Room temperature transparent conducting oxides based on zinc oxide thin films

Doped zinc oxide thin films are grown on glass substrate at room temperature under oxygen atmosphere, using pulsed laser deposition (PLD). O₂ pressure below 1 Pa leads to conductive films. A careful characterization of the film stoichiometry and microstructure using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) concludes on a decrease in crystallinity with Al and Ga additions (≤3%). The progressive loss of the (0 0 2) orientation is associated with a variation of the c parameter value as a function of the film thickness and substrate nature. ZnO:Al and ZnO:Ga thin films show a high optical transmittance (>80%) with an increase in band gap from 3.27 eV (pure ZnO) to 3.88 eV and 3.61 eV for Al and Ga doping, respectively. Optical carrier concentration, optical mobility and optical resistivity are deduced from simulation of the optical data.     

A comparative study on structural and optical properties of ZnO and Al-doped ZnO thin films obtained by ultrasonic spray method using different solvents

Transparent conducting ZnO and Al doped ZnO thin films were deposited on glass substrate by ultrasonic spray method. The thin films with concentration of 0.1 M were deposited at 350 °C with 2 min of deposition time. The effects of ethanol and methanol solution before and after doping on the structural, optical and electrical properties were examined. The DRX analyses indicated that ZnO films have nanocrystalline nature and hexagonal wurtzite structure with (1 0 0) and (0 0 2) preferential orientation corresponding to ZnO films resulting from methanol and ethanol solution, respectively. The crystallinity of the thin films improved with methanol solution after doping to (0 0 2) oriented. All films exhibit an average optical transparency about 90%, in the visible range. The band gaps values of ZnO thin films are increased after doping from 3.10 to 3.26 eV and 3.27 to 3.30 eV upon Al doping obtained by ethanol and methanol solution, respectively. The electrical conductivity increase from 7.5 to 15.2 (Ω cm)⁻¹ of undoped to Al doped ZnO thin films prepared by using ethanol solution. However, for the methanol solution; the electrical conductivity of the film is stabilized after doping.     

Property enhancement of transparent conducting zinc oxide thin films—Effect of simultaneous (Sn+F) doping

Undoped and simultaneously (Sn+F) doped ZnO thin films were fabricated using a simplified spray pyrolysis technique and the effects of Sn doping level on their electrical, structural, optical and surface morphological properties were studied. The XRD patterns confirmed the hexagonal wurtzite structure of ZnO. The minimum electrical resistivity of 0.45×10⁻² Ω cm was obtained for ZnO films having Sn+F doping levels of 8+20 at%. All the films exhibited average optical transmittance of 85% in the visible region, suitable for transparent electrode applications. The overall quality of the fabricated films was confirmed from photoluminescence (PL) studies. The PL and surface morphological studies along with the elemental analysis showed the increase of Sn diffusion into the ZnO lattice which was consistent with the concentration of Sn in the starting solution. The results of the analysis of physical properties of simultaneously doped ZnO films proved that these films might be considered as promising candidates for solar cells and other opto-electronic applications.     

Influence of deposition temperature on the crystallinity of Al-doped ZnO thin films at glass substrates prepared by RF magnetron sputtering method

Al-doped ZnO (AZO) transparent conducting films were successfully prepared on glass substrates by RF magnetron sputtering method under different substrate temperatures. The microstructural, electrical and optical properties of AZO films were investigated in a wide temperature range from room temperature up to 350 °C by X-ray Diffraction (XRD), Field-Emission Scanning Electron Microscopy (FESEM), High-Resolution Transmission Electron Microscopy (HRTEM), Hall measurement, and UV–visible meter. The nature of AZO films is polycrystalline thin films with hexagonal wurtzite structure and a preferred orientation along c-axis. The crystallinity and surface morphologies of the films are strongly dependent on the growth temperature, which in turn exerts a great effect on microstructural, electrical and optical properties of the AZO films. The atomic arrangement of AZO film having an wurtzite structure was indeed identified by the HRTEM as well as the Selected Area Electron Diffraction (SAED). The defect density of AZO film was investigated by HRTEM. The film deposited at 100 °C exhibited the relatively well crystallinity and the lowest resistivity of 3.6 × 10⁻⁴ Ω cm. The average transmission of AZO films in the visible range is all over 85%. More importantly, the low-resistance and high-transmittance AZO film was also prepared at a low temperature of 100 °C.     

The crystalline structure,conductivity and optical properties of Co-doped ZnO thin films

Transparent conductive Co-doped ZnO thin films were deposited by ultrasonic spray technique. Conditions of preparation have been optimized to get good quality. A set of cobalt (Co)-doped ZnO (between 0 and 3 wt%) thin films were grown on glass substrate at 350 °C. The thin films were annealed at 500 °C for improvement of the physical properties. Nanocrystalline films with hexagonal wurtzite structure and a strong (0 0 2) preferred orientation were obtained. The maximum value of grain size G = 63.99 nm is attained with undoped ZnO film. The optical transmissions spectra showed that both the undoped and doped ZnO films have transparency within the visible wavelength region. The band gap energy decreased after doping from 3.367 to 3.319 eV when Co concentration increased from 0 to 2 wt% with slight increase of electrical conductivity of the films from 7.71 to 8.33 (Ω cm)⁻¹. The best estimated structure, optical and electrical results are achieved in Co-doped ZnO film with 2 wt%.     

Influence of target substrate distance on the properties of transparent conductive Si doped ZnO thin films

Si doped zinc oxide (SZO, Si3%) thin films are grown at room temperature on glass substrates under argon atmosphere, using direct current magnetron sputtering. The influence of the target substrate distances on structure, morphology, optical and electrical properties of SZO thin films is investigated. Experimental results show that the target substrate distances have a significance impact on the growth rate, crystal quality and electrical properties of the films, and have little impact on the optical properties of the films. SZO thin film samples grown on glasses are polycrystalline with a hexagonal wurtzite structure and have a preferred orientation along the c-axis perpendicular to the substrate. When the target substrate distance decreases from 76 to 60 mm, the degree of crystallization of the films increased, the grain size increases, and the resistivity of films decreases. However, when the distance continuously decreases from 60 to 44 mm, the degree of crystallization of the films decreased, the grain size decreases, and the resistivity of the films increases. SZO(3%) thin films deposited at a target substrate distance of 60 mm show the lowest resistivity of 5.53 × 10⁻⁴ Ω cm, a high average transmission of 94.47% in the visible range, and maximum band gap of 3.45 eV under 5 Pa of argon at sputtering power of 75 W for sputtering time of 20 min.     

Effect of dopants on the structural,optical and electrical properties of sol–gel derived ZnO semiconductor thin films

Undoped, Ga-, In-, Zr-, and Sn-doped ZnO transparent semiconductor thin films were deposited on alkali-free glasses by sol–gel method. 2-methoxyethanol (2-ME) and diethanolamine (DEA) were chosen as a solvent and a stabilizer, respectively. The doping concentration was maintained at 2 at.% in the impurity doping precursor solutions. The effects of different dopants on the structural, optical, and electrical properties of ZnO thin films were investigated. XRD results show that all annealed ZnO-based thin films had a hexagonal (wurtzite) structure. ZnO thin films doped with impurity elements obviously improved the surface flatness and enhanced the optical transmittance. All impurity doped ZnO thin films showed high transparency in the visible range (>91%). The Ga- and In- doped ZnO thin films exhibited higher Hall mobility and lower resistivity than did the undoped ZnO thin film.     

Preparation and characterization of n-type conductive (Al, Co) co-doped ZnO thin films deposited by sputtering from aerogel nanopowders

Highly transparent, n-type conducting ZnO thin films were obtained by low temperature magnetron sputtering of (Co, Al) co-doped ZnO nanocrystalline aerogels. The nanoparticles of ∼30 nm size were synthesized by a sol-gel method using supercritical drying in ethyl alcohol. The structural, optical and electrical properties of the films were investigated. The ZnO films were polycrystalline textured, preferentially oriented with the (0 0 2) crystallographic direction normal to the film plane. The films show within the visible wavelength region an optical transmittance of more than 90% and a low electrical resistivity of 3.5 × 10⁻⁴ Ω cm at room temperature.     

Influence of Al concentration on electrical, structural and optical properties of Al-As codoped p-ZnO thin films

We report the influence of Al concentration on electrical, structural, optical and morphological properties of Al-As codoped p-ZnO thin films using RF magnetron sputtering. Al-As codoped p-ZnO films with different Al concentrations were fabricated using As back diffusion from the GaAs substrate and sputtering Al₂O₃ mixed ZnO targets (1, 2 and 4 at%). The grown films were investigated by Hall effect measurement, X-ray diffraction (XRD), electron probe microanalysis (EPMA), energy dispersive spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS), photoluminescence (PL) and atomic force microscopy (AFM) to study the electrical, structural, optical and morphological properties of the films. From the XRD, it was observed that both full-width at half-maximum (FWHM) and c-axis lattice constant have similar trends with respect to Al concentration. Hall measurements showed that the hole concentration increases as the Al concentration increases from 10¹⁵ to 10²⁰ cm⁻³. The increase in hole concentration upon codoping was supported by the red shift in the near-band-edge (NBE) emission observed from room temperature PL spectra. The proposed p-type mechanism due to As_Zn-2V_Zn complex was confirmed by low temperature PL and XPS analysis. The low FWHM, resistivity and peak-to-valley roughness observed by XRD, Hall measurement and AFM, respectively, suggest that 1 at% Al-doped ZnO:As film is the best codoped film.     

On the paramagnetic behavior of heavily doped Zn1−xMnxO films fabricated by Pechini’s method

Heavily doped Zn_1−xMn_xO (x = 0.3) films were prepared by polymeric precursor method onto glass substrates and their structural, morphological, optical and magnetic properties carefully studied. Undoped ZnO films were also prepared for the purpose of comparison. The polymeric precursor method consists in preparing a coating solution from the Pechini process followed by a three-step thermal treatment of the as deposited films at temperatures up to 550 °C for 30 min. X-ray diffraction (XRD) analysis reveals the typical hexagonal wurtzite structure of the undoped ZnO film. The addition of Mn ions leads to a dramatic reduction of the crystalline quality of film although no evidence of affectation by secondary phases is found. The affectation of the ZnO structure may be due to the formation of Mn clusters and generation of defects such as vacancies and interstitials. Here, the solubility limit of the Mn ions in ZnO should play an important role and it is discussed in the framework of ionic radius and valence states. The scanning electron microscopy (SEM) analysis shows that the surface of the doped sample was affected by the presence of cracks due, probably, to the expansion of the lattice constant of Zn_0.7Mn_0.3O caused by the Mn incorporation in the ZnO lattice. The existence of cluster-type structures on the surface is corroborated by atomic force microscopy (AFM). The EDX analysis, carried out on some areas in the film, yielded Mn/Zn ratios of about 0.3, which points out to an effective Mn incorporation in the film. On the other hand, the absorption edge of the doped films is red shifted to 2.9 eV (3.24 eV for undoped ZnO film) and the absorption edge is less sharp due, probably, to amorphous states appearing in the band gap. No evidence of dilute magnetic semiconductor mean-field ferromagnetic behavior is observed. The temperature dependence of the magnetization follows a Curie law suggesting pure paramagnetic behavior. The very small s-shape behavior of M versus H (without hysteresis) observed at room temperature on selected areas would stem from Mn clusters which are easily formed in transition metal doped ZnO.     

Influence of annealing temperature on structural and optical properties of ZnO: In thin films prepared by ultrasonic spray technique

Transparent conducting indium doped zinc oxide was deposited on glass substrate by ultrasonic spray method. The In doped ZnO samples with indium concentration of 3 wt.% were deposited at 300, 350 and 400 °C with 2 min of deposition time. The effects of substrate temperature and annealing temperature on the structural, electrical and optical properties were examined. The DRX analyses indicated that In doped ZnO films have polycrystalline nature and hexagonal wurtzite structure with (0 0 2) preferential orientation and the maximum average crystallite size of ZnO: In before and annealed at 500 °C were 45.78 and 55.47 nm at a substrate temperature of 350 °C. The crystallinity of the thin films increased by increasing the substrate temperature up 350 °C, the crystallinity improved after annealing temperature at 500 °C. The film annealed at 500 °C and deposited at 350 °C show lower absorption within the visible wavelength region. The band gap energy increased from E_g = 3.25 to 3.36 eV for without annealing and annealed films at 500 °C, respectively, indicating that the increase in the transition tail width. This is due to the increase in the electrical conductivity of the films after annealing temperature.     

Preparation and characterization of Mg-doped ZnO thin films by sol-gel method

Undoped and Mg-doped ZnO thin films were deposited on Si(1 0 0) and quartz substrates by the sol-gel method. The thin films were annealed at 873 K for 60 min. Microstructure, surface topography and optical properties of the thin films have been measured by X-ray diffraction (XRD), atomic force microscope (AFM), UV-vis spectrophotometer, and fluorophotometer (FL), respectively. The XRD results show that the polycrystalline with hexagonal wurtzite structure are observed for the ZnO thin film with Mg:Zn = 0.0, 0.02, and 0.04, while a secondary phase of MgO is evolved for the thin film with Mg:Zn = 0.08. The ZnO:Mg-2% thin film exhibits high c-axis preferred orientation. AFM studies reveal that rms roughness of the thin films changes from 7.89 nm to 16.9 nm with increasing Mg concentrations. PL spectra show that the UV-violet emission band around 386-402 nm and the blue emission peak about 460 nm are observed. The optical band gap calculated from absorption spectra and the resistivity of the ZnO thin films increase with increasing Mg concentration. In addition, the effects of Mg concentrations on microstructure, surface topography, PL spectra and electrical properties are discussed.     

Deposition and characterization of transparent and conductive sprayed ZnO:B thin films

Highly transparent and conductive Boron doped zinc oxide (ZnO:B) thin films were deposited using chemical spray pyrolysis (CSP) technique on glass substrate. The effect of variation of boron doping concentration in reducing solution on film properties was investigated. Low angle X-ray analysis showed that the films were polycrystalline fitting well with a hexagonal wurtzite structure and have preferred orientation in [002] direction. The films with resistivity 2.54×10⁻³ Ω-cm and optical transmittance >90% were obtained at optimized boron doping concentration. The optical band gap of ZnO:B films was found ∼3.27 eV from the optical transmittance spectra for the as-deposited films. Due to their excellent optical and electrical properties, ZnO:B films are promising contender for their potential use as transparent window layer and electrodes in solar cells.     

Effect of doping concentration on the structural and optical properties of pure and tin doped zinc oxide thin films by nebulizer spray pyrolysis (NSP) technique

Pure and tin doped zinc oxide (Sn:ZnO) thin films were prepared for the first time by NSP technique using aqueous solutions of zinc acetate dehydrate, tin (IV) chloride fendahydrate and methanol. X-ray diffraction patterns confirm that the films are polycrystalline in nature exhibiting hexagonal wurtzite type, with (0 0 2) as preferred orientation. The structural parameters such as lattice constant (‘a’ and ‘c’), crystallite size, dislocation density, micro strain, stress and texture coefficient were calculated from X-ray diffraction studies. Surface morphology was found to be modified with increasing Sn doping concentration. The ZnO films have high transmittance 85% in the visible region, and the transmittance is found to be decreased with the increase of Sn doping concentration. The corresponding optical band gap decreases from 3.25 to 3.08 eV. Room temperature photoluminescence reveals the sharp emission of strong UV peak at 400 nm (3.10 eV) and a strong sharp green luminescence at 528 nm (2.34 eV) in the Sn doped ZnO films. The electrical resistivity is found to be 10⁶ Ω-cm at higher temperature and 10⁵ Ω-cm at lower temperature.     

Structural, electrical and optical properties of Gd doped and undoped ZnO:Al (ZAO) thin films prepared by RF magnetron sputtering

The influence of the gadolinium doping on the structural features and opto-electrical properties of ZnO:Al (ZAO) films deposited by radio frequency (RF) magnetron sputtering method onto glass substrates was investigated. X-ray analysis showed that the films were polycrystalline fitting well with a hexagonal wurtzite structure and have preferred orientation in [0 0 2] direction. The Gd doped ZAO film with a thickness of 140 nm showed a high visible region transmittance of 90%. The optical band gap was found to be 3.38 eV for pure ZnO film and 3.58 eV for ZAO films while a drop in optical band gap of ZAO film was observed by Gd doping. The lowest resistivities of 8.4 × 10⁻³ and 10.6 × 10⁻³ Ω cm were observed for Gd doped and undoped ZAO films, respectively, which were deposited at room temperature and annealed at 150 °C.     

Influence of post-deposition annealing on the structural,optical and electrical properties of Li and Mg co-doped ZnO thin films deposited by sol–gel technique

Lithium (Li) and magnesium (Mg) co-doped zinc oxide (ZnO) thin films were deposited by sol–gel method using spin coating technique. The films were deposited on glass substrates and annealed at different temperatures. The effects of annealing temperature on the structural, optical and electrical properties of the deposited films were investigated using X-ray diffraction (XRD), Ultraviolet–Visible absorption spectra (UV–VIS), photoluminescence spectra (PL), X-ray photo electron spectroscopy (XPS) and Hall measurements. XRD patterns indicated that the deposited films had a polycrystalline hexagonal wurtzite structure with preferred (0 0 0 2) orientation. All films were found to exhibit a good transparency in the visible range. Analysis of the absorption edge revealed that the optical band gap energies of the films annealed at different temperatures varies between 3.49 eV and 3.69 eV. Room temperature PL spectra of the deposited films annealed at various temperatures consist of a near band edge emission and visible emission due to the electronic defects, which are related to deep level emissions, such as oxide antisite (O_Zn), interstitial zinc (Zn_i), interstitial oxygen (O_i) and zinc vacancy (V_Zn) which are generated during annealing process. The influence of annealing temperature on the chemical state of the dopants in the film was analysed by XPS spectra. Ion beam analysis (Rutherford back scattering) experiments were performed to evaluate the content of Li and Mg in the films. Hall measurements confirmed the p-type nature of the deposited films.     

Properties of Dy-doped ZnO nanocrystalline thin films prepared by pulsed laser deposition

Highly transparent conductive Dy₂O₃ doped zinc oxide (ZnO)_1-x(Dy₂O₃)_x nanocrystalline thin films with x from 0.5% to 5% have been deposited on glass substrate by pulsed laser deposition technique. The structural, electrical and optical properties of Dy₂O₃ doped thin films were investigated as a function of the x value. The experimental results show that the Dy concentration in Dy-doped ZnO thin films has a strong influence on the material properties especially electrical properties. The resistivity decreased to a minimum value of 5.02 × 10⁻⁴ Ω cm with x increasing from 0.5% to 1.0%, then significantly increased with the further increasing of x value. On the contrary, the optical direct band gap of the (ZnO)_1-x(Dy₂O₃)_x films first increased, then decreased with x increasing. The average transmission of Dy₂O₃ doped zinc oxide films in the visible range is above 90%.     

The influence of different doping elements on microstructure, piezoelectric coefficient and resistivity of sputtered ZnO film

ZnO film is attractive for high frequency surface acoustic wave device application when it is coupled with diamond. In order to get good performance and reduce insertion loss of the device, it demands the ZnO film possessing high electrical resistivity and piezoelectric coefficient d₃₃. Doping ZnO film with some elements may be a desirable method. In this paper, the ZnO films undoped and doped with Cu, Ni, Co and Fe, respectively (doping concentration is 2.0 at.%) are prepared by magnetron sputtering. The effect of different dopants on the microstructure, piezoelectric coefficient d₃₃, and electrical resistivity of the film are investigated. The results indicate that Cu dopant can enhance the c-axis orientation and piezoelectric coefficient d₃₃, the Cu and Ni dopant can increase electrical resistivity of the ZnO film up to 10⁹ Ω cm. It is promising to fabricate the ZnO films doped with Cu for SAW device applications.     

Electrical and optical properties of Ga doped zinc oxide thin films deposited at room temperature by continuous composition spread

Ga doped ZnO (GZO) thin films were deposited on glass substrates at room temperature by continuous composition spread (CCS) method. CCS is thin films growth method of various Ga_xZn_1−xO(GZO) thin film compositions on a substrate, and evaluating critical properties as a function position, which is directly related to material composition. Various compositions of Ga doped ZnO deposited at room temperature were explored to find excellent electrical and optical properties. Optimized GZO thin films with a low resistivity of 1.46 × 10⁻³ Ω cm and an average transmittance above 90% in the 550 nm wavelength region were able to be formed at an Ar pressure of 2.66 Pa and a room temperature. Also, optimized composition of the GZO thin film which had the lowest resistivity and high transmittance was found at 0.8 wt.% Ga₂O₃ doped in ZnO.     

Physical properties of ZnO thin films deposited by spray pyrolysis technique

Thin films of ZnO have been prepared on glass substrates at different thicknesses by spray pyrolysis technique using 0.2 M aqueous solution of zinc acetate. X-ray diffraction reveals that the films are polycrystalline in nature having hexagonal wurtzite type crystal structure. The resistivity at room temperature is of the order 10⁻² Ω cm and decreased as the temperature increased. Films are highly transparent in the visible region. The dependence of the refractive index, n, and extinction coefficient, k, on the wavelength for a sprayed film is also reported. Optical bandgap, E_g, has been reported for the films. A shift from E_g = 3.21 eV to 3.31 eV has been observed for deposited films.