Thermogravimetric analysis and microstructural observations on the formation of GaN from the reaction between Ga2O3 and NH3

Thermogravimetric analysis (TGA) and microstructural observations were carried to investigate the nitridation mechanism of β-Ga₂O₃ powder to GaN under an NH₃/Ar atmosphere. Non-isothermal TGA showed that nitridation of β-Ga₂O₃ starts at ∼650 °C, followed by decomposition of GaN at ∼1100 °C. Isothermal TGA showed that nitridation follows linear kinetics in the temperature range 800–1000 °C. At an early stage of nitridation, small GaN particles (∼5 nm) are deposited on the β-Ga₂O₃ crystal surface and they increase with time. We proposed a mechanism for the nitridation of Ga₂O₃ by NH₃ whereby nitridation of β-Ga₂O₃ proceeds via the intermediate vapor species Ga₂O(g).     

Hydride-assisted growth of GaN nanowires on Au/Si(0 0 1) via the reaction of Ga with NH3 and H2

High quality, straight GaN nanowires (NWs) with diameters of 50 nm and lengths up to 3 μm have been grown on Si(0 0 1) using Au as a catalyst and the direct reaction of Ga with NH₃ and N₂:H₂ at 900 °C. These exhibited intense, near band edge photoluminescence at 3.42 eV in comparison to GaN NWs with non-uniform diameters obtained under a flow of Ar:NH₃, which showed much weaker band edge emission due to strong non-radiative recombination. A significantly higher yield of β-Ga₂O₃ NWs with diameters of ≤50 nm and lengths up to 10 μm were obtained, however, via the reaction of Ga with residual O₂ under a flow of Ar alone. The growth of GaN NWs depends critically on the temperature, pressure and flows in decreasing order of importance but also the availability of reactive species of Ga and N. A growth mechanism is proposed whereby H₂ dissociates on the Au nanoparticles and reacts with Ga giving Ga_xH_y thereby promoting one-dimensional (1D) growth via its reaction with dissociated NH₃ near or at the top of the GaN NWs while suppressing at the same time the formation of an underlying amorphous layer. The higher yield and longer β-Ga₂O₃ NWs grow by the vapor liquid solid mechanism that occurs much more efficiently than nitridation.     

High-resolution imaging of 1:1 [0 0 0 1] ordered a-plane Al0.3Ga0.7N

We report the observation of ordering in Al_0.3Ga_0.7N as part of an epitaxial lateral overgrowth (ELO) of GaN carried out using (1 1 2¯ 2) GaN templates grown by metal-organic chemical vapor deposition on m-plane sapphire. Transmission electron microscopy showed that the crystalline quality of the ELO GaN was greatly improved when the ELO SiO₂ mask was patterned along the [1 1 2¯ 0]_sapphire direction. The ELO GaN wings had an inclined columnar shape with smooth (0 0 0 1) and (1 1 2¯ 0) facets. Layers of 1:1 [0 0 0 1] ordered a-plane Al_0.3Ga_0.7N were observed on the a-plane GaN facets by high-resolution transmission electron microscopy and high-angle annular-dark-field scanning transmission electron microscopy. However, no ordering was observed for c-plane Al_0.3Ga_0.7N layers grown at the same time on the c-plane GaN facets.     

Synchrotron X-ray diffraction studies of heteroepitaxial ZnO films grown by pulsed laser deposition

Heteroepitaxial ZnO films were grown by pulsed laser deposition on various substrates such as GaN-buffered C-Al₂O₃, C-Al₂O₃, A-Al₂O₃, and R-Al₂O₃. The epitaxy nature of the films was investigated mainly by synchrotron X-ray diffraction. The results showed that the GaN interlayer plays a positive role in growing an unstrained, well-aligned epitaxial ZnO film on the basal plane of Al₂O₃. Importantly, the ZnO film grown on R-Al₂O₃ has two differently aligned domains. The dominant (1 1 0) oriented domain has much better alignment in the in-plane direction than the minor portion of (0 0 1) oriented domain, while in the out-of-plane direction the two domains have almost the same mosaic distribution.     

Theoretical investigation on the decomposition process of GaN(0 0 0 1) surface under a hydrogen atmosphere

The activation energies for Ga and N desorption from a GaN surface were calculated using the density functional theory to understand the detailed decomposition process of the hydrogen terminated GaN(0 0 0 1) Ga and N surfaces under a hydrogen atmosphere. It was found that the Ga atoms on the hydrogen terminated GaN(0 0 0 1) Ga surface desorbed as GaH molecules from the surface while the N atoms on the hydrogen terminated GaN(0 0 0 1) N surface desorbed as NH₃ molecules from the surface. The desorption energies of GaH and NH₃ on the hydrogen terminated surface were more consistent with the previous experimental values than those on the ideal surface. These results suggest that the initial surface structure of the GaN(0 0 0 1) surface is terminated with hydrogen.     

Epitaxial growth of β-Ga2O3 nanocolumns on MgO substrate

Crystal structure of Ga₂O₃ nanocolumns grown on MgO substrate is analyzed by electron microscopy and electron diffraction study. The nanocolumns have β-Ga₂O₃ structure and the growth direction is [0 0 1] directions. A thin γ-Ga₂O₃ layer grows on the substrate to relax the lattice misfit between MgO and β-Ga₂O₃. The bottom layer of the γ form layer is disordered by {1 1 0} stacking faults. Poly crystalline structure that consists of β-Ga₂O₃ and γ-Ga₂O₃ nanocrystals exists between the β form nanocolumns and the γ form layer. The γ form changes gradually to the β form growing up to the nanocolumn. Though various crystal forms appear in a specimen, oxygen cubic close-packed lattice in crystal structures has always the same orientation in all layers including the MgO substrate.     

MOCVD growth of GaN on Si(1 1 1) substrates using an ALD-grown Al2O3 interlayer

GaN thin films have been grown on Si(1 1 1) substrates using an atomic layer deposition (ALD)-grown Al₂O₃ interlayer. This thin Al₂O₃ layer reduces strain in the subsequent GaN layer, leading to lower defect densities and improved material quality compared to GaN thin films grown by the same process on bare Si. XRD ω-scans showed a full width at half maximum (FWHM) of 549 arcsec for GaN grown on bare Si and a FWHM as low as 378 arcsec for GaN grown on Si using the ALD-grown Al₂O₃ interlayer. Raman spectroscopy was used to study the strain in these films in more detail, with the shift of the E₂(high) mode showing a clear dependence of strain on Al₂O₃ interlayer thickness. This dependence of strain on Al₂O₃ thickness was also observed via the redshift of the near bandedge emission in room temperature photoluminescence (RT-PL) spectroscopy. The reduction in strain results in a significant reduction in both crack density and screw dislocation density compared to similar films grown on bare Si. Screw dislocation density of the films grown on Al₂O₃/Si substrates approaches that of typical GaN layers on sapphire. This work shows great promise for the use of oxide interlayers for growth of GaN-based LEDs on Si.     

Epitaxial NiO (1 0 0) and NiO (1 1 1) films grown by atomic layer deposition

Epitaxial NiO (1 1 1) and NiO (1 0 0) films have been grown by atomic layer deposition on both MgO (1 0 0) and α-Al₂O₃ (0 0 l) substrates at temperatures as low as 200 °C by using bis(2,2,6,6-tetramethyl-3,5-heptanedionato)Ni(II) and water as precursors. The films grown on the MgO (1 0 0) substrate show the expected cube on cube growth while the NiO (1 1 1) films grow with a twin rotated 180° on the α-Al₂O₃ (0 0 l) substrate surface. The films had columnar microstructures on both substrate types. The single grains were running throughout the whole film thickness and were significantly smaller in the direction parallel to the surface. Thin NiO (1 1 1) films can be grown with high crystal quality with a FWHM of 0.02–0.05° in the rocking curve measurements.     

Growth of GaN based structures on Si(1 1 0) by molecular beam epitaxy

The growth of GaN based structures on Si(1 1 0) substrates by molecular beam epitaxy using ammonia as the nitrogen precursor is reported. The structural, optical and electrical properties of such structures are assessed and are quite similar to the ones obtained on Si(1 1 1) in-spite of the very different substrate surface symmetry. A threading dislocation density of 3.7×10⁹ cm⁻² is evaluated by transmission electron microscopy, which is in the low range of typical densities obtained on up to 2 μm thick GaN structures grown on Si(1 1 1). To assess the potential of such structure for device realization, AlGaN/GaN high electron mobility transistor and InGaN/GaN light emitting diode heterostructures were grown and their properties are compared with the ones obtained on Si(1 1 1).     

Growth of thick GaInN on grooved (1 0 1¯ 1¯) GaN/(1 0 1¯ 2¯) 4H-SiC

We succeeded in growing high-crystalline-quality thick (1 0 1¯ 1¯) Ga_0.92In_0.08N films on a grooved (1 0 1¯ 1¯) GaN/(1 0 1¯ 2¯) 4H-SiC underlying layer. We also fabricated GaInN/GaN multiple quantum wells (MQWs) with a peak wavelength of 580 nm on a high-crystalline-quality thick GaInN film. The photoluminescence intensity of the MQWs is about six times higher than that of MQWs grown on planar GaN and twice as high as that of MQWs grown on a GaN underlying layer having the same grooved structure.     

Fabrication of freestanding m-plane GaN wafer by using the HVPE technique on an aluminum carbide buffer layer on an m-plane sapphire substrate

A freestanding m-plane GaN wafer is fabricated by using the hydride vapor-phase epitaxy (HVPE) technique on an aluminum carbide buffer layer on an m-plane sapphire substrate. X-ray pole-figure measurements show a clear m-plane orientation of the GaN surface. The full-width at half-maximum (FWHM) of GaN (1 1¯ 0 0) X-ray rocking curve (XRC) with the scattering vector along the [1 1 2¯ 0] direction is approximately 800 arcsec; this indicates good crystallinity. On the other hand, the FWHM for the case in which the scattering vector is oriented along the [0 0 0 1] direction is broad; this suggests the influence of structural defects along this direction. In fact, basal plane stacking faults (BSF) with a density of approximately 3×10⁵ cm⁻¹ is observed by transmission electron microscopy (TEM). The preparation of a 45-mm-diameter m-plane GaN wafer due to spontaneous separation of the GaN layer from the sapphire substrate is demonstrated.     

The effects of annealing on non-polar (1 1 2¯ 0) a-plane GaN films

Non-polar a-plane (1 1 2¯ 0) GaN films were grown on r-plane sapphire by metal–organic vapor phase epitaxy and were subsequently annealed for 90 min at 1070 °C. Most dislocations were partial dislocations, which terminated basal plane stacking faults. Prior to annealing, these dislocations were randomly distributed. After annealing, these dislocations moved into arrays oriented along the [0 0 0 1] direction and aligned perpendicular to the film–substrate interface throughout their length, although the total dislocation density remained unchanged. These changes were accompanied by broadening of the symmetric X-ray diffraction 1 1 2¯ 0 ω-scan widths. The mechanism of movement was identified as dislocation glide, occurring due to highly anisotropic stresses (confirmed by X-ray diffraction lattice parameter measurements) and evidenced by macroscopic slip bands observed on the sample surface. There was also an increase in the density of unintentionally n-type doped electrically conductive inclined features present at the film–substrate interface (as observed in cross-section using scanning capacitance microscopy), suggesting out-diffusion of impurities from the substrate along with prismatic stacking faults. These data suggest that annealing processes performed close to film growth temperatures can affect both the microstructure and the electrical properties of non-polar GaN films.     

Structural and electrical properties of Si-doped a-plane GaN grown on r-plane sapphire by MOVPE

Approximately 2-μm-thick Si-doped a-plane GaN films with different doping concentrations were grown on approximately 8-μm-thick undoped a-plane GaN/r-sapphire by metal organic vapor phase epitaxy (MOVPE). The structural and electrical properties of the Si-doped a-plane GaN films were investigated by high-resolution X-ray diffraction (HRXRD), atomic force microscopy (AFM) and temperature-dependent Hall measurement. The results showed that a small amount of Si doping can improve the surface morphology and decrease the density of pits. Upon increasing the CH₃SiH₃ flow rate, the crystalline quality of the (0 0 0 2) plane was slightly improved. The highest room-temperature mobility of 83.4 cm²/Vs was obtained at a carrier density of 6.2×10¹⁸ with a CH₃SiH₃ flow rate of 10 sccm.     

Synthesis of GaN crystal by the reaction of Ga with Li3N in NH3 atmosphere

A novel method to synthesize GaN crystals was studied by the reaction of Ga with Li₃N under NH₃ atmosphere. We have already reported the synthesis technique of GaN by the reaction of Ga₂O₃ with Li₃N. However, the size of GaN crystals obtained by this method was limited to be smaller than several micrometers because of the solid phase reaction. In order to increase the size of GaN crystals, the method using liquid Ga as gallium source was studied for solid–liquid phase reaction. We found that the GaN crystals with the size of more than 100 μm were synthesized at 750 °C for 24 h under NH₃ atmosphere. We propose the possible reaction mechanism as follows. Lithium amide (LiNH₂) is synthesized by the reaction of Li₃N with NH₃ gas and then the crystal growth of GaN occurs by the reaction of Ga with LiNH₂. We found that LiNH₂ is a useful nitrogen source for the GaN synthesis method.     

Maskless selective growth of semi-polar (1 12¯ 2) GaN on Si (3 1 1) substrate by metal organic vapor phase epitaxy

Semi-polar (1 1 2¯ 2) GaN layers were selectively grown by metal organic chemical vapor phase epitaxy on patterned Si (3 1 1) substrates without SiO₂ amorphous mask. The (1 1 2¯ 2) GaN layers could be selectively grown only on Si (1 1 1) facets when the stripe mask width was narrower than 1 μm even without SiO₂. Inhomogeneous spatial distribution of donor bound exciton (DBE) peak in low-temperature cathodoluminescence (CL) spectra was explained by the difference of growth mode before and after the coalescence of stripes. It was found that the emission intensity related crystal defects is drastically decreased in case of selective growth without SiO₂ masks as compared to that obtained with SiO₂ masks.     

Growth of (1 0 1¯ 3¯ ) semipolar GaN on m-plane sapphire by hydride vapor phase epitaxy

The crystalline, surface, and optical properties of the (1 0 1¯ 3¯) semipolar GaN directly grown on m-plane sapphire substrates by hydride vapor phase epitaxy (HVPE) were investigated. It was found that the increase of V/III ratio led to high quality (1 0 1¯ 3¯) oriented GaN epilayers with a morphology that may have been produced by step-flow growth and with minor evidence of anisotropic crystalline structure. After etching in the mixed acids, the inclined pyramids dominated the GaN surface with a density of 2×10⁵ cm⁻², revealing the N-polarity characteristic. In the low-temperature PL spectra, weak BSF-related emission at 3.44 eV could be observed as a shoulder of donor-bound exciton lines for the epilayer at high V/III ratio, which was indicative of obvious reduction of BSFs density. In comparison with other defect related emissions, a different quenching behavior was found for the 3.29 eV emission, characterized by the temperature-dependent PL measurement.     

Microstructural characteristics and crystallographic evolutions of Ga-doped ZnO films grown on sapphire substrates at high temperatures by RF magnetron sputtering

The microstructural characteristics and crystallographic evolutions of Ga-doped ZnO (GZO) films grown at high temperatures were examined by X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM). The GZO films with various film thicknesses were grown on (0 0 0 1) Al₂O₃ substrates at 750 °C by RF magnetron sputtering using a 2 wt% Ga-doped ZnO single target. The (0 0 0 2) ZnO peaks in the XRD patterns shifted to a higher angle with increasing film thickness and an additional (1 0 1¯ 1) ZnO peak was observed in the final stage of film growth. HRTEM showed the epitaxial growth of GZO films in the initial growth stage and the formation of surface protrusions in the intermediate stage due to elastic relaxation. The surface protrusions consisted of {1 0 1¯ 1}, {1 0 1¯ 3}, and {0 0 0 2} planes. After the surface protrusions had formed, a GZO film with many c-axis tilted grains formed due to plastic relaxation, where the tilted grain boundaries had an angle of 62° to the substrate. The formation of the protrusions and c-axis tilted grains was closely related to the strain status of the film induced by Ga incorporation, high-temperature growth and a high film thickness.     

Development of m-plane GaN anisotropic film properties during MOVPE growth on LiAlO2 substrates

The anisotropic film properties of m-plane GaN deposited by metal organic vapour phase epitaxy (MOVPE) on LiAlO₂ substrates are investigated. To study the development of layer properties during epitaxy, the total film thickness is varied between 0.2 and 1.7 μm. A surface roughening is observed caused by the increased size of hillock-like features. Additionally, small steps which are perfectly aligned in (1 1 −2 0) planes appear for samples with a thickness of ∼0.5 μm and above. Simultaneously, the X-ray rocking curve (XRC) full width at half maximum (FWHM) values become strongly dependent on incident X-ray beam direction beyond this critical thickness. Anisotropic in-plane compressive strain is initially present and gradually relaxes mainly in the [1 1 −2 0] direction when growing thicker films. Low-temperature photoluminescence (PL) spectra are dominated by the GaN near-band-edge peak and show only weak signal related to basal plane stacking faults (BSF). The measured background electron concentration is reduced from ∼10²⁰ to ∼10¹⁹ cm⁻³ for film thicknesses of 0.2 μm and ∼1 μm while the electron mobilities rise from ∼20 to ∼130 cm²/V s. The mobilities are significantly higher in [0 0 0 1] direction which we explain by the presence of extended planar defects in the prismatic plane. Such defects are assumed to be also the cause for the observed surface steps and anisotropic XRC broadening.     

MOVPE of AlN-free hexagonal GaN/cubic SiC/Si heterostructures for vertical devices

The heterostructures of GaN/SiC/Si were prepared without using AlN or AlGaN buffer layers (AlN buffers) in the metalorganic vapor phase epitaxy of GaN on SiC. GaN (0 0 0 1) with specular surface was obtained. The AlN buffers are usually used in the conventional growth of GaN on SiC due to the poor nucleation of GaN on SiC. Instead, the nucleation of GaN was controlled by varying the partial pressure of H₂ in the carrier gas, the mixture of H₂ and N₂, during the low-temperature (600 °C) growth of GaN (LT-GaN). After the LT-GaN, the high-temperature (1000 °C) growth of GaN was performed using pure H₂ as the carrier gas. The epitaxial film of cubic SiC (1 1 1) on a Si (1 1 1) substrate was used as the SiC template. Increasing the partial pressure of H₂ in the carrier gas decreased the coverage of SiC surface by LT-GaN. It is suggested that the hydrogen atoms adsorbed on the surface of SiC is preventing the nucleation of GaN.     

GaN grown on (1 1 1) single crystal diamond substrate by molecular beam epitaxy

GaN epilayers are grown on (1 1 1) oriented single crystal diamond substrate by ammonia-source molecular beam epitaxy. Each step of the growth is monitored in situ by reflection high energy electron diffraction. It is found that a two-dimensional epitaxial wurtzite GaN film is obtained. The surface morphology is smooth: the rms roughness is as low as 1.3 nm for 2×2 μm² scan. Photoluminescence measurements reveal pretty good optical properties. The GaN band edge is centred at 3.469 eV with a linewidth of 5 meV. These results demonstrate that GaN heteroepitaxially grown on diamond opens new rooms for high power electronic applications.