ZrO2及其含量对Pd/ZrO2-Al2O3催化剂加氢脱硫性能的影响

采用浸渍法制备了一系列Pd/ZrO2-Al2O3催化剂,并考察了ZrO2-Al2O3复合载体及其ZrO2含量对Pd基催化剂噻吩加氢脱硫(HDS)性能的影响,运用XRD和NH3-TPD等手段对催化剂进行了表征。结果表明,ZrO2-Al2O3复合载体及其ZrO2含量对Pd基催化剂的HDS性能有较大的影响,其中ZrO2含量为12wt%时Pd/ZrO2-Al2O3催化剂的活性最好。ZrO2-Al2O3复合载体及其ZrO2含量对Pd基催化活性的影响是通过增加Pd的分散度、H吸附量和催化剂的酸量、以及降低活性组分与载体的相互作用来实现。     

负载型纳米ZrO2/Al2O3复合载体的制备和表征及其Ni/ZrO2/Al2O3催化性能的研究

以大孔Al2O3为基载体，采用沉积-沉淀法和溶胶-沉积法制备了负载型纳米ZrO2/Al2O3复合载体．用XRD、TEM和比表面与孔径测定等手段对载体进行了表征．结果表明，负载型纳米ZrO2/Al2O3复合载体具有较大的比表面积和适宜的孔径分布，纳米ZrO2在载体上呈单层均匀分布．以CH4-CO2重整制合成气为探针反应，考察了Ni/ZrO2/Al2O3催化剂的活性和选择性．     

ZrO2负载量对负载型纳米ZrO2/Al2O3复合载体的结构及性能影响

ZrO2在基载体Al2O3表面存在分散阈值(0.242 g/gAl2O3).在ZrO2/Al2O3复合载体中,ZrO2负载量不同其分布和粒度大小不同,当ZrO2负载量在0.242 g/gAl2O3-0.60 g/gAl2O3的范围内,ZrO2/Al2O3复合载体中纳米ZrO2的粒子的大小保持在4.2 nm,且单层分布在Al2O3的表面.当ZrO2负载量大于0.60 g/gAl2O3时,纳米粒子的粒径增大,并出现多层分布或堆积.XRD、DSC、HRTEM、XPS、H2-TPR结果表明,随着ZrO2负载量增大,复合载体中纳米ZrO2的分布由单层分布转化为多层或堆积分布,ZrO2负载量为0.60 g/gAl2O3时复合载体表面积最大(164.3 m2/g),ZrO2负载量的继续提高,复合载体的表面积明显下降.     

纳米γ-Al2O3/TiO2复合载体的制备及表征

采用了共溶胶-凝胶法和混凝胶法分别制备了不同Ti含量的纳米γ-Al2O3/TiO2样品.并应用XRD、BET和TEM技术分别对其进行了表征.结果表明,所制备的γ-Al2O3/TiO2样品平均粒径均小于15 nm,氧化铝以γ-Al2O3的形式存在,TiO2以锐钛矿形式存在.当TiO2含量小于20%时,复合载体仅有γ-Al2O3的晶体结构存在,TiO2呈高度分散状态;当TiO2的含量高于75%时,主要表现出锐钛矿晶体结构.BET结果说明,当TiO2含量低于50%时,复合载体的比表面积明显高于单独的Al2O3和TiO2,而且随着TiO2含量的增加,比表面有增大趋势.当TiO2含量大于50%时,载体的比表面积随二氧化钛含量的升高急剧下降.复合载体γ-Al2O3-TiO2表现为具有完好发达中孔的特征.负载Pd后催化剂的活性结果表明,95%TiO2含量的Pd/γ-Al2O3-TiO2(0.95)样品对乙醇和乙醛的催化氧化表现出优异的催化活性,其转化率明显高于单一的Al2O3或TiO2为载体的催化剂.     

Cu/ZrO2-Al2O3上表面氧物种脱附及其对催化性能的影响

采用ＸＲＤ,ＴＰＤ－ＭＳ和ＴＰＲ方法研究了ＺｒＯ２的改性对ＣｕＯ／γ－Ａｌ２Ｏ３催化剂上铜物种人散状态,表面氧物种的脱附和恢复性能,铜物种还原再氧行为的影响,并ＣＯ氧化反应为探针考察了催化剂的氧化活性,结果表明,ＺｒＯ２的存在的铜物种在γ－Ａｌ２Ｏ３载体上的分散容量降低,促进ＣｕＯ／γ－Ａｌ２Ｏ３催化剂上表面氧物种的脱附,同时有效地促进铜物种的还原,从而增加ＣＯ的氧化活性,实验还发现热处理条件对催     

共沉淀法制备ZrO2-Al2O3纳米复合氧化物的物相表征

用Al(NO3)3和ZrO(NO3)2混合溶液，加氨水共沉淀制备了一系列Al2O3含量由低到高的ZrO2-Al2O3复合氧化物，用XRD、XPS、BET等实验手段对其进行了表征.结果表明，随着一种组分含量由低到高，其主要存在形式按形成固溶体-表面单层分散-析出单独晶相的规律变化，而一种组分的加入均使另一种组分的XRD衍射峰明显宽化，晶粒变细；复合氧化物的比表面明显大于两种组分纯样品比表面的简单加和.实验表明体系中两种组分存在相互表面单层分散，即在一定的相对含量范围内，该体系的任一组分的微晶固溶体都既接受另一组分在其表面上的单层分散，同时也在另一组分的微晶固溶体表面上单层分散.相互单层分散和固溶体的生成都可能使高温焙烧时微晶的增大受到抑制，从而维持了样品的高比表面.     

助剂Cu对Ni/γ-Al2O3催化剂低温还原性能影响

制备了一系列铜质量分数不同的CuNi/γ-Al2O3催化剂,进行了TPR和XRD表征并测定了该系列催化剂对苯加氢制环己烷的催化活性。结果表明,助剂Cu的负载量对低温（160 ℃）还原后催化剂的催化活性影响很大,在铜镍原子摩尔比为1∶1时,催化剂具有较高的催化活性和稳定性;添加铜组分可促进镍在载体表面分散,使负载NiO的还原温度降低,催化活性提高。     

助剂调变对CoO／γ-Al2O3催化性能的影响

采用XRD、TPR和催化活性评价等技术,考察了负载型CoO催化剂的表面特征和其对CH4与CO2重整制合成气反应的催化性能.实验结果表明,采用浸渍法和焙烧温度为400℃时制备的11.0%CoO/γ-Al2O3催化剂,在反应温度为750 ℃和空速(GHSV)为2 500 h-1下,对CH4和CO2转化反应具有最佳的催化初活性,而大量的Co3O4晶粒的存在能导致催化剂因积炭而快速失去活性.CaO、MgO和La2O3助剂的添加能有效地改善其催化剂的抗积炭能力和还原性能,CoO/(CaO-γ-Al2O3)催化剂显示出最佳的催化反应稳定性,在750 ℃、GHSV=2 500 h-1、CH4/CO2原料比为1:1下,连续反应100 h催化剂活性较为稳定.CoO/(CaO-γ-Al2O3)和CoO/γ-Al2O3催化剂的表面特性本质上是不相同的.     

负载型纳米ZrO_2/Al_2O_3复合载体的制备和表征及其Ni/ZrO_2/Al_2O_3催化性能的研究

以大孔Al2O3为基载体,采用沉积-沉淀法和溶胶-沉积法制备了负载型纳米ZrO2/Al2O3复合载体.用XRD、TEM和比表面与孔径测定等手段对载体进行了表征.结果表明,负载型纳米ZrO2/Al2O3复合载体具有较大的比表面积和适宜的孔径分布,纳米ZrO2在载体上呈单层均匀分布.以CH4-CO2重整制合成气为探针反应,考察了Ni/ZrO2/Al2O3催化剂的活性和选择性.     

La2O3对Ni/γ-Al2O3甲烷化催化剂的助催化作用

我国将稀土作为助剂引入镍基甲烷化催化剂,大大提高了催化剂的活性和热稳定性,并已投入工业应用［1－3］．稀土对不同镍催化剂反应性能及其作用机理的研究已有一些报导［3－7］．谢有畅等观察到镍负载在经单层La2O3改性的γ－Al2O3表面,其晶粒要比没有La2O3时小得多．Rotgerink等认为添加La后反应速率的增加不只是由于几何效应,而是La对甲烷化本身有促进作用,单位镍表面的活性是随La含量不同而改变的,活性增加的同时表观活化能也增加［5］．作为助剂的La2O3在氢还原和反应过程中的变化及其作用的研究和讨论较少,目前一般认为添…     

催化精馏专用填料型固体酸SO42-/ZrO2-Al2O3-Al的研究

为了研制催化精馏专用催化剂,采用铝阳极氧化法制备了Al2O3-Al一体型载体,并将活性固体超强酸SO42-/ZrO2引入到Al2O3-Al上,得到一种新型催化精馏专用填料式固体酸SO42-/ZrO2-Al2O3-Al催化剂.利用XRD、 SEM、 BET、 XPS、 NH3-TPD等手段对其进行了表征.结果表明,所制得的阳极氧化铝膜厚为56 μm, SO42-/ZrO2-Al2O3-Al固体酸具有比表面积大、酸强度适中的特点.XRD结果表明, ZrO2在Al2O3-Al上处于高度分散状态.将该固体酸用于乙酸/乙醇酯化反应中,显示出较高的催化活性,且稳定性较好.     

Autothermal reforming of methane over Ni catalysts supported over ZrO2-CeO2-Al2O3

Ni catalysts supported on Al2O3, ZrO2-Al2O3, CeO2-Al2O3 and ZrO2-CeO2-Al2O3 were prepared by coprecipitation method, and their catalytic performances for autothermal reforming of methane to hydrogen were investigated. The Ni-supported catalysts were characterized by XRD, TPR and XPS. The relationship between the structures and catalytic activities of the catalysts was discussed. The results showed that the catalytic activity and stability of the Ni/ZrO2-CeO2-Al2O3 catalyst was better than those of other catalysts with the highest CH4 conversion, H2/CO and H2/COx ratio at 750 ℃. The catalyst showed a little deactivation along the reaction time during its 72 h on stream with the mean deactivation rate of 0.08%/h. The catalytic performance of the Ni/ZrO2-CeO2-Al2O3 catalyst was also affected by reaction temperature, no2 ： nCH4 molar ratio and nH2O ： nCH4 molar ratio. TPR, XRD and XPS measurements indicated that the formation of ZrO2-CeO2 solid solution could improve the dispersion of NiO, and inhibit the formation of NiAl2O3, and thus significantly promoted the catalytic activity of the Ni/ZrO2-CeO2-Al2O3 catalyst.     

CoMo/ZrO2-Al2O3催化剂的制备及其加氢脱氧性能

以ZrOCl₂·6H₂O和Al₂(SO₄)₃为原料,采用超声波共沉淀法制得一系列不同ZrO₂质量分数的ZrO₂- Al₂O₃复合氧化物载体;并以该复合氧化物为载体,采用等体积浸渍法制得Co和Mo质量分数分别为6.0%和16.0%的CoMo/ZrO₂-Al₂O₃催化剂。BET、XRD、H₂-TPR和NH₃-TPD等表征结果表明,ZrO₂-Al₂O₃复合氧化物载体具有较高的比表面积与较大的孔容、孔径,随着复合载体中ZrO₂质量分数的增加,复合载体比表面积逐渐减小。ZrO₂-Al₂O₃复合载体能高度分散活性组分,钴钼负载量接近其在载体上的单层分散阈值。相比于CoMo/Al₂O₃,CoMo/ZrO₂-Al₂O₃催化剂具有较高的还原性能和较多的表面酸性活性中心,由此导致其在苯酚加氢脱氧(HDO)反应中,具有较高的加氢脱氧活性和苯选择性。
     

制备条件及添加稀土对SO42- /ZrO2 -Al2O3固体超强酸酸性影响的研究

用共沉淀法制备了SO42-/ZrO2-Al2O3固体超强酸,并采用低温陈化和添加稀土La对其制备方法进行改进.通过样品催化正丁烷异构化反应考察了该固体超强酸中nZr和nAl的最佳配比为1∶ 2.该法制备的样品的IR显示,在1393 cm-1处的吸收峰强度较常温陈化样品大大增加.XRD分析表明,低温陈化和加入稀土添加剂的样品在650℃焙烧温度下,出现了亚稳态的ZrO2 四方晶相的晶体是表面酸性和催化活性增加的微观原因.样品催化合成八乙酸蔗糖酯反应结果同样证明,在相同的时间内,低温陈化和添加稀土添加剂的样品具有较好的催化活性.     

碱土金属对ZrO2-Al2O3及其负载Pd-Rh密偶催化剂的影响

采用胶溶法制备了一系列碱土金属改性的ZrO₂-Al₂O₃, 并以其为载体采用等体积浸渍法制备了Pd-Rh密偶催化剂. 采用低温N₂吸附-脱附、X射线衍射(XRD)、氨气程序升温脱附(NH3-TPD)对载体样品进行了表征. 结果表明, 碱土金属的添加增大了ZrO₂-Al₂O₃的比表面积, Sr-Zr-Al样品经1000 °C焙烧5 h后具有最大的比表面积, 为164 m²·g^-1. 对催化剂进行了H₂程序升温还原(H₂-TPR)、X射线光电子能谱(XPS)和活性表征, 考察了催化剂对C₃H₈的转化活性. 测试结果表明, 添加碱土金属能有效提高催化剂上丙烷的转化活性.     

ZrO2在Rh/γ-Al2O3催化剂中对NO催化还原反应的作用

测定了含ZrO2的Rh/γ-Al2O3催化剂上NO+C2H4和NO+C2H4+O2的反应活性,并应用TPR、XRD、BET比表面等表征了ZrO2的加入方式和晶型对Rh/γ-Al2O3催化剂活性和结构的影响。结果表明,ZrO2的加入一定程度地抑制了Rh3+与γ-Al2O3之间的相互作用和γ-Al2O3的相变,提高了催化剂的热稳定性,明显提高了850℃老化样品的NO+C2H4反应活性。对于NO+C2H4+O2反应,含ZrO2样品的选择还原活性却较低,表明反应机理不同,而且ZrO2对C2H4的深度氧化有促进作用,但老化后活性下降幅度比不含ZrO2的样品小。     

Ni2P/TiO2的制备及其对苯加氢反应的催化性能

采用程序升温还原方法制备了TiO2负载的晶态Ni2P催化剂。用X射线衍射（XRD）及低温N2吸附（BET）等技术对样品的物相、比表面积等性质进行了表征。以苯气相加氢为模型反应考察了Ni2P/TiO2催化剂加氢性能,并对Ni2P负载量、前驱体中P的质量分数对催化剂的物相及性能的影响进行了研究。实验结果表明, TiO2负载的晶态磷化镍催化剂上,Ni2P是主要物相。Ni2P/TiO2催化剂对苯加氢反应具有较高的活性、选择性以及良好的稳定性能。Ni2P/TiO2制备对催化剂的性能有影响。Ni2P负载量增加,催化剂的活性先升高后降低,Ni2P负载量为12%时催化剂活性较高。催化剂前驱体中P的质量分数越高,制备出的催化剂对苯加氢反应的稳定性越好,但随前驱体中P的质量分数增加,催化反应的活性先升高,后降低。与Ni2P/SiO2比较,Ni2P/TiO2催化剂具有较高的活性和稳定性。     

Application of ZrO2-Al2O3 Aerogels to Catalysts

ZrO2-Al2O3 aerogels were prepared by hydrolysis of metal alkoxides in alcoholic solutions and supercritical drying in order to obtain an improved de-NOx catalyst with high activity in a wide temperature range. The aerogels have about 20–50% higher activity than the xerogels in the range 300–600°C. The higher activity of aerogels may be attributed to the higher effective gas diffusivity in them, estimated to be about 20–60 times higher than that of the xerogels, because of their high porosity and large pore size. The catalytic activity of aerogels containing 4–10 mol% ZrO2 is more than 20% higher than that of Al2O3 aerogels at temperatures <450°C.