Up-conversion emissions of Er<Superscript>3+</Superscript>-Yb<Superscript>3+</Superscript> codoped Al<Subscript>2</Subscript>O<Subscript>3</Subscript> nanoparticles by the arc discharge synthesis method

The Er³⁺-Yb³⁺ codoped Al₂O₃ nanoparticles with an average particle size of about 50 nm have been synthesized by an arc discharge synthesis method. The green and red up-conversion emissions centered at about 526, 547 and 677 nm, corresponding respectively to the ²H_11/2→⁴I_15/2, ⁴S_3/2→⁴I_15/2 and ⁴F_9/2→⁴I_15/2 transitions of Er³⁺, were detected by a 978-nm semiconductor laser diode excitation. The Annealing has evident effect on the up-conversion emissions of the samples: The red up-conversion emission is noticeable before annealing; however, the green up-conversion emission becomes predominant after annealing. The mixture of (Er,Yb)₃Al₅O₁₂ and α-(Al,Er,Yb)₂O₃ phases is more favorable for green up-conversion emissions due to an enhancement of the ESA (I) of ⁴I_11/2+a photon→⁴F_7/2 and ET (III) of ²F_5/2(Yb³⁺)+⁴I_11/2(Er³⁺)→²F_7/2(Yb³⁺)+⁴F_7/2(Er³⁺) processes. The two-photon absorption up-conversion process is involved in the green and red up-conversion emissions. The results have proved that arc discharge synthesis is a new promising preparation technology for optical materials. Supported by National Natural Science Foundation of China (Grant No. 10804015), the Scientific Research Foundation for Doctor of Liaoning Province (Grant No. 20071095), and the Educational Committee Foundation of Liaoning Province (Grant No. 2008123)     

Defect Structure and Up-conversion Luminescence Properties of ZrO<Subscript>2</Subscript>:Yb<Superscript>3+</Superscript>,Er<Superscript>3+</Superscript> Nanomaterials

The up-converting ZrO₂:Yb³⁺,Er³⁺ nanomaterials were prepared with the combustion and sol–gel methods. FT-IR spectroscopy was used for analyzing the impurities. The crystal structures were characterized with X-ray powder diffraction and the mean crystallite sizes were estimated with the Scherrer formula. Up-conversion luminescence measurements were made at room temperature with IR-laser excitation at 977 nm. The IR spectra revealed the conventional and OH⁻ impurities for the combustion synthesis products. The structure of the ZrO₂:Yb³⁺, Er³⁺ nanomaterials was cubic except for the minor monoclinic and tetragonal impurities obtained with the sol–gel method. The materials showed red (650–700 nm) and green (520–560 nm) up-conversion luminescence due to the ⁴F_9/2→⁴I_15/2 and (²H_11/2, ⁴S_3/2)→⁴I_15/2 transitions of Er³⁺, respectively. The products obtained with the combustion synthesis exhibited the most intense luminescence intensity and showed considerable afterglow.     

Er3+离子掺杂钡镓锗玻璃上转换发光机理研究

研究了Er³⁺离子掺杂钡镓锗玻璃的吸收光谱、拉曼光谱和上转换光谱.分析了Er³⁺离子在钡镓锗玻璃中的上转换发光机理.结果表明：玻璃的最大声子能量为828cm^-1，紫外截止波长为275nm.采用800nm和980nmLD激发玻璃样品，在室温下观察到强烈的上转换绿光和红光发射.随着Er³⁺离子浓度的增加，绿光发光强度先增加后减小，而红光发光强度呈单调递增趋势.能量分析表明：800nmLD激发产生的绿光主要源于Er³⁺离子4I_13/2能级的激发态吸收过程；红光发射主要源于Er³⁺离子4I_13/2能级与4I_11/2能级之间的能量转移过程.980nmLD激发产生的绿光主要源于Er³⁺离子4I_11/2能级之间的能量转移过程；而红光发射主要源于Er³⁺离子4I_13/2能级与4I_11/2能级之间的能量转移过程和4I_13/2能级的激发态吸收过程.通过量子效率分析，发现采用800nmLD激发Er³⁺离子掺杂浓度为1mol% 的样品时，上转换绿光发光效率最高. 关键词： 上转换发光机理 3+离子掺杂')" href="#">Er³⁺离子掺杂 钡镓锗玻璃     

Green,blue, red,near-infrared up-conversion luminescence of Yb<Superscript>3+</Superscript>/Er<Superscript>3+</Superscript>/Tm<Superscript>3+</Superscript> co-doped YVO<Subscript>4</Subscript> nanoparticles

YVO₄:Yb³⁺,Er³⁺; YVO₄:Yb³⁺,Tm³⁺; and YVO₄:Yb³⁺,Er³⁺,Tm³⁺ were all synthesized via sol-gel method with a subsequent thermal treatment. Specifically, YVO₄:Yb³⁺,Er³⁺,Tm³⁺ phosphors were prepared with different annealing temperatures to study the influence of temperature. The transmission electron microscope (TEM), scanning electron microscope (SEM), X-ray diffractometer (XRD), and photoluminescent (PL) spectrofluorometer were used to investigate the morphology, crystal structure, and up-conversion luminescent properties of all samples. In summary, all samples were granular-like nanoparticles and well crystallized with the same tetragonal phase as YVO₄. Under the irradiation at 980 nm, YVO₄:Yb³⁺,Er³⁺ phosphors can generate green emission at 525 and 553 nm and red emission at 657 nm, while YVO₄:Yb³⁺,Tm³⁺ phosphors can generate blue emission at 476 nm, red emission at 648 nm, and near-infrared emission at 800 nm. Notably, YVO₄:Yb³⁺,Er³⁺,Tm³⁺ samples can exhibit green emission, blue emission, red emission, and near-infrared emission at the same time, which might endow the as-prepared samples with potential applications in many fields, such as luminous paint, infrared detection, and biological label.     

Synthesis and luminescence properties of Gd6MoO12:Yb3+, Er3+ phosphor with enhanced photoluminescence by Li+ doping

Yb³⁺/Er³⁺ co-doped Gd₆MoO₁₂ and Yb³⁺/Er³⁺/Li⁺ tri-doped Gd₆MoO₁₂ phosphors were prepared by adjusting the annealing temperature via the high temperature solid-state method. Under the excitation of 980 nm semiconductor, the upconversion luminescence properties were investigated and discussed. In the experimental process, we get the optimum Yb³⁺ concentration and the concentration quench effect will happen while the concentration extends the given region. According to the Yb³⁺ concentration quenching effects, the critical distance between Yb³⁺ ions had been calculated. The measured UC luminescence exhibited a strong red emission near 660 nm and green emission at 530 nm and 550 nm, which are due to the transitions of Er³⁺(⁴F_9/2, ²H_11/2, ⁴S_3/2) → Er³⁺(⁴I_15/2). Then the effect of excitation power density in different regions on the upconversion mechanisms was investigated and the calculated results demonstrate that the green and red upconversion is a two-photon process. A possible mechanism was discussed. After Li⁺ ions mixing, the upconversion emission enhanced largely, and the optimum Li⁺ concentration was obtained while fixed the Yb³⁺ and Er³⁺ on the above optimum concentration. This enhancement owns to the decrease of the local symmetry around Er³⁺ after Li⁺ ions doping into the system. This result indicates that Li⁺ is a promising candidate for improving luminescence in some case.     

Comparative Investigation on Nanocrystal Structure and Luminescence Properties of Gadolinium Molybdates Codoped with Er<Superscript>3+</Superscript>/Yb<Superscript>3+</Superscript>

This paper reports on the comparative investigation of nanocrystal structure and luminescence properties of Er³⁺/Yb³⁺-codoped gadolinium molybdate nanocrystals Gd₂(MoO₄)₃ and Gd₂MoO₆ synthesized by the Pechini method with citric acid and ethylene glycol. Their crystallization, structure transformation, and morphologies have been investigated by X-ray diffraction, thermogravimetric/differential scanning calorimetry, and transmission electron microscopy. It is noticed that Er³⁺/Yb³⁺-codoped monoclinic Gd₂(MoO₄)₃ nanocrystals have shown an intense upconversion through a sintering of the organic complex precursor at 600°C. Furthermore, it transforms to orthorhombic Gd₂(MoO₄)₃ when the precursor is sintered at 900°C. In counterpart of monoclinic Gd₂MoO₆, however, the monoclinic structure remains unchanged when the precursor is sintered at a temperature ranging from 600°C to 900°C. Intense visible emissions of Er³⁺ attributed to the transitions of ²H_11/2, ⁴S_3/2–⁴I_15/2 at 520 and 550 nm, and ⁴F_9/2–⁴I_15/2 at 650 nm have been observed upon an excitation with a UV source and a 980 nm laser diode, and the involved mechanisms have been explained. It is quite interesting to observe obvious differences both in the excitation and the upconversion emission spectra of Er³⁺/Yb³⁺-codoped Gd₂(MoO₄)₃ respectively with monoclinic and orthorhombic structure. The quadratic dependence of fluorescence on excitation laser power has confirmed that two-photons contribute to upconversion of the green–red emissions.     

Luminescence of transparent glass ceramics containing Er<Superscript>3+</Superscript> and Yb<Superscript>3+</Superscript> zirconate-titanate nanocrystals

Luminescence regularities have been studied in new erbium/ytterbium materials based on glasses and glass ceramics of a magnesium-aluminosilicate system containing nanoscale erbium/ytterbium zirconate titanate crystals with the pyrochlore structure. Lifetimes of Yb³⁺ and Er³⁺ ions in the ² F_5/2 state and in the ⁴I_11/2 and ⁴I_13/2 states, respectively, and the efficiency of Yb³⁺ → Er³⁺ energy transfer have been evaluated. The identified spectral-luminescent characteristics of the studied glasses and glass ceramics co-doped with erbium and ytterbium ions show that these materials are promising media for producing laser generation in the spectral range around 1.5 μm.     

Polarized spectral properties of Er<Superscript>3+</Superscript> ions in NaGd(WO<Subscript>4</Subscript>)<Subscript>2</Subscript> crystal

Polarized spectral properties of Er³⁺:NaGd(WO₄)₂ single crystal are reported. The crystal was grown by the Czochralski method. The Judd–Ofelt theory was applied to analyze the polarized absorption spectra and then calculate the spontaneous emission probabilities, radiative lifetimes, and branching ratios. Fluorescence decay curves of the ⁴ I _13/2, ⁴ I _11/2, and ⁴ S _3/2 multiplets for the Er³⁺ ions were measured. Stimulated emission cross-sections of the ⁴ I _13/2→⁴ I _15/2 transition obtained by the Fuchtbauer–Ladenberg formula and the reciprocity method were compared. Multi-phonon relaxation rates of the crystal were estimated. Green up-conversion fluorescence around 531 and 552 nm was observed, and the possible up-conversion mechanisms were proposed. PACS 78.20.-e; 42.70.Hj     

Localized desvitrifiation in Er<Superscript>3+</Superscript>-doped strontium barium niobate glass by laser irradiation

Localized desvitrifiation in strontium barium niobate glass doped with Er³⁺ under laser irradiation has been carried out. The samples of this study have been fabricated by the melt quenching method and doped with 5% mol of Er³⁺. A 1.5-W cw Ar laser was focused on the sample to obtain desvitrifiation of the glass. Evidence of the changes induced by the Ar laser has been observed through the analysis of the photoluminescence of the Er³⁺ ions. The transitions corresponding to ²H_11/2→⁴I_15/2, ⁴S_3/2→⁴I_15/2 and ⁴F_9/2→⁴I_15/2 have been studied to analyze structure changes. Microluminescence measurements have been carried out to spatially select positions inside and outside the irradiated area. We have observed changes in the emission bands corresponding to these transitions. The emission bands from Er³⁺ ions in the irradiated zone show a resolved structure while they are broadened outside that area. These changes in the optical properties of the Er³⁺ ions indicate that the Ar-laser irradiation has produced a change in the local structure of the material. These results show that a localized desvitrifiation has been produced after the laser action and the transition from glass to glass ceramic has been completed.     

The upconversion luminescence and magnetism in Yb<Superscript>3+</Superscript>/Ho<Superscript>3+</Superscript> co-doped LaF<Subscript>3</Subscript> nanocrystals for potential bimodal imaging

Biocompatible upconversion nanoparticles with multifunctional properties can serve as potential nanoprobes for multimodal imaging. Herein, we report an upconversion nanocrystal based on lanthanum fluoride which is developed to address the imaging modalities, upconversion luminescence imaging and magnetic resonance imaging (MRI). Lanthanide ions (Yb³⁺ and Ho³⁺) doped LaF₃ nanocrystals (LaF₃ Yb³⁺/Ho³⁺) are fabricated through a rapid microwave-assisted synthesis. The hexagonal phase LaF₃ nanocrystals exhibit nearly spherical morphology with average diameter of 9.8 nm. The inductively coupled plasma mass spectrometry (ICP-MS) analysis estimated the doping concentration of Yb³⁺ and Ho³⁺ as 3.99 and 0.41%, respectively. The nanocrystals show upconversion luminescence when irradiated with near-infrared (NIR) photons of wavelength 980 nm. The emission spectrum consists of bands centred at 542, 645 and 658 nm. The stronger green emission at 542 nm and the weak red emissions at 645 and 658 nm are assigned to ⁵S₂ → ⁵I₈ and ⁵F₅ → ⁵I₈ transitions of Ho³⁺, respectively. The pump power dependence of luminescence intensity confirmed the two-photon upconversion process. The nanocrystals exhibit paramagnetism due to the presence of lanthanide ion dopant Ho³⁺ and the magnetization is 19.81 emu/g at room temperature. The nanocrystals exhibit a longitudinal relaxivity (r ₁) of 0.12 s^?1 mM^?1 and transverse relaxivity (r ₂) of 28.18 s^?1 mM^?1, which makes the system suitable for developing T2 MRI contrast agents based on holmium. The LaF₃ Yb³⁺/Ho³⁺ nanocrystals are surface modified by PEGylation to improve biocompatibility and enhance further functionalisation. The PEGylated nanocrystals are found to be non-toxic up to 50 μg/mL for 48 h of incubation, which is confirmed by the MTT assay as well as morphological studies in HeLa cells. The upconversion luminescence and magnetism together with biocompatibility enables the adaptability of the present system as a nanoprobe for potential bimodal imaging.     

Enhanced Green Emission from Er<Subscript>2</Subscript>WO<Subscript>6</Subscript> Nanocrystals Embedded Composite Tellurite Glasses

A series of tungsten-tellurite glasses activated with different concentrations (0–1.5 mol %) of Er³⁺ has been synthesized. The structural properties of the best luminescent sample and the optical properties of its Er³⁺ ions, are studied both immediate after its preparation as well as after its ageing. On ageing the glass suffers structural reorganization and generates Er₂WO₆—nanocrystals in the matrix, which greatly enhances the normal and upconversion green luminescence efficiency of Er³⁺. The nanocrystal aided enhancement of normal and upconversion luminescence of Er³⁺ of the glass has been attributed to the crystal field effects of the new environment of Er³⁺ in the nanocrystals. A phenomenon of preferential enhancement of red upconversion luminescence at the cost of green upconversion luminescence of Er³⁺ at its higher concentrations in the glass has been observed and the related photo-physics is proposed. The material shows the prospect of being used as NIR solar concentrator.     

On the Luminescence of Ce<Superscript>3+</Superscript>, Eu<Superscript>3+</Superscript>, and Tb<Superscript>3+</Superscript> in Novel Borate LiSr<Subscript>4</Subscript>(BO<Subscript>3</Subscript>)<Subscript>3</Subscript>

This paper reports on the photoluminescence (PL) and time-resolved properties of Ce³⁺, Eu³⁺, and Tb³⁺ in novel LiSr₄(BO₃)₃ powder phosphors. Ce³⁺ shows an emission band peaking at 420 nm under 350-nm UV excitation. Energy transfer from Ce³⁺ to Mn²⁺ takes place in the co-doped samples. Eu³⁺ shows red emission under near UV excitation. LiSr₄(BO₃)₃:Eu³⁺ phosphor could be a suitable candidate for phosphor-converted solid state lighting. The luminescence lifetime is 2.13 ms for Eu³⁺ in LiSr₄(BO₃)₃:0.001Eu³⁺. As Eu³⁺ concentration increasing, the decay curves deviate from exponential behavior. Tb³⁺ shows the strongest ⁵D₄→⁷ F₅ emission line at 540 nm. Decay curves of ⁵D₄→⁷ F₅ and ⁵D₃→⁷ F₅ emission with different Tb³⁺ concentrations were also measured. Cross-relaxation process is discussed based on the decay curves.     

Upconversion white-light emission in Ho³⁺/Yb³⁺/Tm³⁺ tridoped LiNbO₃ single crystal

Ho³⁺/Yb³⁺/Tm³⁺ tridoped LiNbO₃ single crystal exhibiting intense upconversion white light under 980?nm excitation has been successfully fabricated by the Czochralski method. The tridoped LiNbO₃ single crystal offers power dependent color tuning properties by simply changing excitation power. Efficient three-photon blue upconversion emission and two-photon green and red upconversion emissions have been observed. In addition, the red emission of Ho³⁺ originates dominantly from the nonradiative decay of green emission. The LiNbO₃ with upconversion white light will be a potential laser candidate material.     

Spectroscopic properties of fluorophosphate glass with high Er<Superscript>3+</Superscript> concentration

Fluorophosphate glass with 4 mol. % ErF₃ content was prepared. The different scanning calorimetry was conducted. Raman spectrum, infrared transmission spectrum, absorption spectrum were measured. Fluorescence spectrum and lifetime of emission around 1.53 μm were measured under 970 nm laser diode excitation. The metaphosphate content in the composition is limited, but the maximum phonon energy of glass amounts to 1290 cm^-1, and is comparatively high. The full width at half maximum is about 56 nm, and is wider than for most of the materials investigated. The measured lifetime of ⁴ I _13/2→⁴ I _15/2 transition, contributed by the high phonon energy, inefficient interaction of Er³⁺ ions, and low water content, amounts to no less than 7.36 ms though the Er³⁺ concentration is high. This work might provide useful information for the development of compact optical devices. PACS 78.20.-e; 42.70.Ce; 42.70.Hj; 32.70.Cs     

Improvement of thermal and spectroscopic behavior of Er<Superscript>3+</Superscript>/Ce<Superscript>3+</Superscript> co-doped tellurite glass for lasing materials

Tellurite glasses (TeO₂–ZnO–Nb₂O₅) mono-doped Er³⁺ and co-doped Er³⁺/Ce³⁺ have been prepared using the melt-quenching technique. To evaluate the effect of Ce³⁺ on the structural, thermal stability of glass hosts and fluorescence properties of Er³⁺, X-ray diffraction patterns, Ftir spectra, differential scanning calorimeter curves, absorption spectra, fluorescence emission spectra, fluorescence lifetimes, up-conversion emission spectra of glass samples were measured and investigated. Using Judd–Ofelt theory, we calculated intensity parameters (Ω₂, Ω₄ and Ω₆), spontaneous emission probabilities, the radiative lifetime, luminescence branching factors and the quantum yield of luminescence for ⁴I_13/2 → ⁴I_15/2 transition. The co-doping with Ce³⁺ was effective on the suppression of up-conversion emission of Er³⁺ owing to the phonon-assisted energy transfer: Er³⁺:⁴I_11/2 + Ce³⁺:²F_5/2 → Er³⁺:⁴I_13/2 + Ce³⁺:²F_7/2 which contributed the effective enhancement of 1.53 µm fluorescence emission. The change in optical properties with the addition of Ce³⁺ ions have been discussed and compared with other glasses. Using the Mc Cumber method for the ⁴I_13/2 → ⁴I_15/2 transition, absorption cross-section, calculated emission cross-section, and gain cross-section values support that TZNEr1Ce1 glass is a potential material for developing broad-band and high-gain erbium-doped fiber amplifiers applied for 1.53 µm.     

Er3+掺杂新型GeS2-In2S3-CsI玻璃上转换光谱性质研究

用熔融淬冷法制备了掺Er³⁺的80GeS₂-10In2S₃-10CsI(mol%)硫卤玻璃样品,测试了样品的热学稳定性、喇曼光谱、吸收光谱以及上转换光谱,分析了Er³⁺离子在该玻璃中的上转换发光机理.应用Judd-Ofelt理论计算分析了Er3+离子在该样品中的强度参量Ωt(t=2,4,6)、自发辐射跃迁几率A、荧光分支比β以及辐射寿命τrad等光谱参量.在980 nm LD泵浦激发下,首次在该种玻璃中观察到强烈的绿光(526 nm、549 nm),分别对应于2H11/2→4I15/2和4S3/2→4I15/2的跃迁,其中549 nm处绿光较强.549 nm处上转换荧光寿命为0.34 ms,量子效率为69%.同时研究了绿光(526 nm、549 nm)上转换发光强度随泵浦激发功率的变化,其发光曲线拟合斜率分别为1.71和2.03,表明绿光是双光子吸收过程.研究结果表明：掺Er³⁺的80GeS₂-10In2S₃-10CsI硫卤玻璃是一种上转换绿光激光器的潜在基质材料.     

980 nm激发下Er3+/Yb3+共掺杂ZrO2-Al2O3粉末的上转换发光特性

通过固相反应法制备了Er³⁺/Yb³⁺共掺杂ZrO₂-Al₂O₃粉末的样品，并对样品在980nm激光激发下的上转换发光特性进行了研究.从发射光谱可以发现，在可见光范围内有3个强的发光带，一个位于654nm附近的红光带和两个分别位于545nm、525nm附近的绿光带，分别对应于Er³⁺离子的以下辐射跃迁：⁴F_9/2→⁴I_15/2、⁴S_3/2→⁴I_15/2、 ²H_11/2→⁴I_15/2.其中又以Er³⁺离子的⁴F_9/2→⁴I_15/2跃迁产生的红色荧光辐射最强.对其上转换发光机制进行了分析，发现这三个发光过程都是双光子过程.对样品粉末进行了XRD检测，发现ZrO₂主要以立方相为主，并且计算得到了这种立方结构的晶格常数.Al₂O₃固溶于ZrO₂中，Al³⁺嵌入ZrO₂后产生氧空位，导致ZrO₂晶体的对称性降低，这种结构变化更有利于提高上转换效率，即上转换发光强度增强. 关键词： 3+/Yb³⁺')" href="#">Er³⁺/Yb³⁺ 上转换 2-Al₂O₃')" href="#">ZrO₂-Al₂O₃ 荧光 稀土     

Sensitizer-dependent up-conversion of Ho<Superscript>3+</Superscript> in nanocrystalline Y<Subscript>2</Subscript>O<Subscript>3</Subscript>

Ho³⁺–Yb³⁺ co-doped Y₂O₃ nanocrystals were synthesized by firing hydroxy carbonate precursors. Yb³⁺-concentration-dependent up-conversion properties of Ho³⁺ in Y₂O₃ nanocrystals have been investigated. The relative intensity of up-converted red emission increases more quickly than that of the green and the near-infrared ones with the enhancement of the concentration of Yb³⁺. It is believed that the energy process ⁵ S ₂ (⁵F₄) (Ho) + ⁵ I ₇ (Ho) →⁵ I ₆ (Ho)+⁵ F ₅ (Ho) plays an important role in the population of the ⁵ F ₅ level of Ho³⁺. The result indicates that the intensity ratio of the green emission to the red one can be tuned by changing the sensitizer concentration. PACS 78.55.-m     

Study of frequency upconversion in Yb<Superscript>3+</Superscript>/Eu<Superscript>3+</Superscript> by cooperative energy transfer in oxyfluoroborate glass matrix

Oxyfluoroborate glass co-doped with Eu and Yb ions has been prepared and characterized for its optical properties through photoluminescence, absorption and lifetime measurements. An intense red upconversion is observed from the ⁵D₀ level of Eu³⁺ ions through energy transfer from Yb³⁺ to Eu³⁺ ion when excited with 980 nm. The Judd–Ofelt parameters have been evaluated to estimate the local site symmetry around the Eu³⁺ ions. These parameters have been used to derive radiative properties such as transition probabilities, branching ratios, radiative lifetimes and stimulated emission cross-sections for the ⁵D₀–⁷F_J transitions. Decay of excitation of the ⁵D₀ level has been measured by monitoring the ⁵D₀→⁷F₂ transition (613 nm) at room temperature. Quantum efficiency for this transition is found to be 73%. We also monitored the effect of temperature on the fluorescence emission of Eu³⁺. PACS 42.70.Ce; 42.70.Hj     

Upconversion excitations in Pr<Superscript>3+</Superscript>-doped BaY<Subscript>2</Subscript>F<Subscript>8</Subscript> crystal

We report the orange-to-blue and infrared-(IR)-to-blue wavelengths upconversion luminescence in Pr³⁺:BaY₂F₈ crystals. Mechanism of the orange light upconversion into blue ³P₀ state emission was confirmed to be energy transfer between two Pr³⁺ ions in the ¹D₂ state. IR-to-blue upconversion has only been observed under two different color IR pumping. The first resonant step was the ³H₄→¹G₄ ground state absorption transition, and the second resonant transition was the excited state absorption from the ¹G₄ to ¹I₆ and ³P_J levels. A comparison of the efficiency of the IR-to-blue upconversion in several praseodymium activated host is presented and discussed. A model of the IR pumped upconversion praseodymium blue laser is presented and the population inversion conditions are calculated.