Magnetic and magnetoresistive properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–Sr<Subscript>2</Subscript>FeMoO<Subscript>6–δ</Subscript>–Al<Subscript>2</Subscript>O<Subscript>3</Subscript> nanoheterostructures

A method has been developed for fabricating nanoporous matrices based on anodic aluminum oxide for the deposition of ferromagnetic nanoparticles in them. The modes of deposition of strontium ferromolybdate thin films prepared by the ion-plasma method have been worked out, and the magnetic and magnetoresistive properties, structure, and composition of the films have been investigated. It has been revealed that the microstructure and properties of the strontium ferromolybdate films deposited by ionplasma sputtering depend on the deposition rate and the temperature of the substrate. Based on the measurement of the electrical resistivity of nanoheterostructures in a magnetic field, it has been found that the magnetoresistance reaches 14% at T = 15 K and B = 8 T, which is due to the manifestation of tunneling magnetoresistance.     

Elastic properties of TeO<Subscript>2</Subscript>–B<Subscript>2</Subscript>O<Subscript>3</Subscript>–Ag<Subscript>2</Subscript>O glasses

A series of glasses [(TeO₂) _x (B₂O₃)_1−x ]_1−y [Ag₂O] _y with x = 70 and y = 10, 15, 20, 25 and 30 mol% were synthesised by rapid quenching. Longitudinal and shear ultrasonic velocity were measured at room temperature and at 5 MHz frequency. Elastic properties, Poisson's ratio, microhardness, softening temperature and Debye temperature have been calculated from the measured density and ultrasonic velocity at room temperature. The experimental results indicate that the elastic constants depend upon the composition of the glasses and the role of the Ag₂O inside the glass network is discussed. Estimated parameters based on Makishima–Mackenzie theory and bond compression model were calculated in order to analyse the experimental elastic moduli. Comparison between the experimental elastic moduli data obtained in the study and the calculated theoretically by the mentioned above models has been discussed.     

Calculation of refractive indices for the (NH<Subscript>2</Subscript>CH<Subscript>2</Subscript>COOH)<Subscript>2</Subscript> · HNO<Subscript>3</Subscript> crystal

The refraction R of the diglycine nitrate (DGN) crystal, (NH₂CH₂COOH)₂ · HNO₃, in the para-and ferroelectric phases has been calculated in the model of noninteracting diatomic chemical bonds of the elementary unit cell of the crystal on the basis of the longitudinal and transversal polarizabilities of these bonds. The calculated magnitudes of the principal refractive indices n _p , n _m , and n _g and the orientations of the optical indicatrix of the crystal agree satisfactorily with experimentally observed values. Introducing the coefficient of Lorenz-Lorentz interaction x into the corresponding formula permits better agreement of the calculated and experimental refractive indices of DGN crystal to be obtained. The temperature changes of these x coefficients upon the ferroelectric phase transition in the DGN crystal have been analyzed.     

Structural properties of composite cathode material LiFePO<Subscript>4</Subscript>–Li<Subscript>3</Subscript>V<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>

Composite cathode material LiFePO₄–Li₃V₂(PO₄)₃ is synthesized through a chemical reduction and lithiation using FeVO₄·xH₂O as both iron and vanadium sources. The structural properties of LiFePO₄–Li₃V₂(PO₄)₃ are investigated. X-ray diffraction results show the composite material containing olivine type LiFePO₄ and monoclinic Li₃V₂(PO₄)₃ phases. High-resolution transmission electron microscopy and energy-dispersive X-ray spectrometry results indicate that mutual doping effects take place between the LiFePO₄ and Li₃V₂(PO₄)₃ particles with V³⁺ doping the LiFePO₄ while Fe²⁺ dopes the Li₃V₂(PO₄)₃. LiFePO₄–Li₃V₂(PO₄)₃ nanocomposites are formed in the carbon webs. There is no structural compatibility between monoclinic (Li₃V₂(PO₄)₃) and olivine (LiFePO₄) domains in composite material LiFePO₄–Li₃V₂(PO₄)₃.     

Specific heat of the [NH<Subscript>2</Subscript>(CH<Subscript>3</Subscript>)<Subscript>2</Subscript>]<Subscript>2</Subscript>ZnCl<Subscript>4</Subscript> crystal in the temperature region 80–300 K

The specific heat of [NH₂(CH₃)₂]₂ZnCl₄ was measured calorimetrically in the temperature region 80–300 K. As the temperature T decreases, the C _p (T) dependence indicates a phase transition sequence, with the phase transition at T₆=151 K observed for the first time. The thermodynamic characteristics of the crystal were refined. The transformation occurring at T₂=298.3 K is shown to be an incommensurate-commensurate phase transition.     

High-Temperature Heat Capacity of Zn<Subscript>2</Subscript>V<Subscript>2</Subscript>O<Subscript>7</Subscript>–Cu<Subscript>2</Subscript>V<Subscript>2</Subscript>O<Subscript>7</Subscript> Solid Solutions

Differential scanning calorimetry has been used to study the influence of temperature on the heat capacity of synthesized vanadates Zn₂V₂O₇, (Cu_0.56Zn_1.44)V₂O₇, and (Cu_1.0Zn_1.0)V₂O₇. It is found that dependences C_p = f(T) have extremes. The thermodynamic properties of Zn₂V₂O₇ have been determined.     

Sol–gel synthesis and characterization of Li<Subscript>2</Subscript>CO<Subscript>3</Subscript>–Al<Subscript>2</Subscript>O<Subscript>3</Subscript> composite solid electrolytes

Composite solid electrolytes in the system (1???x)Li₂CO₃–xAl₂O₃, with x?=?0.0–0.5 (mole), were synthesized by a sol–gel method. The synthesis carried out at low temperature resulted in voluminous and fluffy products. The obtained materials were characterized by X-ray diffraction, differential scanning calorimetry, scanning electron microscopy/energy-dispersive X-ray, Fourier transform infrared spectroscopy and AC impedance spectroscopy. Structural analysis of the samples showed an amorphous feature of Li₂CO₃ and traces of α-LiAlO₂, γ-LiAlO₂ and LiAl₅O₈. The prepared composite samples possess high ionic conductivities at 130–180 °C on account of the presence of lithium aluminates as well as the formation of a high concentration of an amorphous phase of Li₂CO₃ via this sol–gel preparative technique.     

XRD,impedance, and Mössbauer spectroscopy study of the Li<Subscript>3</Subscript>Fe<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript> + Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> composite for Li ion batteries

The synthesis procedure of the Li₃Fe₂(PO₄)₃?+?Fe₂O₃ composite is presented. The monoclinic (A type) and hematite phases were detected by X-ray diffraction after the synthesis of the composite. The structural α–β (at a temperature of 460 K) and β–γ (at a temperature of 523 K) phase transitions in the composite were indicated by the anomalies of the electrical conductivity, dielectric permittivity, and changes of activation energies of conductivity. Two phase transitions have been detected in the Li₃Fe₂(PO₄)₃?+?Fe₂O₃ composite by ⁵⁷Fe Mössbauer spectroscopy: the phase transition in Li₃Fe₂(PO₄)₃ from the paramagnetic to antiferromagnetic phase at temperature T _N?=?29.5 K and the Morin phase transition in Fe₂O₃ at temperature T _M?=?235 K.     

Electrical switching in the MoO<Subscript>3</Subscript>–WO<Subscript>3</Subscript>–P<Subscript>2</Subscript>O<Subscript>5</Subscript> and MoO<Subscript>3</Subscript>–P<Subscript>2</Subscript>O<Subscript>5</Subscript> glasses

High field electrical switching on blown films of MoO₃(60%)–P₂O₅(40%), MoO₃(50%)–WO₃(10%)–P₂O₅(40%), and MoO₃(45%)–WO₃(15%)–P₂O₅(40%) having different thicknesses was studied and compared. Switching was observed using two terminal samples. S-type current–voltage characteristic (current-controlled negative resistance—CCNR) with memory was observed in molybdenum–phosphate glasses, but N-type characteristic (voltage-controlled negative resistance—VCNR) with threshold in tungsten–molybdenum–phosphate glasses was observed. The important observation was that with the addition of WO₃ to binary MoO₃–P₂O5 led to a change of I–V characteristic from CCNR with memory to VCNR with threshold. The measurements of density and molar volume showed linear relation between MoO₃ content and density which decreased with the increase of MoO₃ content. The samples’ thickness had no significant effect on threshold voltage. The attained results also indicated that the electrode material had no effect on switching property of devices. The switching behavior of the devices did not show any dependence on the polarity of the applied voltage. In terms of the effect of heat on the switching behavior of molybdenum–phosphate glasses, it was found that threshold voltage decreases with increasing of temperature. Finally, the switching phenomenon was explained by thermal (formation of crystalline filaments) and electronic models.     

Influence of Matrix Nature on the Structural Characteristics of In<Subscript>2</Subscript>O<Subscript>3</Subscript>–CeO<Subscript>2</Subscript> and SnO<Subscript>2</Subscript>–CeO<Subscript>2</Subscript> Composites Fabricated by the Impregnation Method

The structural characteristics, valence states, and distribution of cerium ions between the components in In₂O₃–CeO₂ and SnO₂–CeO₂ nanocomposites fabricated using the impregnation method were studied. X-ray photoelectron spectroscopy (XPS) and energy-dispersive X-ray spectroscopy (EDX) were used to show that, during impregnation, cerium ions are not included into In₂O₃ crystals and are disposed only on their surface in the form of nano-sized crystallites or amorphous clusters. On the other side, under the contact of CeO₂ clusters with a surface of SnO₂ matrix crystals, cerium ions penetrate into the surface layer of these crystals. In contrast to an In₂O₃–CeO₂ system, where the addition of CeO₂ does not affect the conduction activation energy, where cerium oxide is added to SnO₂, the observed increase in the resistance of a SnO₂–CeO₂ composite is accompanied by a sufficient increase in activation energy. These data and the XPS spectra confirm the modification of the surface layers of conductive SnO₂ crystals as, a result of the penetration of cerium ions into these layers.     

Temperature dependence of the quenching of N<Subscript>2</Subscript> (C <Superscript>3</Superscript>Π<Subscript>u</Subscript>) by N<Subscript>2</Subscript> (X) and O<Subscript>2</Subscript> (X)

The temperature dependences of the quenching rate constants of the states N₂ (${\rm C} \ {^{3}{ \rm \Pi }_{u}}${\rm C} \ {^{3}{ \rm \Pi }_{u}} v^′=0,1) by N₂ (X) and of the state N₂ (${\rm C} \ {^{3}{ \rm \Pi }_{u}} \ v^{\prime}=0${\rm C} \ {^{3}{ \rm \Pi }_{u}} \ v^{\prime}=0) by O₂ (X) are studied. Time-resolved light emission from the gas was analyzed in the temperature range from 300 K to 210 K keeping the gas at constant density. In case of quenching by N₂ (X), the quenching rate constant for the vibrational level v^′= 0 increases by (13 ±3)% with gas cooling whereas the quenching rate constant for v^′= 1 decreases by (5.0 ±2.5)% in this temperature range. For quenching by O₂ (X), the quenching rate constant decreases by (3 ±2)% with gas cooling. The temperature variation of the N₂ (C ³Π_u v^′=0) emission intensity for pure nitrogen and dry air are calculated using the obtained quenching rate constants and is compared with the experimental data available in the literature.     

Synthesis and characterization of Li<Subscript>3</Subscript>V<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>·LiMn<Subscript>0.33</Subscript>Fe<Subscript>0.67</Subscript>PO<Subscript>4</Subscript>/C cathode materials

A new polyanionic cathode material, Li₃V₂(PO₄)₃·LiMn_0.33Fe_0.67PO₄/C for lithium-ion batteries, was synthesized using a sol-gel method and with N,N-dimethyl formamide as a dispersion agent. The analysis of electron transmission spectroscopy and X-ray diffraction revealed that the composite contained two phases. The material has high crystallinity with a grain size of 20–50 nm. The valence states of Mn, V, and Fe in the composite were analyzed by X-ray photoelectron spectroscopy. The electrochemical kinetics in Li₃V₂(PO₄)₃ is effectively enhanced by the incorporation of LiMnPO₄ and LiFePO₄, via structure modification and reduced Li diffusion length. The Li₃V₂(PO₄)₃·LiMn_0.33Fe_0.67PO₄/C materials displayed high rate capacity and steady cycle performance with discharge capacity remained 148 mAh g^?1 after 50 cycles at the rate of 0.2C. In particular, the composite exhibited excellent reversible capacities, with the values of 157, 134, 120, 102, and 94 mAh g^?1 at charge/discharge 0.2, 0.5, 1, 2, and 5C rates, respectively.     

O<Subscript>2</Subscript> photodesorption from AuO<Stack><Subscript>2</Subscript><Superscript>−</Superscript></Stack> and Au<Subscript>2</Subscript>O<Stack><Subscript>2</Subscript><Superscript>−</Superscript></Stack>

Using time-resolved photoelectron spectroscopy, the decay channels of AuO₂⁻ and Au₂O₂⁻ following photoexcitation with 3.1-eV photons have been studied. For AuO₂⁻, a state with a rather long lifetime of 30 ps has been identified. Its decay path could not be determined but photodesorption can be excluded. For Au₂O₂⁻, the spectra indicate O₂ desorption after 3.1-eV photoexcitation on a time scale of 1 ps. While comparing these results on Au _n O₂⁻ with analogous data on Ag _n O₂⁻ clusters, a discernible pattern emerges: for dissociatively bound O₂(AuO₂⁻, Ag₃O₂⁻), there are long-living excited states which do not decay by oxygen desorption, while for molecular chemisorption (Au₂O₂⁻, Ag₂O₂⁻, Ag₄O₂⁻, Ag₈O₂⁻), the 3.1-eV photoexcitation triggers fast O₂ desorption with a high quantum yield.     

Nanostructural inhomogeneity of EuBa<Subscript>2</Subscript>Cu<Subscript>3</Subscript>O<Subscript>6 + δ</Subscript> superconductors

Samples of high-temperature superconducting oxide EuBa₂Cu₃O_{6 + δ} (Eu-123) with total cationic composition Eu: Ba: Cu = 1: 2: 3 are investigated by means of local X-ray microanalysis and high-resolution transmission electron microscopy. The cationic nonstoichiometry of Eu-123 oxide is revealed. The particles of the studied samples are inhomogeneous in structure on the nanoscale, with two types of inhomogeneities: one with typical sizes of one to several nanometers, and one with typical sizes of 10 to 20 nm, respectively.     

Coercivity of homogenized ensembles of anisotropic γ-Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> nanoparticles

The influence of interaction between anisotropic γ-Fe₂O₃ nanoparticles on their coercive force H _c is studied. In samples where the degree of homogenization of anisotropic γ-Fe₂O₃ nanoparticles is high owing to mechanical, ultrasonic, and magnetic dispersion with subsequent filtering of resulting suspensions, H _c is almost independent of volume concentration η of the particles when η varies between 4 × 10⁻⁴ and 10⁻¹. In samples homogenized only mechanically, the H _c versus logη dependence is linear.     

Phase formation in the BaCO<Subscript>3</Subscript>–PbO–Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>–Nb<Subscript>2</Subscript>O<Subscript>5</Subscript> system

Features of the formation of lead-ferroniobate compounds in the xBaCO₃–(1 – x)PbO–Fe₂O₃–Nb₂O₅ system by solid-phase synthesis are investigated. For perovskite-type lead-ferroniobate solid solution, a single-phase concentration region is revealed at 1233 K. The crystalline structures of the synthesized compounds are refined using Rietveld analysis and the Pm3?m and R3m space groups. Ceramic samples of lead ferroniobate are studied by scanning electron microscopy.     

Study of the KNO<Subscript>3</Subscript>–Al<Subscript>2</Subscript>O<Subscript>3</Subscript> system by differential scanning calorimetry

The structural and the thermodynamic properties of potassium nitrate KNO₃ and its composites with nanosized aluminum oxide Al₂O₃ have been studied by differential scanning calorimetry. It has been found that an amorphous phase forms in composites (1–x)KNO_3–xAl₂O₃. The thermal effect corresponding to this phase has been observed at 316°C. It has been found that the phase transition heats of potassium nitrate decreased as the aluminum oxide fraction increased.     

μSR study of Eu<Subscript>0.8</Subscript>Ce<Subscript>0.2</Subscript>Mn<Subscript>2</Subscript>O<Subscript>5</Subscript> and EuMn<Subscript>2</Subscript>O<Subscript>5</Subscript> multiferroics

A comparative μSR study of ceramic samples of the EuMn₂O₅ and Eu_0.8Ce_0.2Mn₂O₅ multiferroics is performed in the temperature range from 15 to 300 K. It is found that the Ce doping of the EuMn₂O₅ sample slightly reduces the temperature of the magnetic phase transition from T _N = 45 K for the EuMn₂O₅ sample to T _N = 42.5 K for the Eu_0.8Ce_0.2Mn₂O₅ sample. Below the temperature T _N for both samples, there are two types of localization of a thermalized muon with different temperature dependences of the precession frequency of the magnetic moment of the muon in an internal magnetic field. The higher frequency in both samples refers to the initial antiferromagnetic matrix. The behavior of this frequency in Eu_0.8Ce_0.2Mn₂O₅ follows the Curie–Weiss law with the exponent β = 0.29 ± 0.02, which differs from the value β = 0.39 standard for 3D Heisenberg magnetics and is observed in EuMn₂O₅, because of the strong frustration of the doped sample. The temperature-independent low frequency is due to the presence of Mn³⁺–Mn⁴⁺ ferromagnetic pairs located along the b axis of the antiferromagnetic matrix and in the regions of phase separation, which contain such ion pairs and e _g electrons recharging them. In both samples, polarization losses are the same (about 20%) and are associated with the formation of Mn⁴⁺–Mn⁴⁺ + Mu complexes near Mn³⁺–Mn⁴⁺ ferromagnetic pairs. In the temperature interval from 25 to 45 K, the separation of the Eu_0.8Ce_0.2Mn₂O₅ structure into two fractions where the relaxation rates of polarization of muons differ by an order of magnitude is revealed. This effect is due to a change in the state of regions of phase separation (1D superlattices) at the indicated temperatures. Such effect in EuMn₂O₅ is significantly weaker.     

Synthesis of cubic Li<Subscript>7</Subscript>La<Subscript>3</Subscript>Zr<Subscript>2</Subscript>O<Subscript>12</Subscript> by modified sol–gel process

Polycrystalline cubic Li₇La₃Zr₂O₁₂ (LLZ) with garnet-related type structure has been synthesized at 700 °C by modified sol–gel processes using citric acid as organic complexing agent and butan-1-ol or propan-2-ol as surface active agent. Thermal analysis (thermogravimetric/differential thermal analysis) indicated that the gel must be annealed at around 700 °C to completely remove the organic solvent. X-ray powder diffraction, X-ray fluorescence, and scanning electron microscopic investigations revealed that Al may not be essential to form cubic-phase LLZ; however, the addition of Al₂O₃ led to enhanced sintering of LLZ.