Surface modification of the titanium implant using TEA CO2 laser pulses in controllable gas atmospheres - Comparative study

Interaction of a TEA CO₂ laser, operating at 10.6 μm wavelength and pulse duration of 100 ns (FWHM), with a titanium implant in various gas atmospheres was studied. The Ti implant surface modification was typically studied at the moderate laser beam energy density/fluence of 28 J/cm² in the surrounding of air, N₂, O₂ or He. The energy absorbed from the TEA CO₂ laser beam is partially converted to thermal energy, which generates a series of effects, such as melting, vaporization of the molten material, shock waves, etc. The following titanium implant surface changes and phenomena were observed, depending on the gas used: (i) creation of cone-like surface structures in the atmospheres of air, N₂ and O₂, and dominant micro-holes/pores in He ambient; (ii) hydrodynamic features, most prominent in air; (iii) formation of titanium nitride and titanium oxide layers, and (iv) occurrence of plasma in front of the implant. It can be concluded from this study that the reported laser fluence and gas ambiences can effectively be applied for enhancing the titanium implant roughness and creation of titanium oxides and nitrides on the strictly localized surface area. The appearance of plasma in front of the implants indicates relatively high temperatures created above the surface. This offers a sterilizing effect, facilitating contaminant-free conditions.     

Mg-based photocathodes prepared by ns, ps and fs PLD for the production of high brightness electron beams

Mg-based films have been prepared by pulsed laser deposition technique for photocathode applications. We have investigated the influence of pulse laser duration on morphology and photoemissive properties. Two laser sources have been used, generating pulses of 30 ns at 308 nm (XeCl excimer laser), 5 ps and 500 fs at 248 nm (KrF excimer laser) to grow Mg films onto Si and Cu substrates in high vacuum (∼10⁻⁷ Pa) and at room temperature. Morphological investigations carried out by scanning electron microscopy (SEM) have revealed that, in our experimental conditions, the number and the mean size of the droplets on the films surfaces decreases as the pulse laser duration shortens. The contamination level of Mg film surfaces have been studied by energy dispersive X-ray spectroscopy (EDX). The photoelectron performances in terms of quantum efficiency (QE) and emission stability have been tested in a UHV DC photodiode cell (10⁻⁷ Pa). Measures of the QE of the samples surfaces have revealed a decrease on the initial value for Mg-based photocathodes prepared by fs laser (from 7.8 × 10⁻⁴ to 6.6 × 10⁻⁴) PLD with respect to ps (from 6.2 × 10⁻⁴ to 7.4 × 10⁻⁴) and ns lasers (from 5.0 × 10⁻⁴ to 1.6 × 10⁻³). A comparison among Mg-based photocathodes prepared by ns, ps and fs PLD for the production of high brightness electron beams has been presented and discussed.     

Atomic force microscopic characterization of films grown by inverse pulsed laser deposition

Carbon nitride films have been deposited by KrF excimer laser ablation of a rotating graphite target in 5 Pa nitrogen ambient in an inverse pulsed laser deposition configuration, where the backward motion of the ablated species is utilised for film growth on substrates lying in the target plane. Topometric AFM scans of the films, exhibiting elliptical thickness distribution, have been recorded along the axes of symmetry of the deposition area. High resolution AFM scans revealed the existence of disk-like, or somewhat elongated rice-like features of 5-10 nm average thickness and ∼100 nm largest dimension, densely packed over the whole, approximately 14 × 10 cm² deposition area. The RMS roughness of the film decreased from 9 nm near to the laser spot down to 2 nm in the outer regions. Even the highest RMS value obtained for IPLD films was less than half of the typical, 25 nm roughness measured on simultaneously deposited PLD films.     

Structural characterization of AlN films synthesized by pulsed laser deposition

We obtained AlN thin films by pulsed laser deposition (PLD) from a polycrystalline AlN target using a pulsed KrF* excimer laser source (248 nm, 25 ns, intensity of ∼4 × 10⁸ W/cm², repetition rate 3 Hz, 10 J/cm² laser fluence). The target-Si substrate distance was 5 cm. Films were grown either in vacuum (10⁻⁴ Pa residual pressure) or in nitrogen at a dynamic pressure of 0.1 and 10 Pa, using a total of 20,000 subsequent pulses. The films structure was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and spectral ellipsometry (SE). Our TEM and XRD studies showed a strong dependence of the film structure on the nitrogen content in the ambient gas. The films deposited in vacuum exhibited a high quality polycrystalline structure with a hexagonal phase. The crystallite growth proceeds along the c-axis, perpendicular to the substrate surface, resulting in a columnar and strongly textured structure. The films grown at low nitrogen pressure (0.1 Pa) were amorphous as seen by TEM and XRD, but SE data analysis revealed ∼1.7 vol.% crystallites embedded in the amorphous AlN matrix. Increasing the nitrogen pressure to 10 Pa promotes the formation of cubic (≤10 nm) crystallites as seen by TEM but their density was still low to be detected by XRD. SE data analysis confirmed the results obtained from the TEM and XRD observations.     

Effect of spot size on cone formation in a XeCl laser ablation of polyethersulfone films

Radiation from the UV excimer lasers, with the fluence above the ablation threshold, can etch the polymer surfaces by photoablation. In some cases different microstructures may appear on the surface during the laser ablation. In this paper the effect of the laser spot size on the cone formation on polyethersulfone films has been investigated. The experiments have been performed with a XeCl laser at the wavelength of 308 nm and at the fluences of 70 and 100 mJ/cm² at air. For the investigation of the effect of the laser spot size on cone formation, the samples were irradiated at two different laser spot sizes of w₁ and w₂ = 0.1 w₁. The morphology of the processed surface was studied by scanning electron microscopy (SEM). It has shown that the shape, size and density of cones change with the change of the laser spot size. Also, the number of pulses and the pulse repetition rate which are needed for threshold of cone formation are affected by the laser beam spot size on the surface.     

Laser isotope separation of carbon by multiple IR photon and subsequent UV excitation of CF3I molecules

A new approach to laser isotope separation is considered. It is based on collisionless multiple photon ir laser excitation and subsequent uv laser dissociation of vibrationally excited molecules. TEA CO₂ and excimer XeF, XeCl lasers are used for ir excitation and uv dissociation, respectively. The products of photolysis (C₂F₆) are enriched with¹²C.     

Effect of excimer laser annealing on the properties of ZnO thin film prepared by sol-gel method

Pristine ZnO thin films have been deposited with zinc acetate [Zn(CH₃COO)₂], mono-ethanolamine (stabilizer), and isopropanol solutions by sol-gel method. After deposition, pristine ZnO thin films have been irradiated by excimer laser (λ = 248, KrF) source with energy density of 50 mJ/cm² for 30 sec. The effect of excimer laser annealing on the optical and structural properties of ZnO thin films are investigated by photoluminescence and field emission scanning electron microscope. As-grown ZnO thin films show a huge peak of visible region and a wide full width at half maximum (FWHM) of UV region due to low quality with amorphous ZnO thin films. After KrF excimer laser annealing, ZnO thin films show intense near-band-edge (NBE) emission and weak deep-level emission. The optically improved pristine ZnO thin films have demonstrated that excimer laser annealing is novel treatment process at room temperature.     

Chemical and morphological difference between TiN/DLC and a-C:H/DLC grown by pulsed vacuum arc techniques

In order to improve the adherence of DLC films, interlayers of amorphous hydrogenated carbon (a-C:H) and titanium nitride (TiN) were deposited by means of the pulsed vacuum arc technique. Bilayers were obtained by using a carbon target of 99.98% of purity in mixtures of (Ar + CH₄) and (Ar + H₂) for producing a-C and DLC, respectively and a target of titanium of 99.999% in a mixture of (Ar + N₂) for growing TiN. After the deposition, chemical and morphological differences between TiN/DLC and a-C:H/DLC bilayers grown on silicon and stainless steel 304 were studied using X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR), and scanning probe microscopy (SPM) techniques. XPS analysis showed a difference in sp³/(sp²+sp³) bonds ratio for each bilayer, being 0.67 for TiN/DLC and 0.45 for a-C:H/DLC bilayers. sp³ and sp² bonds were also observed by the FTIR technique. SPM images, in atomic force microscopy (AFM) and lateral force microscopy (LFM) modes were carried out for illustrating the comparison between TiN/DLC and a-C/DLC morphologic characteristics. Roughness and grain size were studied as a function of the H₂ concentration for both bilayers.     

Radio-frequency assisted pulsed laser deposition of nanostructured WOx films

The synthesis of tungsten oxide films with large surface area is promising for gas sensing applications. Thin WO_x films were obtained by radio-frequency assisted pulsed laser deposition (RF-PLD). A tungsten target was ablated at 700 and 900 Pa in reactive oxygen, or in a 50% mixed oxygen-helium atmosphere at the same total pressure values. Corning glass was used as substrate, at temperatures including 673, 773 and 873 K. Other deposition parameters such as laser fluence (4.5 J cm⁻²), laser wavelength (355 nm), radiofrequency power (150 W), target to substrate distance (4 cm), laser spot area (0.7 mm²), and number of laser shots (12,000) were kept fixed. The sensitivity on the deposition conditions of morphology, nanostructure, bond coordination, and roughness of the obtained films were analyzed by scanning and transmission electron microscopy, micro-Raman spectroscopy, and atomic force microscopy.     

Au cluster growth on ZnO thin films by pulsed laser deposition

Nanostructures formed by Au nanoparticles on ZnO thin film surface are of interest for applications which include medical implants, gas-sensors, and catalytic systems. A frequency tripled Nd:YAG laser (λ = 355 nm, τ_FWHM ∼ 10 ns) was used for the successive irradiation of the Zn and Au targets. The ZnO films were synthesized in 20 Pa oxygen pressure while the subsequent Au coverage was grown in vacuum. The obtained structures surface morphology, crystalline quality, and chemical composition depth profile were investigated by acoustic (dynamic) mode atomic force microscopy, X-ray diffraction, and wavelength dispersive X-ray spectroscopy. The surface is characterized by a granular morphology, with average grain diameters of a few tens of nanometers. The surface roughness decreases with the increase of the number of laser pulses applied for the irradiation of the Au target. The Au coverage reveals a predominant (1 1 1) texture, whereas the underlying ZnO films are c-axis oriented. A linear dependence was established between the thickness of the Au coverage and the number of laser pulses applied for the irradiation of the Au target.     

Reactive pulsed laser deposition of gold nitride thin films

We report on the growth and characterization of gold nitride thin films on Si 〈1 0 0〉 substrates at room temperature by reactive pulsed laser ablation. A pure (99.95%) Au target was ablated with KrF excimer laser pulses in nitrogen containing atmosphere (N₂ or NH₃). The gas ambient pressure was varied in the range 0.1-100 Pa. The morphology of the films was studied by using optical, scanning electron and atomic force microscopy, evidencing compact films with RMS roughness in the range 3.6-35.1 nm, depending on the deposition pressure. Rutherford backscattering spectrometry and energy dispersion spectroscopy (EDS) were used to detect the nitrogen concentration into the films. The EDS nitrogen peak does not decrease in intensity after 2 h annealing at 250 °C. Film resistivity was measured using a four-point probe and resulted in the (4-20) × 10⁻⁸ Ω m range, depending on the ambient pressure, to be compared with the value 2.6 × 10⁻⁸ Ω m of a pure gold film. Indentation and scratch measurements gave microhardness values of 2-3 GPa and the Young's modulus close to 100 GPa. X-ray photoemission spectra clearly showed the N 1s peak around 400 eV and displaced with respect to N₂ phase. All these measurements point to the formation of the gold nitride phase.     

Influence of the laser wavelength on the epitaxial growth and electrical properties of La0.8Sr0.2MnO3 films grown by excimer laser-assisted MOD

Epitaxial La_1−xSr_xMnO₃ (LSMO) films were prepared by excimer laser-assisted metal organic deposition (ELAMOD) at a low temperature using ArF, KrF, and XeCl excimer lasers. Cross-section transmission electron microscopy (XTEM) observations confirmed the epitaxial growth and homogeneity of the LSMO film on a SrTiO₃ (STO) substrate, which was prepared using ArF, KrF, and XeCl excimer lasers. It was found that uniform epitaxial films could be grown at 500 °C by laser irradiation. When an XeCl laser was used, an epitaxial film was formed on the STO substrate at a fluence range from 80 to 140 mJ/cm² of the laser fluence for the epitaxial growth of LSMO film on STO substrate was changed. When the LaAlO₃ (LAO) substrate was used, an epitaxial film was only obtained by ArF laser irradiation, and no epitaxial film was obtained using the KrF and XeCl lasers. When the back of the amorphous LSMO film on an LAO substrate was irradiated using a KrF laser, no epitaxial film formed. Based on the effect of the wavelength and substrate material on the epitaxial growth, formation of the epitaxial film would be found to be photo thermal reaction and photochemical reaction. The maximum temperature coefficient of resistance (TCR) of the epitaxial La_0.8Sr_0.2MnO₃ film on an STO substrate grown using an XeCl laser is 4.0%/K at 275 K. XeCl lasers that deliver stabilized pulse energies can be used to prepare LSMO films with good a TCR.     

Femtosecond pulsed laser deposition of diamond-like carbon films: The effect of double laser pulses

The bonding structure of carbon films prepared by pulsed laser deposition is determined by the plasma properties especially the change of the kinetic energy. Using double laser pulses the ablation process and the characteristics of the generated plasma can be controlled by the setting of the delay between the pulses. In our experiments, amorphous carbon films have been deposited in vacuum onto Si substrates by double pulses from a Ti:sapphire laser (180 fs, λ = 800 nm, at 1 kHz) and a KrF laser system (500 fs, λ = 248 nm, at 5 Hz). The intensities have been varied in the range of 3.4 × 10¹² to 2 × 10¹³ W/cm². The morphology and the main properties of the thin layers were investigated as a function of the time delay between the two ablating pulses (0-116.8 ps) and as a function of the irradiated area on the target surface. Atomic force microscopy, spectroscopic ellipsometry and Raman-spectroscopy were used to characterize the films. It was demonstrated that the change of the delay and the spot size results in the modification of the thickness distribution of the layers, and the carbon sp²/sp³ bonding ratio.     

Fabrication of p-type Li-doped ZnO films by pulsed laser deposition

p-Type ZnO thin films have been realized via doping Li as acceptor by using pulsed laser deposition. In our experiment, Li₂CO₃ was used as Li precursor, and the growth temperature was varied from 400 to 600 °C in pure O₂ ambient. The Li-doped ZnO film prepared at 450 °C possessed the lowest resistivity of 34 Ω cm with a Hall mobility of 0.134 cm² V⁻¹ s⁻¹ and hole concentration of 1.37 × 10¹⁸ cm⁻³. X-ray diffraction (XRD) measurements showed that the Li-doped ZnO films grown at different substrate temperatures were of completely (0 0 2)-preferred orientation.     

Towards the synthesis of MAX-phase functional coatings by pulsed laser deposition

Pulsed laser deposition with a Nd:YAG laser was used to grow thin films from a pre-synthesized Ti₃SiC₂ MAX-phase formulated ablation target on oxidized Si(1 0 0) and MgO(1 0 0) substrates. The depositions were carried out in a substrate temperature range from 300 to 900 K, and the pressure in the deposition chamber ranged from vacuum (10⁻⁵ Pa) to 0.05 Pa Argon background pressure. The properties of the films have been investigated by Rutherford backscattering spectrometry for film thickness and stoichiometric composition and X-ray diffraction for the crystallinity of the films. The silicon content of the films varied with the energy density of the laser beam. To suppress especially the silicon re-sputtering from the substrate, the energy of the incoming particles must be below a threshold of 20 eV. Therefore, the energy density of the laser beam must not be too high. At constant deposition energy density the film thickness depends strongly on the background pressure. The X-ray diffraction measurements show patterns that are typical of amorphous films, i.e. no Ti₃SiC₂ related reflections were found. Only a very weak TiC(2 0 0) reflection was seen, indicating the presence of a small amount of crystalline TiC.     

Surface modification of a WTi thin film on Si substrate by nanosecond laser pulses

Interaction of a nanosecond transversely excited atmospheric (TEA) CO₂ laser, operating at 10.6 μm, with tungsten-titanium thin film (190 nm) deposited on silicon of n-type (1 0 0) orientation, was studied. Multi-pulse irradiation was performed in air atmosphere with laser energy densities in the range 24-49 J/cm². The energy absorbed from the laser beam was mainly converted to thermal energy, which generated a series of effects. The following morphological changes were observed: (i) partial ablation/exfoliation of the WTi thin film, (ii) partial modification of the silicon substrate with formation of polygonal grains, (iii) appearance of hydrodynamic features including nano-globules. Torch-like plumes started appearing in front of the target after several laser pulses.     

Characterization of pulsed laser deposited chalcogenide thin layers

In this work we report on pulsed laser deposition (PLD) of chalcogenide thin films from the systems (AsSe)_100−xAgI_x and (AsSe)_100−xAg_x for sensing applications. A KrF* excimer laser (λ = 248 nm; τ_FWHM = 25 ns) was used to ablate the targets that had been prepared from the synthesised chalcogenide materials. The films were deposited in either vacuum (4 × 10⁻⁴ Pa) or argon (5 Pa) on silicon and glass substrates kept at room temperature. The basic properties of the films, including their morphology, topography, structure, and composition were characterised by complementary techniques. Investigations by X-ray diffraction (XRD) confirmed the amorphous nature of the films, as no strong diffraction reflections were found. The film composition was studied by energy dispersive X-ray (EDX) spectroscopy. The morphology of the films investigated by scanning electron microscopy (SEM), revealed a particulate-covered homogeneous surface, typical of PLD. Topographical analyses by atomic force microscopy (AFM) showed that the particulate size was slightly larger in Ar than in vacuum. The uniform surface areas were rather smooth, with root mean square (rms) roughness increasing up to several nanometers with the AgI or Ag doping. Based upon the results from the comprehensive investigation of the basic properties of the chalcogenide films prepared by PLD and their dependence on the process parameters, samples with appropriate sorption properties can be selected for possible applications in cantilever gas sensors.     

Dual excimer and CO2 laser etching studies of polyethylene terephthalate

Polyethylene terephthalate (PET) films preheated with a pulsed CO₂ laser have been ablatively etched with an XeCl laser. The observed reduction in ablation threshold, from 170 to 140 mJ cm^–2, is consistent with a thermal mechanism for XeCl laser ablation of PET. Transient changes in the UV absorption coefficient of PET caused by heating with pulsed CO₂ laser radiation have also been studied and a significant increase in absorption observed at 308 nm. Permanent changes in the ultraviolet absorption of PET following exposure to low fluence XeCl laser radiation are also reported.     

Bioactive glass and hydroxyapatite thin films obtained by pulsed laser deposition

Bioactive glass (BG), calcium hydroxyapatite (HA), and ZrO₂ doped HA thin films were grown by pulsed laser deposition on Ti substrates. An UV KrF^* (λ = 248 nm, τ ≥ 7 ns) excimer laser was used for the multi-pulse irradiation of the targets. The substrates were kept at room temperature or heated during the film deposition at values within the (400-550 °C) range. The depositions were performed in oxygen and water vapor atmospheres, at pressure values in the range (5-40 Pa). The HA coatings were heat post-treated for 6 h in a flux of hot water vapors at the same temperature as applied during deposition. The surface morphology, chemical composition, and crystalline quality of the obtained thin films were studied by scanning electron microscopy, atomic force microscopy, and X-ray diffractometry. The films were seeded for in vitro tests with Hek293 (human embryonic kidney) cells that revealed a good adherence on the deposited layers. Biocompatibility tests showed that cell growth was better on HA than on BG thin films.     

Study of the structure and electrical properties of the copper nitride thin films deposited by pulsed laser deposition

Copper nitride thin films were prepared on glass and silicon substrates by ablating a copper target at different pressure of nitrogen. The films were characterized in situ by X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES) and ex situ by X-ray diffraction (XRD). The nitrogen content in the samples, x = [N]/[Cu], changed between 0 and 0.33 for a corresponding variation in nitrogen pressure of 9 × 10⁻² to 1.3 × 10⁻¹ Torr. Using this methodology, it is possible to achieve sub-, over- and stoichiometric films by controlling the nitrogen pressure. The XPS results show that is possible to obtain copper nitride with x = 0.33 (Cu₃N) and x = 0.25 (Cu₄N) when the nitrogen pressure is 1.3 × 10⁻¹ and 5 × 10⁻² Torr, respectively. The lattice constants obtained from XRD results for copper nitride with x = 0.25 is of 3.850 Å and with x = 0.33 have values between 3.810 and 3.830 Å. The electrical properties of the films were studied as a function of the lattice constant. These results show that the electrical resistivity increases when the lattice parameter is decreasing. The electrical resistivity of copper nitride with x = 0.25 was smaller than samples with x = 0.33.