燃料电池用磺化聚酰亚胺质子交换膜材料的制备与性质

以联萘二酐、磺化二胺和含咪唑基团的非磺化二胺单体为原料,制备了一系列高相对分子质量的磺化聚酰亚胺,该类聚合物具有优异的溶解性和良好的成膜性.得到的质子交换膜具有优异的水解稳定性.苯并咪唑碱性基团的存在提高了磺化聚酰亚胺质子交换膜膜的溶胀稳定性和热稳定性、降低了膜的甲醇透过率.质子导电率测试结果表明,IEC值为2.55mequiv·g-1的膜室温条件下的质子导电率为0.121 S·cm-1,高于在相同测试条件下Nafion 117膜的质子导电率(0.09 S·cm-1).     

Synthesis and Characterization of Sulfonated Polyphosphazene-graft-Polystyrene Copolymersfor Proton Exchange Membranes简

A novel series of polyphosphazene-grafl-polystyrene （PP-g-PS） copolymers were successfully prepared by atom transfer radical polymerization （ATRP） of styrene monomers and brominated poly（bis（4-methylphenoxy）phosphazene） macroinitiator. The graft density and the graft length could be regulated by changing the bromination degree of the macroinitiator and the ATRP reaction time, respectively. The PP-g-PS copolymers readily underwent a regioselective sulfonation reaction, which occurred preferentially at the polystyrene sites, producing the sulfonated PP-g-PS copolymers with a range of ion exchange capacities. The resulting sulfonated PP-g-PS membranes prepared by solution casting showed high water uptake, low water swelling and considerable proton conductivity. They also exhibited good oxidative stability and high resistance to methanol crossover. Morphological studies of the membranes by transmission electron microscopy showed clear nanophase-separated structures resulted from hydrophobic polyphosphazene backbone and hydrophilic polystyrene sulfonic acid segments, indicating the formation of proton transferring tunnels. Therefore, these sulfonated copolymers may be candidate materials for proton exchange membranes in direct methanol fuel cell （DMFC） applications.     

Preparation and characterization of branched and linear sulfonated poly(ether ketone sulfone) proton exchange membranes for fuel cell applications

Branched sulfonated poly(ether ketone sulfone)s (Br‐SPEKS) were prepared with bisphenol A, bis(4‐fluorophenyl)sulfone, 3,3′‐disodiumsulfonyl‐4,4′‐difluorobenzophenone, and THPE (1,1,1‐tris‐p‐hydroxyphenylethane), respectively, at 180 °C using potassium carbonate in NMP (N‐methylpyrrolidinone). THPE, as a branching agent, was used with 0.4 mol % of bisphenol A to synthesize branched copolymers. Copolymers containing 10–50 mol % disulfonated units were cast from dimethylsulfoxide solutions to form films. Linear sulfonated poly(ether ketone sulfone)s (SPEKS) were also synthesized without THPE. The films were converted from the salt to acid forms with dilute hydrochloric acid. A series of copolymers were studied by Fourier transform infrared, ¹H‐NMR spectroscopy, differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). Sorption experiments were conducted to observe the interaction of sulfonated polymers with water and methanol. The ion‐exchange capacity (IEC), a measure of proton conductivity, was evaluated. The synthesized Br‐SPEKS and SPEKS membranes exhibit conductivities (25 °C) from 1.04 × 10^?3 to 4.32 × 10^?3 S/cm, water swell from 20.18 to 62.35%, IEC from 0.24 to 0.83 mequiv/g, and methanol diffusion coefficients from 3.2 × 10^?7 to 4.7 × 10^?7 cm²/S at 25 °C. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 1792–1799, 2008     

燃料电池聚合物电解质膜的研究进展

本文根据聚合物电解质膜燃料电池操作温度、使用的电解质和燃料的不同,将其分为高温质子交换膜燃料电池、低温质子换膜燃料电池、直接甲醇燃料电池和阴离子交换膜燃料电池,综述了它们所用电解质膜的最新进展.第一部分简要介绍了这4种燃料电池的优点和不足.第二部分首先介绍了Nafion膜的结构模型,并对平行柱状纳米水通道模型在介观尺度上进行了修正;接着分别对应用于不同燃料电池的改性膜的改性思路作了分析;最后讨论了用于不同燃料电池的新型质子交换膜的研究,同时列举了性能突出的改性膜和新型质子交换膜.第三部分介绍了阴离子交换膜的研究现状.第四部分对未来聚合物电解质膜的研究作了展望.     

Sulfonated poly(ether sulfone)s with binaphthyl units as proton exchange membranes for fuel cell application

Sulfonated poly(ether sulfone)s containing binaphthyl units (BNSHs) were successfully prepared for fuel cell application. BNSHs, which have very simple structures, were easily synthesized by postsulfonation of poly(1,1′‐dinaphthyl ether phenyl sulfone)s and gave tough, flexible, and transparent membranes by solvent casting. The BNSH membranes showed low water uptake compared to a typical sulfonated poly(ether ether sulfone) (BPSH‐40) membrane with a similar ion exchange capacity (IEC) value and water insolubility, even with a high IEC values of 3.19 mequiv/g because of their rigid and bulky structures. The BNSH‐100 membrane (IEC = 3.19 mequiv/g) exhibited excellent proton conductivity, which was comparable to or even higher than that of Nafion 117, over a range of 30–95% relative humidity (RH). The excellent proton conductivity, especially under low RH conditions, suggests that the BNSH‐100 membrane has excellent proton paths because of its high IEC value, and water insolubility due to the high hydrophobicity of the binaphthyl structure. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 5827–5834, 2009     

Chemical stability enhancement of crown ether grafted sulfonated poly(arylene ether ketone) fuel cell membrane by cerium ion fixation

In operation of polymer electrolyte membrane fuel cell or direct methanol fuel cell, ·OH radicals are the major cause for the degradation of polymer electrolyte membrane. In order to enhance its antioxidation stability, cerium ion (Ce³⁺, CE), an ·OH radical quencher, is introduced to membrane, as it converts the ·OH radicals into inactive chemicals. In this study, aminoethyl‐15‐crown‐5 (CRE) is grafted on the sulfonated poly(arylene ether ketone) (SPAEK) to prevent the migration of CE ions from the membrane for long‐term antioxidation stability, as CRE forms a coordination complex with CE. The chemical and physical structures of the CRE grafted SPAEK are examined using proton nuclear magnetic resonance, energy dispersive X‐ray, and small‐angle X‐ray scattering spectroscopy. The physical properties of the CRE grafted SPAEK membrane are investigated and compared with those of the CRE blended and CE blended ones. While the grafting of CRE does not significantly affect the thermal and mechanical and water uptake behaviors of membranes, it leads to a significant improvement of antidegradation effect compared with other blend systems according to Fenton's test. The proton conductivity decreases with addition of CE but its effect is lessened by introduction of CRE. © 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019 , 57, 101–109     

A review on key factors influencing the electrical conductivity of proton exchange membrane fuel cell composite bipolar plates

Fuel cells are gaining increasing importance as a promising alternative to traditional energy sources, primarily due to their exceptional efficiency and environmental advantages. The electrical performance of proton exchange membrane fuel cells (PEMFCs) largely depends on the effectiveness of proton and electron transport within the cell components. A critical factor impacting this efficiency is the electrical conductivity of polymer-based bipolar plates (BPPs), which play a fundamental role as current collectors. BPPs in PEMFCs can be made from various materials including coated metallic materials, graphitic materials, and polymer composites. This review exclusively concentrates on polymer composite BPPs. Enhancing the overall cell performance is achievable through the integration of electrically conductive additives into the polymer matrix of these plates. Graphite (GR), carbon black (CB), carbon fibers (CF), carbon nanotubes (CNT), and graphene (Gr) all emerge as highly promising functional materials capable of substantially elevating BPPs performance. This study, among its various objectives, delves into the synergistic effects of these electrically conductive additives and their capacity to enhance the electrical conductivity within polymeric matrices. Furthermore, this review article thoroughly explores the influence of the polymeric matrix, encompassing co-continuous morphology and processing conditions. In essence, it focuses on the improvement of BPPs electrical conductivity through innovative designs of their polymer-based composites and nanocomposites and the particular selection of the electrically conductive fillers. The insights derived from this study significantly contribute to a more profound understanding of how to effectively harness the potential of this vital PEMFC component.     

Synthesis of sulfonated poly(imidoaryl ether sulfone) membranes for polymer electrolyte membrane fuel cells

New sulfonated poly(imidoaryl ether sulfone) copolymers derived from sulfonated 4,4′‐dichlorodiphenyl sulfone, 4,4′‐dichlorodiphenyl sulfone, and imidoaryl biphenol were evaluated as polymer electrolyte membranes for direct methanol fuel cells. The sulfonated membranes were characterized with Fourier transform infrared spectroscopy, thermogravimetric analysis, and proton nuclear magnetic resonance spectra. The state of water in the membranes was measured with differential scanning calorimetry, and the existence of free water and bound water was discussed in terms of the sulfonation level. The 10 wt % weight loss temperatures of these copolymers were above 470 °C, indicating excellent thermooxidative stability to meet the severe criteria of harsh fuel‐cell conditions. The proton conductivities of the membranes ranged from 3.8 × 10^?2 to 5 × 10^?2 S/cm at 90 °C, depending on the degree of sulfonation. The sulfonated membranes maintained the original proton conductivity even after a boiling water test, and this indicated the excellent hydrolytic stability of the membranes. The methanol permeabilities ranged from 1.65 × 10^?8 to 5.14 × 10^?8 cm²/s and were lower than those of other conventional sulfonated ionomer membranes, particularly commercial perfluorinated sulfonated ionomer (Nafion). The properties of proton and methanol transport were discussed with respect to the state of water in the membranes. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 5620–5631, 2005     

Evaluation of proton conductivity of sulfonated polyimide/dihydroxy naphthalene charge‐transfer complex hybrid membranes

Sulfonated polyimide (SPI)/dihydroxynaphthalene (DHN) charge‐transfer (CT) complex hybrid films were investigated as possible alternative for polymer electrolyte membranes in polymer electrolyte fuel cells. SPI/DHN CT complex hybrid films include CT complexes, which might work as electronic conductors, and sulfonic acid units, which could work as proton conductors. Therefore, the origin of the conductivity of SPI/DHN complex hybrid films was evaluated by four‐probe impedance measurements in the through‐plane direction of the films. The obtained conductivity of the CT complex hybrid films increased with the increase of ion exchange capacity of the CT films and the decrease of CT complex concentration in the films. These results indicated that proton transfer dominantly occurred in the CT complex hybrid films. Proton conductivity of the CT complex hybrid films consisting of 2,6‐ or 1,5‐DHN showed the similar values, although the molecular geometries of the CT complex were different. The activation energy values for proton conductivity in the CT films were approximately the same as that of Nafion 212. Water uptake (WU) results were also conducted and suggest that CT complex formation could control the degree of WU of the films and prevent dissolution of SPI. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 2991–2997     

Preparation of Nafion/sulfonated poly(phenylsilsesquioxane) nanocomposite as high temperature proton exchange membranes

Nafion/sulfonated poly(phenylmethyl silsesquioxane) (sPPSQ) composite membranes are fabricated using homogeneous dispersive mixing and a solvent casting method for direct dimethyl ether fuel cell (DDMEFC) applications operated above 100 °C. The inorganic conducting filler, sPPSQ significantly affects the characteristics in the nanocomposite membranes by functionalization with an organic sulfonic acid to PPSQ. Moreover, sPPSQ content plays an important role in membrane properties such as microstructure, proton conductivity, fuel crossover, and single cell performance test. With increasing sPPSQ content in the nanocomposite membrane, the proton conductivity increased and fuel crossover decreased. However, in a higher temperature range above 110 °C, Nafion/sPPSQ 5 wt.% composite membrane has the highest proton conductivity. Also, the DME permeability for the composite membrane with higher sPPSQ content increased sharply. The excessive sPPSQ content caused a large aggregation of inorganic fillers, leading to the deterioration of membrane properties. In this study, the optimal sPPSQ content for maximizing the DDMEFC performance was 5 wt.%. Our nanocomposite membranes demonstrated proton conductivities as high as 1.57 × 10⁻¹ S/cm at 120 °C, which is higher than that of Nafion. The cell performances were compared to Nafion/sPPSQ composite membrane with Nafion 115, and the composite membrane with sPPSQ yielded better cell performance than Nafion 115 at temperatures ranging from 100 to 120 °C and at pressures from 1 to 2 bar.     

Mechanical endurance of polymer electrolyte membrane and PEM fuel cell durability

The life of proton exchange membrane fuel cells (PEMFC) is currently limited by the mechanical endurance of polymer electrolyte membranes and membrane electrode assemblies (MEAs). In this paper, the authors report recent experimental and modeling work toward understanding the mechanisms of delayed mechanical failures of polymer electrolyte membranes and MEAs under relevant PEMFC operating conditions. Mechanical breach of membranes/MEAs in the form of pinholes and tears has been frequently observed after long‐term or accelerated testing of PEMFC cells/stacks. Catastrophic failure of cell/stack due to rapid gas crossover shortly follows the mechanical breach. Ex situ mechanical characterizations were performed on MEAs after being subjected to the accelerated chemical aging and relative humidity (RH) cycling tests. The results showed significant reduction of MEA ductility manifested as drastically reduced strain‐to‐failure of the chemically aged and RH‐cycled MEAs. Postmortem analysis revealed the formation and growth of mechanical defects such as cracks and crazing in the membranes and MEAs. A finite element model was used to estimate stress/strain states of an edge‐constrained MEA under rapid RH variations. Damage metrics for accelerated testing and life prediction of PEMFCs are discussed. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2346–2357, 2006     

Synthesis and properties of novel sulfonated (co)polyimides bearing sulfonated aromatic pendant groups for PEFC applications

Novel sulfonated diamines bearing aromatic pendant groups, namely, 3,5‐diamino‐3′‐sulfo‐4′‐(4‐sulfophenoxy) benzophenone (DASSPB) and 3,5‐diamino‐3′‐sulfo‐4′‐(2,4‐disulfophenoxy) benzophenone (DASDSPB), were successfully synthesized. Novel side‐chain‐type sulfonated (co)polyimides (SPIs) were synthesized from these two diamines, 1,4,5,8‐naphthalene tetracarboxylic dianhydride (NTDA) and nonsulfonated diamines such as 4,4′‐bis(3‐aminophenoxy) phenyl sulfone (BAPPS). Tough and transparent membranes of SPIs with ion exchange capacity of 1.5–2.9 meq g^?1 were prepared. They showed good solubility and high thermal stability up to 300 °C. They showed isotropic membrane swelling in water, which was different from the main‐chain‐type and sulfoalkoxy‐based side‐chain‐type SPIs. The relative humidity (RH) and temperature dependence of proton conductivity were examined. At low RH, the novel SPI membranes showed much higher conductivity than the sulfoalkoxy‐based SPIs. They showed comparable or even higher proton conductivity than Nafion 112 in water at 60 °C (>0.10 S cm^?1). The membrane of NTDA‐DASDSPB/BAPPS (1/1)‐s displayed reasonably high proton conductivities of 0.05 and 0.30 S cm^?1 at 50 and 100% RH, respectively, at 120 °C. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2862–2872, 2006     

Synthesis and properties of highly branched sulfonated poly(arylene ether)s as proton exchange membranes

A series of branched sulfonated poly(arylene ether)s were successfully synthesized using 1,3,5-tris[4-(4-fluorobenzoyl)phenoxy]benzene (B₃) as branching agent. The synthesized branched copolymers were soluble in polar organic solvents, such as N-methyl-2-pyrrolidone (NMP), N,N-dimethylacetamide (DMAc) and dimethylsulfoxide (DMSO), and could be cast to form tough and smooth films. The effect of degree of branching (DB) on the proton conductivity, swelling ratio and oxidative stability of the membranes was investigated. With increasing DB value, the proton conductivity and oxidative stability of the membranes increased. A maximum oxidative stability of the branched membrane with 4% of DB value was determined to be 3.4 times larger than that of the linear membrane. In addition, as the DB value increased, the swelling ratio of the membranes decreased from 13.51% to 9.09% at 80 °C. The results indicated that increasing DB value might be an effective way to improve the properties of proton exchange membranes.     

Highly sulfonated multiblock copoly(ether sulfone)s for fuel cell membranes

Highly sulfonated multiblock copoly(ether sulfone)s applicable to proton electrolyte fuel cells (PEFCs) were synthesized by the coupling reaction of corresponding hydroxyl‐ terminated oligomers in the presence of highly reactive decafluorobiphenyl (DFB) as a chain extender, followed by postsulfonation with concentrated sulfuric acid. Their molecular weights were reasonably high as determined by viscosity measurement (η_inh = 0.72–1.58 dL/g). It was also confirmed that postsulfonation selectively took place in hydrophilic segments to yield highly sulfonated multiblock copolymers (IEC = 1.90–2.75 mequiv/g). The resulting polymers gave transparent, flexible, and tough membranes by solution casting. The 4b membrane, as a representative sample, demonstrated good mechanical strength in the dry state regardless of high IEC value (2.75 mequiv/g). The 4a–c membranes with higher IEC values (IEC = 2.75–2.79 mequiv/g) maintained high water uptake (13.7–17.7 wt %) at 50% RH and it was still high (7.4–8.5 wt %) at 30% RH. Proton conductivity of all membranes at 80 °C and 95% RH was higher than that of Nafion 117. Furthermore, the 4a membrane showed high proton conductivity, comparable with Nafion 117 in the range of 50–95% RH, and maintained high proton conductivity (2.3 × 10^?3 S/cm) even at 30% RH. Finally, the surface morphology of the membrane was investigated by tapping mode atomic force microscopy, which showed well‐connected hydrophilic domains that could work as proton transportation channel. This phase separation and the high water uptake behavior probably contributed to high and effective proton conduction in a wide range of relative humidity. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2757–2764, 2010     

Influence of chemical composition and sequence length on the transport properties of proton exchange membranes

One of the integral parts of the fuel cell is the proton exchange membrane. Our research group has been engaged in the past few years in the synthesis of several sulfonated poly(arylene ether) random copolymers. The copolymers were varied in both the bisphenol structure as well as in the functional groups in the backbone such as sulfone and ketones. To compare the effect of sequence length, multiblock copolymers based on poly(arylene ether sulfone)s were synthesized. This paper aims to describe our investigation of the effect of chemical composition, morphology, and ion exchange capacity (IEC) on the transport properties of proton conducting membranes. The key properties examined were proton conductivity, methanol permeability, and water self diffusion coefficient in the membranes. It was observed that under fully hydrated conditions, proton conductivity for both random and block copolymers was a function of IEC and water uptake. However, under partially hydrated conditions, the block copolymers showed improved proton conductivity over the random copolymers. The proton conductivity for the block copolymer series was found to increase with increasing block lengths under partially hydrated conditions. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2226–2239, 2006     

Characterization and performance of proton exchange membranes for direct methanol fuel cell: Blending of sulfonated poly(ether ether ketone) with charged surface modifying macromolecule

Modification of sulfonated poly(ether ether ketone) (SPEEK) membrane was attempted by blending charged surface modifying macromolecule (cSMM). The modified membrane was tested for direct methanol fuel cell (DMFC) application; i.e. a SPEEK/cSMM blend membrane was compared to a SPEEK membrane and a Nafion 112 membrane for the thermal and mechanical stability, methanol permeability, and proton conductivity. Thermal and mechanical stability of the blended membrane were slightly reduced from the SPEEK membrane but still higher than the Nafion 112 membrane. The blend membrane was found to be promising for DMFC applications because of its lower methanol diffusivity (2.75 × 10⁻⁷ cm² s⁻¹) and higher proton conductivity (6.4 × 10⁻³ S cm⁻¹), than the SPEEK membrane. A plausible explanation was given for the favorable effect of cSMM blending.     

Locally sulfonated poly(ether sulfone)s with highly sulfonated units as proton exchange membrane

Novel locally sulfonated poly(ether sulfone)s with highly sulfonated units were successfully synthesized for fuel cell applications. Poly(ether sulfone)s were prepared by the nucleophilic substitution of bis(4‐fluorophenyl) sulfone with 1,2,4,5‐tetrakis([1,1′‐biphenyl]‐2‐oxy)‐3,6‐bis(4‐hydroxyphenoxy)benzene and bis(4‐hydroxyphenyl) sulfide, followed by oxidation using m‐chloroperoxybenzoic acid. The desired highly sulfonated units were easily introduced by postsulfonation and each one had ten sulfonic acid groups. The sulfonated polymers gave tough, flexible, and transparent membranes by solvent casting. The high contrast in polarity between highly sulfonated units and hydrophobic poly(ether sulfone) units enabled the formation of defined phase‐separated structures and well‐connected proton paths. The sulfonated polymers exhibited excellent proton conductivity over a wide range of relative humidities. The proton conductivity of the sulfonated polymer with an ion exchange capacity value of 2.38 mequiv/g was comparable to that of Nafion 117 even at 30% relative humidity. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3444–3453, 2009     

Optimal method for preparing sulfonated polyaryletherketones with high ion exchange capacity by acid-catalyzed crosslinking for proton exchange membrane fuel cells

Sulfonated polyaryletherketones (SPAEK) bearing four sulfonic acid groups on the phenyl side groups were synthesized. The benzophenone moiety of polymer backbone was further reduced to benzydrol group with sodium borohydride. The membranes were crosslinked by acid-catalyzed Friedel-Crafts reaction without sacrifice of sulfonic acid groups and ion exchange capacity (IEC) values. Crosslinked membranes with the same IEC value but different water uptake could be prepared. The optimal crosslinking condition was investigated to achieve lower water uptake, better chemical stability (Fenton's test), and higher proton conductivity. In addition, the hydrophilic ionic channels from originally course and disordered could be modified to be narrow and continuous by this crosslinking method. The crosslinked membranes, CS4PH-40-PEKOH (IEC = 2.4 meq./g), reduced water uptake from 200 to 88% and the weight loss was reduced from 11 to 5% during the Fenton test compared to uncrosslinked one (S4PH-40-PEK). The membrane showed comparable proton conductivity (0.01–0.19 S/cm) to Nafion 212 at 80°C from low to high relative humidity (RH). Single H₂/O₂ fuel cell based on the crosslinked SPAEK with catalyst loading of 0.25 mg/cm² (Pd/C) exhibited a peak power density of 220.3 mW/cm², which was close to that of Nafion 212 (214.0 mW/cm²) at 80°C under 53% RH. These membranes provide a good option as proton exchange membrane with high ion exchange capacity for fuel cells.     

Gas diffusion electrodes for polymer electrolyte fuel cell using sulfonated polyimide

Gas diffusion electrodes for high temperature polymer electrolyte fuel cells (PEFCs) have been prepared by using a novel proton conductive sulfonated polyimide (SPI) electrolyte. The catalyst layer was composed of Pt-loaded carbon black (Pt-CB) and SPI ionomer. The polarization properties and the microstructure of the catalyst layer were investigated as a function of the SPI/CB weight ratio. The anodic polarization was found to be negligibly small for all the compositions examined. The highest cathode performance was obtained at SPI/CB = 0.5 (by weight), where the best balance of high catalyst utilization and oxygen gas diffusion rate through the ionomer was obtained.     

Doping phosphoric acid in polybenzimidazole membranes for high temperature proton exchange membrane fuel cells

Polybenzimidazole (PBI) membranes were doped in phosphoric acid solutions of different concentrations at room temperature. The doping chemistry was studied using the Scatchard method. The energy distribution of the acid complexation in polymer membranes is heterogeneous, that is, there are two different types of sites in PBI for the acid doping. The protonation constants of PBI by phosphoric acid are found to be 12.7 L mol^?1 (K¹) for acid complexing sites with higher affinity, and 0.19 L mol^?1 (K²) for the sites with lower affinity. The dissociation constants for the complexing acid onto these two types of PBI sites are found to be 5.4 × 10^?4 and 3.6 × 10^?2, respectively, that is, about 10 times smaller than that of aqueous phosphoric acid in the first case but 5 times higher in the second. The proton conducting mechanism is also discussed. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2989–2997, 2007