Synthesis of methyl methacrylate,styrene, and isobutylene multiblock copolymers using atom transfer and cationic polymerization

ABCBA‐type pentablock copolymers of methyl methacrylate, styrene, and isobutylene (IB) were prepared by the cationic polymerization of IB in the presence of the α,ω‐dichloro‐PS‐b‐PMMA‐b‐PS triblock copolymer [where PS is polystyrene and PMMA is poly(methyl methacrylate)] as a macroinitiator in conjunction with diethylaluminum chloride (Et₂AlCl) as a coinitiator. The macroinitiator was prepared by a two‐step copper‐based atom transfer radical polymerization (ATRP). The reaction temperature, ?78 or ?25 °C, significantly affected the IB content in the resulting copolymers; a higher content was obtained at ?78 °C. The formation of the PIB‐b‐PS‐b‐PMMA‐b‐PS‐b‐PIB copolymers (where PIB is polyisobutylene), prepared at ?25 (20.3 mol % IB) or ?78 °C (61.3 mol % IB; rubbery material), with relatively narrow molecular weight distributions provided direct evidence of the presence of labile chlorine atoms at both ends of the macroinitiator capable of initiation of cationic polymerization of IB. One glass‐transition temperature (T_g), 104.5 °C, was observed for the aforementioned triblock copolymer, and the pentablock copolymer containing 61.3 mol % IB showed two well‐defined T_g's: ?73.0 °C for PIB and 95.6 °C for the PS–PMMA blocks. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 3823–3830, 2005     

Structure–property relationships in modified natural rubber latexes grafted with methyl methacrylate and vinyl neo‐decanoate

A series of modified natural rubber latexes (NRLs) grafted with poly(methyl methacrylate) (PMMA) were prepared by seeded emulsion polymerization with NRL as the seed polymer. Two different redox systems, cumene hydroperoxide (CHP)/tetraethylene pentamine (TEPA) and tert‐butyl hydroperoxide (t‐BHP)/TEPA, were used to initiate polymerization, and phase mixing was promoted by the addition of vinyl neo‐decanoate (VneoD). The CHP/TEPA system was more efficient than t‐BHP/TEPA for the grafting of secondary polymers in modified natural rubber (NR). The enhanced phase mixing in the presence of VneoD was attributed to the solubility parameter of the VneoD‐rich methyl methacrylate–VneoD copolymer formed late in the reaction, lying between that of PMMA and NR, and the extent to which this polymer was grafted to the NR backbone. The viscoelastic properties of the polymers were investigated as a function of composition, temperature, and frequency; changes in viscoelastic behavior consistent with the presence of a high‐T_g PMMA phase (where T_g is the glass‐transition temperature) were observed. This suggested a degree of phase mixing that increased with increasing VneoD content and increasing flux of oxygen‐centered radicals within the NR particles. More phase mixing resulted in poorer film formation, which was consistent with the localization of a high‐T_g secondary polymer phase near the particle surface. The apparent concentration of PMMA near the surface of the particles was also observed with transmission electron microscopy. The localization of PMMA near the particle surfaces was consistent with the presumed locus of radical generation in these systems: the redox couple used to initiate the polymerization consisted of an oil‐soluble hydroperoxide and a water‐soluble amine that reacted predominantly at the water/particle interface. The viscoelastic properties of the modified NRLs that were prepared suggest that these synthetic procedures provide a means of controlling phase mixing and branching, such as for improving the suitability of these modified rubbers in pressure‐sensitive‐adhesive formulations. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 809–822, 2002; DOI 10.1002/pola.10165     

Rich‐Syndiotacticity of Poly(cyclohexyl methacrylate) Prepared by Modified Microemulsion Polymerization

Nanoscale poly(cyclohexyl methacrylate) (PCHMA) particles were prepared by a modified microemulsion polymerization procedure. ¹³C‐NMR analysis suggested that such PCHMA samples were higher in syndiotactic content (61–72% rr) and lower in isotactic content (1–3% mm). The glass transition temperatures (T_g's) of the products were also higher than that reported in the literature. The polymer properties, such as particle size, molecular weight, tacticity, and T_g were affected by the reaction conditions. The smaller the particle size, the higher the syndiotacticity, the lower the isotacticity and the greater the molecular weight, then the higher the T_g of the PCHMA samples. Possible mechanism of rich‐syndiotacticity was also discussed.     

Covalent bonded polymer–graphene nanocomposites

This report describes a new route to covalently bonded polymer–graphene nanocomposites and the subsequent enhancement in thermal and mechanical properties of the resultant nanocomposites. At first, the graphite is oxidized by the modified Hummers method followed by functionalization with Octadecylamine (ODA). The ODA functionalized graphite oxides are reacted with methacryloyl chloride to incorporate polymerizable ? C?C? functionality at the nanographene platelet surfaces, which were subsequently employed in in situ polymerization of methylmethacrylate to obtain covalently bonded poly(methyl methacrylate) (PMMA)–graphene nanocomposites. The obtained nanocomposites show significant enhancement in thermal and mechanical properties compared with neat PMMA. Thus, even with 0.5 wt % graphene nanosheets, the T_g increased from 119 °C for neat PMMA to 131 °C for PMMA–graphene nanocomposite, and the respective storage modulus increased from 1.29 to 2 GPa. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 4262–4267, 2010     

Influence of sample preparation and processing on observed glass transition temperatures of polymer nanocomposites

Polymer composites composed of poly(methyl methacrylate) (PMMA) and silica (14 nm diameter) have been investigated. The influences of sample preparation and processing have been probed. Two types of sample preparation methods were investigated: (i) solution mixture of PMMA and silica in methyl ethyl ketone and (ii) in situ synthesis of PMMA in the presence of silica. After removing all solvent or monomer, as confirmed using thermogravimetric analysis, and after compression molding, drops in T_g of 5–15 °C were observed for all composites (2–12% w/w silica) and even pure polymer reference samples. However, after additional annealing for 72 h at 140 °C, all previously observed drops in T_g disappeared, and the intrinsic T_g of bulk, pure PMMA was again observed. This is indicative of nonequilibrium trapped voids being present in the as‐molded samples. Field‐emission scanning electron microscopy was used to show well‐dispersed particles, and dynamic mechanical analysis was used to probe the mechanical properties (i.e., storage modulus) of the fully equilibrated composites. Even though no equilibrium T_g changes were observed, the addition of silica to the PMMA matrices was observed to improve the mechanical properties of the glassy polymer host. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 2270–2276, 2007     

Miscibility and phase structure of binary blends of polylactide and poly(methyl methacrylate)

Blends of amorphous poly(DL‐lactide) (DL‐PLA) and crystalline poly(L‐lactide) (PLLA) with poly(methyl methacrylate) (PMMA) were prepared by both solution/precipitation and solution‐casting film methods. The miscibility, crystallization behavior, and component interaction of these blends were examined by differential scanning calorimetry. Only one glass‐transition temperature (T_g) was found in the DL‐PLA/PMMA solution/precipitation blends, indicating miscibility in this system. Two isolated T_g's appeared in the DL‐PLA/PMMA solution‐casting film blends, suggesting two segregated phases in the blend system, but evidence showed that two components were partially miscible. In the PLLA/PMMA blend, the crystallization of PLLA was greatly restricted by amorphous PMMA. Once the thermal history of the blend was destroyed, PLLA and PMMA were miscible. The T_g composition relationship for both DL‐PLA/PMMA and PLLA/PMMA miscible systems obeyed the Gordon–Taylor equation. Experiment results indicated that there is no more favorable trend of DL‐PLA to form miscible blends with PMMA than PLLA when PLLA is in the amorphous state. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 23–30, 2003     

Glass‐transition temperature behavior of alumina/PMMA nanocomposites

Alumina/poly(methyl methacrylate) (PMMA) nanocomposites were synthesized by an in situ free‐radical polymerization process with 38 and 17 nm diameter γ‐alumina nanoparticles. At extremely low filler weight fractions (<1.0 wt % of 38 nm fillers or < 0.5 wt % of 17 nm fillers) the glass‐transition temperature (T_g) of the nanocomposites drops by 25 °C when compared to the neat polymer. Further additions of filler (up to 10 wt %) do not lead to additional T_g reductions. The thermal behavior is shown to vary with particle size, but this dependence can be normalized with respect to a specific surface area. The nanocomposite T_g phenomenon is hypothesized to be because of nonadhering nanoparticles that serve as templates for a porous system with many internal interfaces that break up the percolating structure of dynamically heterogeneous domains recently suggested by Long, D.; and Lequeux, F. Eur Phys J E 2001, 4, 371 to be responsible for the T_g reductions in polymer ultrathin films. The results also point to a far field effect of the nanoparticle surface on the bulk matrix. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4371–4383, 2004     

A macromonomer approach to the synthesis of poly(1,1‐bis(ethoxycarbonyl)‐2‐vinyl cyclopropane‐graft‐dimethyl siloxane)

Poly(1,1‐bis(ethoxycarbonyl)‐2‐vinyl cyclopropane (ECVP)‐graft‐dimethyl siloxane) copolymers were prepared using a macromonomer approach. Poly(dimethyl siloxane) (PDMS) macromonomers were prepared by living anionic polymerization of cyclosiloxanes followed by sequential chain‐end capping with allyl chloroformate. These macromonomers were then copolymerized with ECVP. MALDI‐ToF mass spectrometry and ¹H NMR spectroscopy were used to show that the macromonomers had approximately 80% of the end groups functionalized with allyl carbonate groups. Gradient polymer elution chromatography showed that high yields of the graft copolymers were obtained, along with only small fractions of the PECVP and PDMS homopolymers. Differential scanning calorimetry showed that the low glass transition temperature (T_g) of the PDMS component could be maintained in the graft copolymers. However, the T_g was a function of polymer composition and the polymers produced had T_gs that ranged from ?50 to ?120 °C. © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Influence of interaction between poly(methyl methacrylate) and clay on the properties of nanocomposites prepared by a heterocoagulation method

To have a better insight into the effect of interaction between polymer matrix and clay on the properties of nanocomposite, poly(methyl methacrylate)/clay nanocomposites were prepared by a heterocoagulation method. Using a reactive cationic emulsifier, methacryloyloxyethyltrimethyl ammonium chloride (METAC), a strong polymer–clay interaction was obtained with the advantage of keeping a consistent polymer matrix property. X‐ray diffraction and transmission electronic microscopy indicated an exfoliated structure in nanocomposites. The glass transition temperature (T_g) of the nanocomposites was measured by DSC and DMA. The DMA results showed that with a strong interaction, PMMA–METAC nanocomposite showed a 20 °C enhancement in glass transition temperature (T_g), whereas a slight increase in T_g was observed for PMMA–cetyl trimethylammonium bromide (CTAB)/clay nanocomposite with a weak interaction. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 733–738, 2010     

Synthesis and thermal characterization of poly(dimethyl bicyclobutane‐1,3‐dicarboxylate) and its copolymers

Dimethyl bicyclobutane‐1,3‐dicarboxylate was synthesized. Its homopolymer (PDBD) containing exclusively cyclobutane rings in its backbone was prepared by free radical polymerization. The copolymers of this bicyclobutane monomer with methyl methacrylate were also prepared. The glass transition temperature of the homopolymer is 159°C, while those of its copolymers are 143 and 121°C with 75/25 and 50/50 of the P(DBD/MMA) composition ratio, respectively. The T_g of PDBD homopolymer is substantially higher than that of commercial PMMA homopolymer despite a lower molecular weight, and is also much higher than that of its monomethyl cyclobutanecarboxylate analogue. These DBD homopolymer and copolymers also show better thermostability than the PMMA homopolymer. The weight‐average molecular weight of homopolymer is 37,000. The polydispersities of these polymers are relatively narrow, with the range of 1.6–1.9. These polymers form clear colorless films resembling PMMA film. The DBD homopolymer film shows a very similar optical cutoff compared to PMMA. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1569–1575, 1999     

Synthesis of well‐defined multigraft copolymers by a two‐step living radical polymerization with nitroxyl‐functionalized poly(methyl methacrylate)

Novel multigraft copolymers of poly(methyl methacrylate‐graft‐polystyrene) (PMMA‐g‐PS) in which the number of graft PS side chains was varied were prepared by a subsequent two‐step living radical copolymerization approach. A polymerizable 4‐vinylbezenyl 2,2,6,6‐tetramethyl‐1‐piperidinyloxy (TEMPO) monomer (STEMPO), which functioned as both a monomer and a radical trapper, was placed in a low‐temperature atom transfer radical polymerization (60°C) process of methyl methacrylate with ethyl 2‐bromopronionate (EPNBr) as an initiator to gain ethyl pronionate‐capped prepolymers with TEMPO moieties, PMMA‐STEMPOs. The number of TEMPO moieties grafted on the PMMA backbone could be designed by varying STEMPO/EPNBr, for example, the ratios of 1/2, 2/3, or 3/4 gained one, two, or three graft TEMPO moieties, respectively. The resulting prepolymers either as a macromolecular initiator or a trapper copolymerized with styrene in the control of stable free‐radical polymerization at an elevated temperature (120 °C), producing the corresponding multigraft copolymers, PMMA‐g‐PSs. The nitroxyl‐functionalized PMMA prepolymers produced a relatively high initiation efficiency (>0.8) as a result of the stereohindrance and slow diffusion of TEMPO moieties connected on the long PMMA backbone. The polymerization kinetics in two processes showed a living radical polymerization characteristic. The molecular structures of these prepolymers and graft copolymers were well characterized by combining Fourier transform infrared spectroscopy, gel permeation chromatography, chemical element analysis, and ¹H NMR. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1876–1884, 2002     

Modifying an amorphous polymer to a fast crystallizing semi‐crystalline material by copolymerization with monodisperse amide segments

Segmented block copolymers of polysulphone with monodisperse amide segments were synthesized by a melt and a solution polymerization method. Both triblock and multiblock copolymers were prepared. The length of the difunctional polysulphone was varied from 2000 to 20,000 g/mol. The monodisperse amide segment was the tetra‐amide T6T6T based on terephthalic acid (T) and hexamethylene diamine (6) units. The main goal of this work was to study if the high T_g amorphous polysulphone could be modified to a high T_g semi‐crystalline PSU‐T6T6T copolymer. The copolymers were characterized by viscosity measurements, NMR, FTIR, MALDI‐TOF, DSC, and DMA. Depending on the amide concentration in the copolymers the T6T6T melting temperatures ranged between 220 and 270 °C and thus the crystallization window was small 50–100 °C. From the FTIR results, it was revealed that the crystallinity of the T6T6T segments in the copolymer could be very high, up to 92–97%. The T6T6T has crystallized out into nanoribbons with a high aspect ratio. These high T_g semi‐crystalline copolymers had a high dimensional and solvent resistance. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 63–73, 2010     

Poly(methyl methacrylate)/Methacryl-POSS Nanocomposites with Excellent Thermal Properties

Poly(methyl methacrylate) (PMMA) nanocomposites containing (methacryloxy)propyl polyhedral oligomeric silsesquioxane (methacryl‐POSS) were prepared by bulk‐polymerization process. The structures of the products were characterized by FTIR, solid‐state NMR, TEM, XRD, DSC, TGA, XPS and UV‐Vis spectra. The hybrid materials were found to be largely homogeneous. DSC and TGA results indicate that the thermal properties of PMMA nanocomposites are significantly improved. The glass transition temperature (T_g) and thermal decomposition temperature (T_dec) of the nanocomposites increased by 58 and 110°C, respectively. The bulk hybrid material maintains excellent optical transparency in visible region.     

Indentation of poly(methyl methacrylate) under high‐pressure gases

The variation of the indentation hardness of a high molecular weight poly(methyl methacrylate) (PMMA) subjected to CO₂ and Ar at high pressure was measured in situ. The samples were subjected to gas exposure for 3 h at 40 °C before a conical indenter of an included angle at 105 °, with a fixed load of 0.237 kg, was applied for a loading time of 60 s. The data show that both CO₂ and Ar reduce the hardness of PMMA to a comparable extent at low pressures. The hardness of PMMA subjected to Ar indicates a minimum at about 4 MPa and then increases. CO₂ produced a monotone decreasing trend in hardness in the pressure range studied, and the glass‐transition temperature (T_g) was achieved at about 6.0 MPa. The change in hardness is attributed to plasticization of the polymer matrix that is more extensive for CO₂. The relationship between the change in hardness for this PMMA subjected to high‐pressure CO₂, the corresponding change in the T_g, and the associated swelling of the polymer is discussed. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 3020–3028, 2001     

Segmental and secondary dynamics in hydrogen‐bonded poly(4‐vinylphenol)/poly(methyl methacrylate) blends

Broadband dielectric spectroscopy was used to study the segmental (α) and secondary (β) relaxations in hydrogen‐bonded poly(4‐vinylphenol)/poly(methyl methacrylate) (PVPh/PMMA) blends with PVPh concentrations of 20–80% and at temperatures from ?30 to approximately glass‐transition temperature (T_g) + 80 °C. Miscible blends were obtained by solution casting from methyl ethyl ketone solution, as confirmed by single differential scanning calorimetry T_g and single segmental relaxation process for each blend. The β relaxation of PMMA maintains similar characteristics in blends with PVPh, compared with neat PMMA. Its relaxation time and activation energy are nearly the same in all blends. Furthermore, the dielectric relaxation strength of PMMA β process in the blends is proportional to the concentration of PMMA, suggesting that blending and intermolecular hydrogen bonding do not modify the local intramolecular motion. The α process, however, represents the segmental motions of both components and becomes slower with increasing PVPh concentration because of the higher T_g. This leads to well‐defined α and β relaxations in the blends above the corresponding T_g, which cannot be reliably resolved in neat PMMA without ambiguous curve deconvolution. The PMMA β process still follows an Arrhenius temperature dependence above T_g, but with an activation energy larger than that observed below T_g because of increased relaxation amplitude. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3405–3415, 2004     

Effect on structural relaxation of the poly(methyl‐methacrylate) copolymers chain flexibility

The structural relaxation of poly(methyl‐methacrylate) (PMMA)‐based copolymers with different chain flexibility has been studied by DSC with the classical procedure of the isothermal and dynamical approach. Modified PMMA with different chain flexibility have been prepared by free radical polymerization in solution using a mixture of monomers containing 10 mol % of alkyl methacrylate (i.e., ethyl, buthyl, and hexyl methacrylate). The molecular characteristics of all the prepared copolymers have been performed by a multiangle laser light scattering (MALS) photometer on‐line to a size exclusion chromatography (SEC) system (SEC‐MALS) after and before the thermal treatments, NMR (¹H and ¹³C) and MALDI‐TOF mass spectrometry. A comparison of the apparent relaxation rate (R_H) was appraised from the enthalpy loss by annealing the different samples at the same level of undercooling (T_a = T_g ? 18 °C). It was found an increase of R_H increasing the chain flexibility in the copolymers. Dynamical tests, performed at different cooling rates, have been used to estimate the apparent activation energy of the relaxation process. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 596–607, 2009     

Preparation,Tg improvement,and thermal stability enhancement mechanism of soluble poly(methyl methacrylate) nanocomposites by incorporating octavinyl polyhedral oligomeric silsesquioxanes

The soluble poly(methyl methacrylate‐co‐octavinyl‐polyhedral oligomeric silsesquioxane) (PMMA–POSS) hybrid nanocomposites with improved T_g and high thermal stability were synthesized by common free radical polymerization and characterized using FTIR, high‐resolution ¹H NMR, ²⁹Si NMR, GPC, DSC, and TGA. The POSS contents in the nanocomposites were determined based on FTIR spectrum, revealing that it can be effectively adjusted by varying the feed ratio of POSS in the hybrid composites. On the basis of the ¹H NMR analysis, the number of the reacted vinyl groups on each POSS molecules was determined to be about 6–8. The DSC and TGA measurements indicated that the hybrid nanocomposites had higher T_g and better thermal properties than the pure PMMA homopolymer. The T_g increase mechanism was investigated using FTIR, displaying that the dipole–dipole interaction between PMMA and POSS also plays very important role to the T_g improvement besides the molecular motion hindrance from the hybrid structure. The thermal stability enhances with increase of POSS content, which is mainly attributed to the incorporation of nanoscale inorganic POSS uniformly dispersed at molecular level. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5308–5317, 2007     

Nanostructured latexes made by a sequential multistage emulsion polymerization

A series of linear and lightly crosslinked nanostructured latices was prepared by a sequential multistage semicontinuous emulsion polymerization process alternating styrene (S) and n‐butyl acrylate (BA) monomer feeds five times, that is ten stages, and vice versa, along with several control latices. Transmission electron micrographs of the RuO₄‐stained cross sections of nanostructured and copolymer latex particles and films showed that their particle morphologies were not very different from each other, but the nanostructured latex particles were transformed into a nanocomposite film containing both polystyrene (PS) and poly(n‐butyl acrylate) (PBA) nanodomains interconnected by their diffuse polymer mixtures (i.e. interlayers). The thermal mechanical behaviors of the nanostructured latex films showed broad but single T_gs slightly higher than those of their counterpart copolymer films. These single T_gs indicated that their major component phases were the diffuse interlayers and that they behaved like pseudopolymer alloys. The minimum film formation temperatures of nanostructured latices capped with PBA and PS, respectively, were 15 °C lower than and equal to those of their counterpart copolymer latices, but their T_gs were about 10 °C higher. Consequently, nanostructured latices enabled us to combine good film formation with high strengths for adhesives and coatings applications. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2826–2836, 2006     

The design,synthesis, and nonlinear optical properties of novel X‐type polyurethane containing dicyanovinylnitroresorcinoxy group with enhanced SHG thermal stability

Novel X‐type polyurethane 5 containing 4‐(2′,2′‐dicyanovinyl)‐6‐nitroresorcinoxy groups as nonlinear optical (NLO) chromophores, which constitute parts of the polymer backbone, was prepared and characterized. Polyurethane 5 is soluble in common organic solvents such as acetone and N,N‐dimethylformamide. It shows thermal stability up to 280 °C from thermogravimetric analysis with a glass transition temperature (T_g) obtained from differential scanning calorimetry thermogram of around 120 °C. The second harmonic generation (SHG) coefficient (d₃₃) of poled polymer film at 1064‐nm fundamental wavelength is around 6.12 × 10^?9 esu. The dipole alignment exhibits a thermal stability even at 5 °C higher than T_g, and there was no SHG decay below 125 °C due to the partial main chain character of the polymer structure, which is acceptable for NLO device applications. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Micromechanical fast quasi‐static detection of α and β relaxations with nanograms of polymer

Micromechanical string resonators are used as a highly sensitive tool for the detection of glass transition (T_g or α relaxation) and sub‐T_g (β relaxation) temperatures of polystyrene (PS) and poly (methyl methacrylate) (PMMA). The characterization technique allows for a fast detection of mechanical relaxations of polymers with only few nanograms of sample in a quasi‐static condition. The polymers are spray coated on one side of silicon nitride (SiN) microstrings. These are pre‐stressed suspended structures clamped on both ends to a silicon frame. The resonance frequency of the microstrings is then monitored as a function of increasing temperature. α and β relaxations in the polymer affect the net static tensile stress of the microstring and result in measureable local frequency slope maxima. T_g of PS and PMMA is detected at 91 ±2°C and 114 ±2°C, respectively. The results match well with the glass transition values of 93.6°C and 114.5°C obtained from differential scanning calorimetry of PS and PMMA, respectively. The β relaxation temperatures are detected at 30 ± 2°C and 33 ± 2°C for PS and PMMA which is in accordance with values reported in literature. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1035–1039