correspond to the transitions ¹G₄→³H₆ of Tm³⁺, ²H_11/2/⁴S_3/2→⁴I_15/2, and ⁴F_9/2→⁴I_15/2 of Er³⁺ ions, respectively. This is similar to that in Tm³⁺–Yb³⁺ and/or Er³⁺–Yb³⁺ co-doped glass ceramics. However, the blue UC radiations of the Er³⁺–Yb³⁺ co-doped glass ceramics is two-photon process due to cooperative energy transfer. The UC mechanisms were proposed based on spectral, kinetic, and pump power dependence analyses.     

The up-conversion properties of Yb and Er doped Y4Al2O9 phosphors

Er³⁺ doped and Yb³⁺/Er³⁺ co-doped Y₄Al₂O₉ phosphors are prepared by the sol-gel method. The effect of dopant concentration on the structure and up-conversion properties is investigated by X-ray diffraction (XRD) and photoluminescence, respectively. XRD pattern indicates that the sample structure belongs to monoclinic. Under 980 nm excitation, the green and red up-conversion emissions are observed and the emission intensities depended on the Yb³⁺ ion concentration. The green up-conversion emissions decrease with the increase of Yb³⁺ concentration, while red emission increases as Yb³⁺ concentration increases from 0 to 8 at% and then decreases at high Yb³⁺ concentration. The mechanisms of the up-conversion emissions are discussed and results shows that in Er³⁺ and Yb³⁺/Er³⁺ co-doped system, cross-relaxation (CR) and energy transfer (ET) processes play an important role for the green and red up-conversion emissions.     

Yb3+敏化的Er3+/Ho3+共掺碲酸盐玻璃的上转换发光研究

用高温熔融法制备了系列Er³⁺/Yb³⁺共掺，Ho³⁺/Yb³⁺共掺，和Er³⁺/Yb³⁺/Ho³⁺三掺碲酸盐玻璃，在975nm激光抽运下三种掺杂玻璃中都出现了较强的绿光和红光上转换.研究了Yb³⁺离子对Er³⁺和Ho³⁺离子上转换发光强度的影响以及Yb³⁺→Er关键词： 3+/Yb³⁺/Ho³⁺共掺')" href="#">Er³⁺/Yb³⁺/Ho³⁺共掺 碲酸盐玻璃 光谱性质 上转换     

Upconversion emission enhancement in Er/Yb-codoped BaTiO3 nanocrystals by tridoping with Li ions

Er³⁺/Yb³⁺/Li⁺-tridoped BaTiO₃ nanocrystals were prepared by a sol-gel method to improve the upconversion (UC) luminescence of rare-earth doped BaTiO₃ nanoparticles. Effects of Li⁺ ion on the UC emission properties of the Er³⁺/Yb³⁺/Li⁺-tridoped BaTiO₃ nanocrystals were investigated. The results indicated that tridoping with Li⁺ ion enhanced the visible green and red UC emissions of Er³⁺/Yb³⁺-codoped BaTiO₃ nanocrystals under the excitation of a 976 nm laser diode. X-ray diffraction and decay time of the UC luminescence were studied to explain the reasons of the enhancement of UC emission intensity. X-ray diffraction results gave evidence that tridoping with Li⁺ ion decreased the local symmetry of crystal field around Er³⁺, which increased the intra-4f transitions of Er³⁺ ion. Moreover, lifetimes in the intermediate ⁴ S_3/2 and ⁴I_11/2 (Er) states were enhanced by Li⁺ ion incorporation in the lattice. Therefore, it can be concluded that Li⁺ ion in rare-earth doped nanocrystals is effective in enhancing the UC emission intensity.     

Infrared-to-visible upconversion in Er and Er/Yb activated Sb2O4 nanopowders prepared by sol-gel route

We prepared Er³⁺ doped and Er³⁺/Yb³⁺ codoped Sb₂O₄ nanocrystals by the sol-gel method. The Raman, X-ray diffraction (XRD), transmission electron microscope (TEM), and photoluminescence spectra of the samples were studied. The phonon energy of the Sb₂O₄ nanocrystals is very low (the maximum value being 461 cm⁻¹). The upconversion (UC) red emission of the Er³⁺/Yb³⁺ codoped sample is very strong at 975 nm laser diode excitation. The Sb₂O₄ nanocrystals will be a promising luminous material.     

Er3+及Er3+/Yb3+掺杂ZrO2-Al2O3的制备及发光性质

采用共沉淀法制备了纳米晶ZrO₂-Al₂O₃∶Er³⁺发光粉体.所制备的粉体室温下具有Er3+离子特征荧光发射,主发射在绿光,其中位于547 nm、560 nm的绿光最强,并得出稀土离子与基质之间有能量传递.对不同煅烧温度下的样品研究表明:因不同温度下所制得的样品晶相不同.研究了纳米晶ZrO2-Al2O3∶Er3+及ZrO₂-Al₂O₃∶Er³⁺/Yb³⁺的上转换发光,并分析了上转换的跃迁机制.发现ZrO₂-Al₂O₃∶Er³⁺的绿光为双光子过程,而ZrO₂-Al₂O₃∶Er³⁺、Yb³⁺的上转换光谱中,红光和绿光也为双光子过程,而极弱的蓝光为三光子过程.讨论了Er³⁺的浓度猝灭现象.最适宜掺杂浓度的原子分数为2%（Er³⁺/Zr⁴⁺）.     

Synthesis and characterization of core-shell structured SiO2@YVO4:Yb,Er microspheres

In this paper, the core-shell structured SiO₂@YVO₄:Yb³⁺,Er³⁺ microspheres have been successfully prepared via a facile sol-gel process followed by a heat treatment. X-ray diffraction, field emission scanning electron microscopy, energy disperse X-ray spectroscopy, transmission electron microscopy, Fourier transform infrared spectroscopy, and photoluminescence spectra were used to characterize the samples. The results reveal that the SiO₂ spheres have been successfully coated by YVO₄:Yb³⁺,Er³⁺ phosphors to form core-shell structures and the size of obtained microspheres has a uniform distribution. Additionally, the samples exhibit bright green luminescence under the excitation of a 980 nm laser diode. The photoluminescence intensity increases with the number of coatings. These core-shell structured SiO₂@YVO₄:Yb³⁺,Er³⁺ microspheres may have great potential in the fields of infrared detection and display devices.     

Er3+离子掺杂钡镓锗玻璃上转换发光机理研究

研究了Er³⁺离子掺杂钡镓锗玻璃的吸收光谱、拉曼光谱和上转换光谱.分析了Er³⁺离子在钡镓锗玻璃中的上转换发光机理.结果表明：玻璃的最大声子能量为828cm^-1，紫外截止波长为275nm.采用800nm和980nmLD激发玻璃样品，在室温下观察到强烈的上转换绿光和红光发射.随着Er³⁺离子浓度的增加，绿光发光强度先增加后减小，而红光发光强度呈单调递增趋势.能量分析表明：800nmLD激发产生的绿光主要源于Er³⁺离子4I_13/2能级的激发态吸收过程；红光发射主要源于Er³⁺离子4I_13/2能级与4I_11/2能级之间的能量转移过程.980nmLD激发产生的绿光主要源于Er³⁺离子4I_11/2能级之间的能量转移过程；而红光发射主要源于Er³⁺离子4I_13/2能级与4I_11/2能级之间的能量转移过程和4I_13/2能级的激发态吸收过程.通过量子效率分析，发现采用800nmLD激发Er³⁺离子掺杂浓度为1mol% 的样品时，上转换绿光发光效率最高. 关键词： 上转换发光机理 3+离子掺杂')" href="#">Er³⁺离子掺杂 钡镓锗玻璃     

Up-conversion white light of Tm/Er/Yb tri-doped CaF2 phosphors

Tm³⁺/Er³⁺/Yb³⁺ tri-doped CaF₂ phosphors were synthesized using a hydrothermal method. The phosphors were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and up-conversion (UC) emission spectra. After annealing, the phosphors emitted white light under a 980 nm continuous wave diode laser (CW LD 2 W) excitation. As the excitation power density changed in the range of 20-260 W/cm², the chromaticity coordinates of the UC light of the phosphor Ca_0.885Tm_0.005Er_0.01Yb_0.1F₂ fell well in the white region of the 1931 CIE diagram. For the proportion of red, green and blue (RGB) in white light is strict, key factors for achieving UC white light, such as host materials, rare earth ions doping concentrations, annealing temperatures, as well as the excitation power densities, were investigated and discussed.     

Optical detection of near infrared femtosecond laser-heating of Er-doped ZnO-Nb2O5-TeO2 glass by green up-conversion fluorescence of Er ions

The green up-conversion fluorescence of Er³⁺ ions doped in an nonlinear optical ZnO-Nb₂O₅-TeO₂ glass was observed by using 800 nm excitation from a regenerative femtosecond (fs) Ti:Sapphire laser. The detailed analysis on two fluorescence lines at 526 nm (²H_11/2-⁴I_15/2) and 548 nm (⁴S_3/2-⁴I_15/2) revealed the fs laser heating of the multi-component TeO₂-based glass, which was possibly due to its nonlinear absorption of the host glass via the imaginary part of the third-order optical susceptibility (χ⁽³⁾). The result was compared with that of a Er³⁺-doped aluminosilicate glass under the same irradiation condition. When the fs laser was irradiated to the multicomponent TeO₂-based glass in the power density of 150 TW/cm², the laser spot was heated up to ∼520 K, which however was still less than the glass transition temperature (T_g=688 K). This technique provides a useful sensing method of laser spot temperature even inside transparent materials.     

Preparation and upconversion properties of Ba2ErF7 and Ba2ErF7:Yb powders

Novel Ba₂ErF₇ and Yb³⁺-doped Ba₂ErF₇ powders were synthesized by a coprecipitation method. In Ba₂ErF₇ sample, abundant upconverted emission bands from violet to infrared region are observed under 980 nm excitation, whereas only green and red emissions are observed under 812 nm excitation. Under the two excitations, the luminescence decay curves of the green and red emissions are measured and the quenching behaviors of Yb³⁺ doping are also explored. It is found that a suitable Yb³⁺ concentration can efficiently enhance the intensity ratio of the blue and violet emissions to the green and red ones, which may be due to the competition between the energy transfer process from Er³⁺ to Yb³⁺ and the sensitizing process from Yb³⁺ to Er³⁺ in Ba₂ErF₇:Yb³⁺. This indicates that the Yb³⁺-doped Ba₂ErF₇ might be a good candidate for blue and violet upconversion phosphor.     

The effect of Y co-doping on the persistent up-conversion luminescence of the ZrO2:Yb,Er nanomaterials

The effect of the defects due to the charge compensation obtained with the yttrium co-doping to the ZrO₂:Yb³⁺,Er³⁺ up-converting phosphors was studied. The materials were prepared with the combustion method. The materials purity was analyzed with the FT-IR spectroscopy. The crystal structure was studied with the X-ray powder diffraction and the crystallite sizes were estimated with the Scherrer formula. Up-conversion luminescence was excited at room temperature with an IR-laser at 970 nm. The up-conversion luminescence spectra showed red (650-685 nm) and green emission (520-560 nm) due to the ⁴F_9/2→⁴I_15/2 and (²H_11/2,⁴S_3/2)→⁴I_15/2 transitions of Er³⁺, respectively. Persistent up-conversion luminescence was observed both in the Yb³⁺,Er³⁺ and Y³⁺,Yb³⁺,Er³⁺ doped materials.     

Er3+，Er3+/Yb3+掺杂氟化镧超微材料的光谱特性与上转换发光

采用共沉淀法制备了Er³⁺掺杂和Er³⁺/Yb³⁺共掺杂LaF₃超微材料,所制备的样品的颗粒呈球形,尺寸为250nm左右.计算得到Er³⁺单掺杂样品中对应着⁴S_3/2和⁴F_9/2能级的发光量子效率分别为67.0%和71.9%.研究发现,随着Yb³⁺离子浓度的增加 关键词： 3+')" href="#">Er³⁺ 3+')" href="#">Yb³⁺ 发光 能量传递     

White up-conversion emission in Ho/Tm/Yb tri-doped glass ceramics embedding BaF2 nanocrystals

Ho³⁺/Tm³⁺/Yb³⁺ tri-doped glass ceramics with white light emitting have been developed and demonstrated. Pumped by 980 nm laser diode (LD), intensive red, green and blue up-conversions (UC) were obtained. The green emission is assigned to Ho³⁺ ion and the blue emission is assigned to Tm³⁺ ion, whereas the red emission is the combination contribution of the Ho³⁺ and Tm³⁺ ions. The RGB intensities could be adjusted by tuning the rare-earth ion concentration and pump power intensity. Thus, multicolor of the luminescence, including perfect white light with CIE-X=0.329 and CIE-Y=0.342 in the 1931 CIE chromaticity diagram can be obtained in 0.15 Ho³⁺/0.2Tm³⁺/3Yb³⁺ tri-doped glass ceramics embedding BaF₂ nanocrystals pumped by a single infrared laser diode source of 980 nm at 500 mW. The up-conversion luminescence mechanism of Yb³⁺ sensitize Ho³⁺ and Tm³⁺ ions and the energy transfer from Ho³⁺ to Tm³⁺ in oxy-fluoride silicate glass ceramics were analyzed.