Luminescence properties of Y2WO6:Eu incorporated with Mo or Bi ions as red phosphors for light-emitting diode applications

In this study, the red phosphors, Y₂W_1−xMo_xO₆:Eu³⁺ and Y₂WO₆:Eu³⁺,Bi³⁺, have been investigated for light-emitting diode (LED) applications. In Y₂WO₆:Eu³⁺, the excitation band edge shifts to longer wavelength with the incorporation of Mo⁶⁺ or Bi³⁺ ions. The emission spectra exhibit ⁵D₀→⁷F₁ and ⁵D₀→⁷F₂ transition of Eu³⁺ ion at 588, 593, and 610 nm, respectively. Moreover, the bluish-green luminescence of the WO₆⁶⁻ at about 460 nm is observed to decrease with the incorporation of Mo⁶⁺, which results in pure red color. Thus, this study shows that the red phosphor, Y₂WO₆:Eu³⁺, incorporated with Mo⁶⁺ or Bi³⁺ ions is advantageous for LEDs applications.     

Synthesis and luminescence properties of europium doped YBa3B9O18

Europium (Eu³⁺) doped YBa₃B₉O₁₈ were synthesized by conventional solid state solidification methods. (Y_1−xEu_x)Ba₃B₉O₁₈ formed solid solutions in the range of x=0–1.0. The luminescence property measurements upon excitation in ultraviolet–visible range show well-known Eu³⁺ excitation and emission. The charge transfer excitation band of Eu³⁺ dominates the excitation spectra. The emission spectrum of Eu³⁺ ions consists mainly of several groups of lines in the 550–720 nm region, due to the transitions from the ⁵D₀ level to the levels ⁷F_J (J=0, 1, 2, 3, 4) of Eu³⁺ ions. The dependence of luminescence intensity on Eu³⁺ concentration shows no concentration quenching for fully concentrated EuBa₃B₉O₁₈. Eu³⁺ doped YBa₃B₉O₁₈ are promising phosphors for applications in displays and optical devices.     

Luminescent properties of HTP AgGd1−xW2O8:Eux and AgGd1−x(W1−yMoy)2O8:Eux phosphor for white LED

Intense red phosphors, AgGd_1−xEu_x(W_1−yMo_y)₂O₈ (x=0.0-1.0, y=0.0-1.0), have been synthesized through traditional solid-state reaction and characterized by X-ray diffraction (XRD) and photoluminescence (PL). XRD results reveal that AgGd_1−xEu_xW₂O₈ synthesized at 1000 °C has a tetragonal crystal structure, which is named as high temperature phase (HTP) AgGdW₂O₈. All phosphors compositions with Eu³⁺ show red and green emission on excitation either in the charge-transfer or Eu³⁺ levels. Analysis of the emission spectra with different Eu³⁺ concentrations reveal that the optimum dopant concentration for Eu³⁺ is x=0.6 in the HTP AgGd_1−xEu_xW₂O₈ (x=0.0-1.0). Studies on the AgGd_0.4Eu_0.6(W_1−yMo_y)₂O₈ (y=0.0-1.0) and AgGd_1−xEu_x(W_0.7Mo_0.3)₂O₈ (x=0.0-1.0) show that the emission intensity is maximum for compositions with y=0.3 and x=0.5, respectively, and a decrease in emission intensity is observed for higher y or x values. The Mo⁶⁺ and Eu³⁺ co-doped AgGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped AgGd(WO₄)₂ in UV region. The intense emission of the tungstate/molybdate phosphors under 394 and 465 nm excitations, respectively, suggests that these materials are promising candidates as red-emitting phosphors for near-UV/blue GaN-based white LED for white light generation.     

Photoluminescence properties of Eu in Y(PO3)3 under VUV excitation

The photoluminescence properties of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) are investigated. The excitation spectrum of Y_0.85(PO₃)₃:0.15Eu₃⁺ shows that both the (PO₃)₃³⁻ groups and the CT bands of O²⁻-Y³⁺ can efficiently absorb the excitation energy in the region of 120-250 nm. Under 147 nm excitation, the optimal emissive intensity of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) is about 36% of the commercial phosphor (Y,Gd)BO₃:Eu³⁺, which hints that the absorbed energy by the host matrix could be efficiently transferred to Eu³⁺. We try to study the concentration quenching mechanism of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) under 147 and 172 nm excitation.     

Abnormally enhanced Eu emission in Y2O2SO4:Eu inherited from their precursory dodecylsulfate-templated concentric-layered nanostructure

A new nanostructure-mediated approach was demonstrated to synthesize Eu³⁺-doped yttrium oxysulfates Y₂O₂SO₄:Eu³⁺ giving rise to abnormally enhanced Eu³⁺ emission. Yttrium and europium salts, sodium dodecylsulfate (SDS), and urea at various Eu³⁺ concentrations were reacted in aqueous solution at 80, 85, and 87 °C to yield Eu³⁺-doped dodecylsulfate-templated yttrium oxide mesophases with straight-layered (S-type), concentric-layered (C-type) and layer-to-hexagonal transient-layered (T-type) structures, respectively. On calcination at 1000 °C, all of these mesophases were converted into Y₂O₂SO₄:Eu³⁺ to exhibit luminescence bands including the ⁵D₀-⁷F₂ transition with a tendency in intensity to saturate or reach a maximum at 10-12 mol% Eu doping. The Eu³⁺ emissions for Y₂O₂SO₄:Eu³⁺ mediated by the T- and C-type mesophases were enhanced in intensity by a factor of about two and three times, respectively, stronger than those for not only compositionally the same sulfate Y₂O₂SO₄:Eu³⁺ obtained from yttrium-based sulfates but also Y₂O₃:Eu³⁺ obtained in the SDS-free system. In contrast, the emission intensities for the S-type-mesophase-mediated Y₂O₂SO₄:Eu³⁺ were close to those for the latter sulfates. The abnormally enhanced emission is likely based on specific deformation of sulfate groups induced through the conversion of concentric dodecylsulfate-layers to straight sulfate-layers in the oxysulfate framework upon calcination.     

Low-voltage cathodoluminescence property of Li-doped Gd2−xYxO3:Eu

Cathodoluminescent (CL) spectra of Li-doped Gd_2−xY_xO₃:Eu³⁺ solid-solution (0.0?x?0.8) were investigated at low voltages (300 V-1 kV). The CL intensity is maximum for the composition of x=0.2 and gradually reduces with increasing the amount of substituted Y content. In particular, small (∼100 nm) particles of Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ are obtained by firing the citrate precursors at only 650°C for 18 h. Relative red-emission intensity at 300 V of this phosphor is close to 180% in comparison with that of commercial red phosphor Y₂O₃:Eu³⁺. An increase of firing temperature to 900°C results in 400-600 nm sized spherical particles. At low voltages (300-800 V), the CL emission of 100 nm sized particles is much stronger than that of 400-600 nm sized ones. In contrast, the larger particles exhibit the higher CL emission intensity at high voltages (1-10 kV). Taking into consideration small spherical morphology and effective CL emission, Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ appears to be an efficient phosphor material for low voltage field emission display.     

Effect of Eu,Tb codoping on the luminescent properties of Y2O3 nanorods

Red-emitting Y₂O₃:Eu³⁺ and green-emitting Y₂O₃:Tb³⁺ and Y₂O₃:Eu³⁺, Tb³⁺ nanorods were synthesized by hydrothermal method. Their structure and micromorphology have been analyzed by X-ray powder diffraction (XRD) and transmission electron microscopy (TEM). The photoluminescence (PL) property of Y₂O₃:Eu³⁺,Tb³⁺ phosphor was investigated. In the same host (Y₂O₃), upon excitation with ultraviolet (UV) irradiation, it is shown that there are strong emissions at around 610 and 545 nm corresponding to the forced electric dipole ⁵D₀-⁷F₂ transition of Eu³⁺ and ⁵D₄-⁷F₅ transition of Tb³⁺, respectively. Different qualities of Eu³⁺and Tb³⁺ ions are induced into the Y₂O₃ lattice. From the excitation spectrum, we speculate that there exists energy transfer from Tb³⁺ to Eu³⁺ ions .The emission color of powders reveals regular change in the separation of light emission. These powders can meet with the request of optical display material for different colors or can be potentially used as labels for biological molecules.     

Luminescence characteristics of Eu3+ activated borate phosphor for white light emitting diode

In this paper, the Sr₃Y₂ (BO₃)₄:Eu³⁺ phosphor was synthesized by high temperature solid-state reaction method and the luminescence characteristics were investigated. The emission spectrum exhibits one strong red emission at 613nm corresponding to the electric dipole ⁵D₀--⁷F₂ transition of Eu³⁺ under 365nm excitation, this is because Eu³⁺ substituted for Y³⁺ occupied the non-centrosymmetric position in the crystal structure of Sr₃Y₂ (BO₃)₄. The excitation spectrum indicates that the phosphor can be effectively excited by ultraviolet (254nm, 365nm and 400nm) and blue (470nm) light. The effect of Eu³⁺ concentration on the red emission of Sr₃Y₂ (BO₃)₄:Eu³⁺ was measured, the result shows that the emission intensities increase with increasing Eu³⁺ concentration, then decrease. The Commission Internationale del'Eclairage chromaticity (x, y) of Sr₃Y₂(BO₃)₄:Eu³⁺ phosphor is (0.640,0.355) at 15 mol% Eu³⁺.     

Investigation of crystallographic sites of Eu in La2BaZnO5 by site-selective laser-excitation spectroscopy

La₂BaZnO₅:Eu³⁺ (0.05 mol%) was prepared by a solid-state reaction at high temperature. X-ray powder diffraction analysis confirmed the formation of single phase La₂BaZnO₅. Luminescence properties of La₂BaZnO₅:Eu³⁺ are investigated by site-selective laser-excitation and emission spectroscopy at 18 K. Two different crystallographic sites for Eu³⁺ corresponding to the La³⁺ and Ba²⁺ sites are identified from the ⁷F₀→⁵D₀ excitation spectra obtained by monitoring the ⁵D₀→⁷F_J (J=1, 2, …, 6) emissions. It is found that Eu³⁺ substituted for the Ba²⁺ ion experiences stronger crystal-field strength than Eu³⁺ substituted for the La³⁺ ion. Energy transfer between the two crystallographic Eu³⁺ centers is investigated by luminescence decay curves at 18 K.     

Preparation and photoluminescence characteristics of Eu-doped MgAl1.8Y0.2O4 nanocrystals

A simple combustion route was employed for the preparation of Eu³⁺-doped MgAl_1.8Y_0.2−xO₄ nanocrystals using metal nitrates as precursors and urea as a fuel in a preheated furnace at 500 °C. The powders thus obtained were then fired at 1000 °C for 3 h to get better luminescent properties. The incorporation of Eu³⁺ activator in these nanocrystals was checked by luminescence characteristics. These nanocrystals displayed bright red color on excitation under 254 nm UV source. The main emission peak was assigned to the transition [⁵D₀→⁷F₂] at 615 nm. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) studies were carried out to understand surface morphological features and the particle size. Crystal structures of the nanocrystals were investigated by the X-ray diffraction (XRD) technique. The crystallite size of the as-prepared nanocrystals was around 29 nm, which was evaluated from the broad XRD peaks. The crystallite size increased to ∼45 nm on further heat treatment at 1000 °C.     

Emission analysis of Pr and Tm: Ca2Gd2W3O14 phosphors

5 mol% of Pr³⁺ and Tm³⁺ ions activated calcium gadolinium tungstate (Ca₂Gd₂W₃O₁₄₎ phosphors were synthesized by traditional solid state reaction method. Crystalline phase structure was identified from the X-ray diffraction (XRD) profiles. From the scanning electron microscopy (SEM) images, we have observed the agglomeration of the particles, and average grain size is around 40-300 nm. Using the energy dispersive X-ray analysis (EDAX) and Fourier transform infrared (FTIR) spectra, identified the elements and functional groups present in the prepared phosphors. The emission spectrum of Pr³⁺: Ca₂Gd₂W₃O₁₄ powder phosphors have shown an intense red emission at 615 nm with the excitation wavelength λ_exci=450 nm and thus these red color emitting powder phosphors are used as one of the components in the preparation of WLEDs. The excitation spectrum of Tm³⁺: Ca₂Gd₂W₃O₁₄ powder phosphor has shown a ligand to metal charge transfer (W-O) band (LMCT) within the WO₄²⁻ group. Emission spectrum of Tm³⁺: Ca₂Gd₂W₃O₁₄ phosphors have shown blue emissions at 453 nm (¹D₂→³F₄).     

Luminescent properties of green- or red-emitting Eu-doped Sr3Al2O6 for LED

Eu²⁺-doped Sr₃Al₂O₆ (Sr_3−xEu_xAl₂O₆) was synthesized by a solid-state reaction under either H₂ and N₂ atmosphere or CO atmosphere. When H₂ was used as the reducing agent, the phosphor exhibited green emission under near UV excitation, while CO was used as the reducing agent, the phosphor mainly showed red emission under blue light excitation. Both emissions belong to the d-f transition of Eu²⁺ ion. The relationship between the emission wavelengths and the occupation of Eu²⁺ at different crystallographic sites was studied. The preferential substitution of Eu²⁺ into different Sr²⁺ cites at different reaction periods and the substitution rates under different atmospheres were discussed. Finally, green-emitting and red-emitting LEDs were fabricated by coating the phosphor onto near UV- or blue-emitting InGaN chips.     

Enhanced luminescence of Dy in Y3Al5O12 by Bi co-doping

In the present paper, phosphors with the composition Y_3−x−yAl₅O₁₂:Bi³⁺_x, Dy³⁺_y were synthesized with solid state reactions. The luminescence properties of Bi³⁺ and Dy³⁺ in Y₃Al₅O₁₂(YAG) and the energy transfer from Bi³⁺ to Dy³⁺ were investigated in detail. Bi³⁺ in YAG emits one broad band peaking at 304 nm which can be ascribed to the transition from excited states ³P_{0, 1} to ground state ¹S₀. Dy³⁺ in YAG emits two groups of peaks around 484 and 583 nm, respectively, which can be ascribed to the transitions from excited state ⁴F_9/2 to ground states ⁶H_15/2 and ⁶H_13/2. The co-doping of Bi³⁺ enhances the luminescent intensity of Dy³⁺ by ∼7 times because Bi³⁺ can transfer the absorbed energy to Dy³⁺ efficiently. The mechanism of energy transfer was also discussed.     

Photoluminescence properties of Sr(Y, Gd)2O4:Euunder VUV excitation

Vacuum ultraviolet (VUV) excitation and photoluminescence (PL) properties of Sr(Y, Gd)₂O₄ doped with Eu³⁺ were studied. The excitation spectra of SrY_1.9Eu_0.1O₄ and SrY_1.0Gd_0.9Eu_0.1O₄ had absorption in the VUV region with the absorption band edge at 149 nm, while the absorption of SrGd_1.9Eu_0.1O₄ in the VUV region was weak, which could be due to the narrow host band gap and no efficient energy transfer occurred in the VUV region. The PL spectra of all samples exhibited the characteristic emission of Eu³⁺ with the red ⁵D₀-⁷F₂ transition (611 nm) being the most prominent group.     

Synthesis of Y2Si2O7:Eu nanocrystal and its optical properties

Nanocrystalline Y₂Si₂O₇:Eu phosphor with an average size about 60 nm is easily prepared using silica aerogel as raw material under ultrasonic irradiation and annealing temperature at 300-600 °C and this nanocrystalline decomposes into Y₂O₃:Eu and silica by heat treatment at 700-900 °C. The excitation broad band centered at 283 and 254 nm results from Eu³⁺ substituting for Y³⁺ in Y₂Si₂O₇ and Y₂O₃/SiO₂, respectively. Compared with Y₂O₃:Eu/SiO₂ crystalline, the PL excitation and emission peaks of Y₂Si₂O₇:Eu nanocrystalline red-shift and lead to the enhance of its luminescence intensity due to the different chemical surroundings of Eu³⁺ in above nanocrystallines. The decrease of PL intensity may be ascribed to quenching effect resulting from more defects in Y₂O₃:Eu/SiO₂ crystalline.     

Effect of concentration on the luminescence of Eu ions in nanocrystalline La2O3

Nanocrystalline powders with various Eu³⁺ concentration (from 1 to 10 mol %) doped La₂O₃ were prepared via a combustion route. Their structure and morphology were characterized using X-ray diffraction (XRD) and High-resolution transmission electron microscopy. The emission spectra of the as-synthesized samples show that the strongest emission position is centered at 626 nm corresponding to ⁵D₀→⁷F₂ transition of Eu³⁺ ions and the intensity change of 626 nm emission is considered as a function of ultraviolet (240 nm) irradiation time. The excitation spectra at 626 nm monitoring indicate that the charge transfer state band is varies with different Eu³⁺ ion concentration. These results are attributed to the surface defects of the nanocrystals.     

Synthesis of Gd2Ti2O7:Eu, V phosphors by sol-gel process and its luminescent properties

A red-emitting phosphor material, Gd₂Ti₂O₇:Eu³⁺, V⁴⁺, by added vanadium ions is synthesized using the sol-gel method. Phosphor characterization by high-resolution transmission electron microscopy shows that the phosphor possesses a good crystalline structure, while scanning electron microscopy reveals a uniform phosphor particle size in the range of 230-270 nm. X-ray photon electron spectrum analysis demonstrates that the V⁴⁺ ion promotes an electron dipole transition of Gd₂Ti₂O₇:Eu³⁺ phosphors, causing a new red-emitting phenomenon, and CIE value shifts to x=0.63, y=0.34 (a purer red region) from x=0.57, y=0.33 (CIE of Gd₂Ti₂O₇:Eu³⁺). The optimal composition of the novel red-emitting phosphor is about 26% of V⁴⁺ ions while the material is calcinated at 800  °C. The results of electroluminescent property of the material by field emission experiment by CNT-contained cathode agreed well with that of photoluminescent analysis.     

A potential reddish orange emitting phosphor Ca2BO3Cl:Eu for white light-emitting diodes

A series of phosphors Ca₂BO₃Cl:Eu³⁺ were synthesized by using a high-temperature solid-state reaction technique, and their UV–vis luminescence properties were investigated. The f–f transitions of Eu³⁺ in the host lattice were assigned and discussed. The excitation and emission spectra indicate that this phosphor can be effectively excited by ultraviolet (394 nm), and exhibit reddish orange emission corresponding to the ⁵D₀→⁷F_J (J=0, 1, 2) transitions of Eu³⁺. The influence of the doping concentration and charge compensators on the relative emission intensity of Eu³⁺ was investigated, and the optimum doping concentration is 0.04. The critical distance R_c was estimated to be 17.1 Å in terms of the concentration quenching data. The present study suggests that Ca₂BO₃Cl:Eu³⁺ can be a potential candidate as an UV-convertible phosphor for white light-emitting diodes (LEDs).     

A white light emitting phosphor Sr1.5Ca0.5SiO4:Eu, Tb, Eu for LED-based near-UV chip: Preparation, characterization and luminescent mechanism

In this work, we report preparation, characterization and luminescent mechanism of a phosphor Sr_1.5Ca_0.5SiO₄:Eu³⁺,Tb³⁺,Eu²⁺ (SCS:ETE) for white-light emitting diode (W-LED)-based near-UV chip. Co-doped rare earth cations Eu³⁺, Tb³⁺ and Eu²⁺ as aggregated luminescent centers within the orthosilicate host in a controlled manner resulted in the white-light phosphors with tunable emission properties. Under the excitation of near-UV light (394 nm), the emission spectra of these phosphors exhibited three emission bands: one broad band in the blue area, a second band with sharp lines peaked in green (about 548 nm) and the third band in the orange-red region (588-720 nm). These bands originated from Eu²⁺ 5d→4f, Tb³⁺⁵D₄→⁷F_J and Eu³⁺⁵D₀→⁷F_J transitions, respectively, with comparable intensities, which in return resulted in white light emission. With anincrease of Tb³⁺ content, both broad Eu²⁺ emission and sharp Eu³⁺ emission increase. The former may be understood by the reduction mechanism due to the charge transfer process from Eu³⁺ to Tb³⁺, whereas the latter is attributed to the energy transfer process from Eu²⁺ to Tb³⁺. Tunable white-light emission resulted from the system of SCS:ETE as a result of the competition between these two processes when the Tb³⁺ concentration varies. It was found that the nominal composition Sr_1.5Ca_0.5SiO₄:1.0%Eu³⁺, 0.07%Tb³⁺ is the optimal composition for single-phased white-light phosphor. The CIE chromaticity calculation demonstrated its potential as white LED-based near-UV chip.     

Synthesis and luminescent properties of nanoparticles GdCaAl3O7:RE (RE=Eu, Tb) via the sol-gel method

By using metal nitrates as starting materials and citric acid as complexing agent, GdCaAl₃O₇:Eu³⁺ and GdCaAl₃O₇:Tb³⁺ powder phosphors were prepared by a citrate-gel method. Thermal analysis (TG-DTG), X-ray diffraction (XRD), transmission electron microscope (TEM) and scanning electron microscope (SEM), photoluminescence excitation and emission, as well as kinetic decays were employed to characterize the resulting samples. The results of the XRD indicated the precursor samples began to crystallize at 800 °C and the crystallinity increased with elevation the annealing temperature. TEM images showed that the phosphor particles were basically of spherical shape, with good dispersion about a particle size of around 40-70 nm. Upon excitation with UV irradiation, it is shown that there is a strong emission at around 617 nm corresponding to the forced electric dipole ⁵D₀-⁷F₂ transition of Eu³⁺, and at around 543 nm corresponding to the ⁵D₄-⁷F₅ transition of Tb³⁺. The dependence of photoluminescence intensity on Eu³⁺ (or Tb³⁺) concentration and annealing temperature were also studied in detail.