Microstructure and properties of Ni-Co/nano-Al2O3 composite coatings by pulse reversal current electrodeposition

Ni-Co/nano-Al₂O₃ (Ni-Co/Al₂O₃) composite coatings were prepared under pulse reversal current (PRC) and direct current (dc) methods respectively. The microstructure of coatings was characterized by means of XRD, SEM and TEM. Both the Ni-Co alloy and composite coatings exhibit single phase of Ni matrix with face-centered cubic (fcc) crystal structure, and the crystal orientation of the Ni-Co/Al₂O₃ composite coating was transformed from crystal face (2 0 0) to (1 1 1) compared with alloy coatings. The hardness, anti-wear property and macro-residual stress were also investigated. The results showed that the microstructure and performance of the coatings were greatly affected by Al₂O₃ content and the electrodeposition methods. With the increasing of Al₂O₃ content, the hardness and wear resistance of the composite coatings enhanced. The PRC composite coatings exhibited compact surface, high hardness, better wear resistance and lower macro-residual stress compared with that of the dc composite coatings.     

Mechanical properties and wear and corrosion resistance of electrodeposited Ni-Co/SiC nanocomposite coating

Ni-Co/SiC nanocomposite coatings with various contents of SiC nano-particulates were prepared by electrodeposition in a Ni-Co plating bath containing SiC nano-particulates to be co-deposited. The influences of the nanoparticulates concentration, current density, stirring rate and temperature of the plating bath on the composition of the coatings were investigated. The shape and size of the SiC nano-particulates were observed and determined using a transmission electron microscope. The polarization behavior of the composite plating bath was examined on a PAR-273A potentiostat/galvanostat device. The wear behavior of the Ni-Co/SiC nanocomposite coatings was evaluated on a ball-on-disk UMT-2MT test rig. The worn surface morphologies of the Ni-Co/SiC nanocomposite coatings were observed using a scanning electron microscope. The corrosion behavior of the nanocomposite coatings was evaluated by charting the Tafel curves of the solution of 0.5 mol L⁻¹ NaCl at room temperature. It was found that the cathodic polarization potential of the composite electrolyte increased with increasing SiC concentration in the plating bath. The microhardness and wear and corrosion resistance of the nanocomposite coatings also increased with increasing content of the nano-SiC in the plating bath, and the morphologies of the nanocomposite coatings varied with varying SiC concentration in the plating bath as well. Moreover, the co-deposited SiC nano-particulates were uniformly distributed in the Ni-Co matrix and contributed to greatly increase the microhardness and wear resistance of the Ni-Co alloy coating.     

Development of electroless Ni-Zn-P/nano-TiO2 composite coatings and their properties

Ni-Zn-P-TiO₂ composite coatings were successfully obtained on low carbon steel by electroless plating technique. Deposits were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy-dispersive analysis (EDS) studies. The hardness and microstructure of as plated and heat treated Ni-Zn-P and Ni-Zn-P-TiO₂ composite coatings were analyzed. The change in microstructure and higher hardness was noticed for heat treated composite. The corrosion resistance behavior of as plated and heat treated Ni-Zn-P and Ni-Zn-P-TiO₂ coatings was investigated by anodic polarization, Tafel plots and electrochemical impedance spectroscopic (EIS) studies in 3.5 wt% NaCl solution. The composite coating exhibited enhanced corrosion resistance property over Ni-Zn-P coating.     

Fortification of Ni–Y<Subscript>2</Subscript>O<Subscript>3</Subscript> nanocomposite coatings prepared by pulse and direct current methods

Ni–Y₂O₃ nanocomposite coatings were prepared under direct current (DC) and pulse current (PC) using acetate bath. The microstructure and corrosion resistance of the coatings were characterized by means of XRD, SEM, AFM, and EIS. The results showed that the microstructure and performances of the coatings were greatly affected by Y₂O₃ content on the deposits prepared by DC and PC methods. The microhardness and corrosion resistance were enhanced in the optimum percentage of Y₂O₃ composite coatings. The PC composite coatings were exhibited compact surface, higher microhardness, and good corrosion resistance compared with that of the DC composite coatings.     

Effect of NaAlO2 concentrations on microstructure and corrosion resistance of Al2O3/ZrO2 coatings formed on zirconium by micro-arc oxidation

In this study, Al₂O₃/ZrO₂ composite coatings were prepared on Zr substrates by micro-arc oxidation (MAO) in the NaAlO₂-containing electrolytes, and the effect of NaAlO₂ concentration on the microstructure, bond strength, microhardness and corrosion resistance of coatings was systematically investigated. The study reveals that the adequate NaAlO₂ in the electrolyte (>0.2 M) is essential to the formation of needle-like α-Al₂O₃ in the coatings, and the amount of α-Al₂O₃ rises with the increase of the NaAlO₂ concentration. m-ZrO₂ and t-ZrO₂ are present in all of the coatings, but their relative amount largely depends on the amount of Al₂O₃. It is also found that as the NaAlO₂ concentration increases from 0.2 to 0.3 M, the coating becomes denser and thicker, and its bond strength, maximum microhardness and corrosion resistance increases as well. The coating formed at 0.3 M NaAlO₂ demonstrates the highest bond strength of 52 MPa, the maximum microhardness of 1600 Hv_0.2N and the superior corrosion resistance. However, the overhigh concentration of NaAlO₂ (0.35 M) is found harmful to the coating's microstructure and properties.     

Electrodeposited nickel-cobalt composite coating containing MoS2

Ni-Co/MoS₂ composite coatings were prepared by electrodeposition in a Ni-Co plating bath containing nano-sized MoS₂ particles to be co-deposited. The polarization behavior of the composite plating bath was examined on a PAR-273A potentiostat/galvanostat device. The friction and wear behaviors of the Ni-Co/MoS₂ composite coatings were evaluated with UMT-2MT test rig in a ball-on-disk contact mode. The morphologies of the original and worn surfaces of the composite coatings were observed on scanning electron microscope (SEM). It was found that the introduction of MoS₂ nano-particulates in the electrolyte caused the shift towards larger negatives of the reduction potential of the Ni-Co alloy coating, and the co-deposited MoS₂ showed no significant effect on the electrodeposition process of the Ni-Co alloy coating. However, the co-deposited MoS₂ led to changes in the surface morphology and structure of the composite coating as well. Namely, the peak width of the Ni-Co solid solution for the composite coating is broader as compared to that of the Ni-Co alloy coating. The co-deposited MoS₂ particulates were uniformly distributed in the Ni-Co matrix and contributed to increase tribological properties of the Ni-Co alloy coating.     

Composite Ni-Co-fly ash coatings on 5083 aluminium alloy

Ni-Co-fly ash coatings were deposited on zincate treated 5083 wrought aluminium alloy substrates with the aid of the electrodeposition technique. Structural and chemical characterization of the produced composite coatings was performed with the aid of X-ray diffraction (XRD), scanning electron microscopy (SEM) and electron dispersive X-ray analysis (EDS) techniques. The Ni-Co-fly ash coatings were found to consist of a crystalline Ni-Co solid solution with dispersed fly ash particles. In addition, chemical analysis of the Ni-Co matrix showed that it consisted of 80 wt.% Ni and 20 wt.% Co. The co-deposition of fly ash particles leads to a significant increase of the microhardness of the coating. The corrosion behaviour of the Ni-Co-fly ash/zincate coated aluminium alloy, in a 0.3 M NaCl solution (pH = 3.5), was studied by means of potentiodynamic corrosion experiments.     

Formation of titania composite coatings on carbon steel by plasma electrolytic oxidation

Titania composite coatings were prepared on carbon steel by plasma electrolytic oxidation in silicate electrolyte and aluminate electrolyte with titania powers doping in the electrolytes. The microstructure of the coatings was characterized by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The properties of the coatings including bond strength, thickness, thermal shock resistance and corrosion resistance varying with the quantities of titania powers in the electrolytes were studied. Investigation results revealed that the coating obtained in silicate electrolyte was composed of anatase-TiO₂, rutile-TiO₂ crystal phases and some Fe, Si, P elements; coating obtained in aluminate electrolyte consisted of anatase-TiO₂, Al₂TiO₅ and some Fe, P elements. Coatings obtained in two types of electrolytes show porous and rough surface. With increasing the concentration of titania powers in the electrolytes, the coating surface first became more compact and less porous and then became more porous and coarse. The bond strength and thickness were not strongly affected by concentration of titania powers in electrolytes. The valves were 23 MPa and for 66 μm for coatings obtained in aluminate electrolyte, and 21 MPa and 35 μm for coatings obtained in silicate electrolyte. Coatings obtained in silicate electrolyte showed a little better thermal shock resistance than those obtained in aluminate electrolyte and the best coatings were obtained with middle concentration of titania powers in the electrolytes. All coated samples showed better corrosion resistance than the substrate in 3.5 wt% NaCl solution. The best coatings were also obtained with middle concentration of titania powers doping in both electrolytes whose corrosion current density was decreased by 2 orders of magnitude compared with the substrate.     

Electrodeposition and properties of Zn-nanosized TiO2 composite coatings

Nanosized TiO₂ particles were prepared by sol-gel method. The TiO₂ particles were co-deposited with zinc from a sulphate bath at pH 4.5 using electrodeposition technique. The corrosion behavior of the coatings was assessed by electrochemical polarization, impedance, weight-loss and salt spray tests. Wear resistance and microhardness of the composite coating was measured. The smaller grain size of the composite coatings was observed in the presence of TiO₂ and it was confirmed by the images of scanning electron microscopy (SEM) and X-ray diffraction (XRD) techniques.     

Effects of pulse electrodeposition parameters on the properties of Ni-TiO2 nanocomposite coatings

The aim of this study is to investigate the effects of pulse electrodeposition parameters on the properties of nickel-titania composite coatings electrodeposited from a nickel Watts type bath. The effects of average current density, frequency and duty cycle on the surface morphology, crystal size, preferred orientation of the deposits and the amount of embedded nano-TiO₂ particles in the composite coatings were investigated. The results represented the optimum amount of average current density (e.g., 4 A dm⁻²) for obtaining the highest volume percentage of the incorporated titania particles and subsequently the maximum microhardness. Moreover, by increasing the frequency up to 10 Hz while reducing the duty cycle to 10% at constant peak current density, the volume percentage of particles increased to about 7% which is almost twice as much the volume percentage as deposited particles in direct current method. According to the results the composite coating exhibited obviously [1 0 0] + [2 1 1] as preferred orientation at low pulse frequency and the diffraction intensity of the [2 1 1] fiber orientation is increased, probably due to the pH increase adjacent to the electrolyte/cathode interface at higher frequencies. Also, it has been found that by reduction in the duty cycle, more titania particles were incorporated in the composite coatings and this promoted the nickel crystals growth on [1 0 0] planes and consequently the coatings preferred orientation changed from the [2 1 1] to [1 0 0] + [2 1 1] planes.     

Electrodeposition of Al-Mn alloy on AZ31B magnesium alloy in molten salts

The Al-Mn alloy coatings were electrodeposited on AZ31B Mg alloy in AlCl₃-NaCl-KCl-MnCl₂ molten salts at 170 °C aiming to improve the corrosion resistance. However, in order to prevent AZ31B Mg alloy from corrosion during electrodeposition in molten salts and to ensure excellent adhesion of coatings to the substrate, AZ31B Mg alloy should be pre-plated with a thin zinc layer as intermediate layer. Then the microstructure, composition and phase constituents of the coatings were investigated by scanning electron microscopy (SEM), energy-dispersive X-ray spectrometry (EDX), and X-ray diffraction (XRD). It was indicated that, by adjusting the MnCl₂ content in the molten salts from 0.5 wt% to 2 wt%, the Mn content in the alloy coating was increased and the phase constituents were changed from f.c.c Al-Mn solid solution to amorphous phase. The corrosion resistance of the coatings was evaluated by potentiodynamic polarization measurements in 3.5% NaCl solution. It was confirmed that the Al-Mn alloy coatings exhibited good corrosion resistance with a chear passive region and significantly reduced corrosion current density at anodic potentiodynamic polarization. The corrosion resistance of the alloy coatings was also related with the microstructure and Mn content of the coatings.     

Characterization of microarc oxidation coatings formed on AM60B magnesium alloy in silicate and phosphate electrolytes

Microarc oxidation coatings on AM60B magnesium alloy were prepared in silicate and phosphate electrolytes. Structure, composition, mechanical property, tribological, and corrosion resistant characteristics of the coatings was studied by scanning electron microscope (SEM), X-ray diffraction (XRD) and microhardness analyses, and by ball-on-disc friction and potentiodynamic corrosion testing. It is found that the coating produced from the silicate electrolyte is compact and uniform and is mainly composed of MgO and forsterite Mg₂SiO₄ phases, while the one formed in phosphate electrolyte is relatively porous and is mainly composed of MgO phase. The thick coating produced from a silicate electrolyte possesses a high hardness and provides a low wear rate (3.55 × 10⁻⁵ mm³/Nm) but a high friction coefficient against Si₃N₄ ball. A relatively low hardness and friction coefficient while a high wear rate (8.65 × 10⁻⁵ mm³/Nm) is recorded during the testing of the thick coating produced from a phosphate electrolyte. Both of these types of coatings provide effective protection for the corrosion resistance compared with the uncoated magnesium alloy. The coating prepared from the silicate electrolyte demonstrates better corrosion behavior due to the compacter microstructure.     

Preparation and wear resistance of pulse electrodeposited Ni-W/Al2O3 composite coatings

The aim of this work is to obtain the electroplating parameters for preparation of Ni-W/Al₂O₃ composite coating with high tungsten content, high micro-hardness and excellent wear resistance by pulse plating procedure. Our results showed that the duty cycle is a dominant parameter for the tungsten content in the coating and the tungsten content increases significantly with increasing duty cycle. The further analysis showed the great influence of tungsten content on micro-hardness of the coating. A maximum micro-hardness of about 859 Hv was obtained in pulse electrodeposited Ni-W/Al₂O₃ composite with tungsten content of 40 wt.% at a peak current density of 20 A/dm², a duty cycle of 80%, a pulse frequency of 1000 Hz and a particle loading of 10 g/L alumina in the plating bath. Although the hardness of Ni-W/Al₂O₃ composite coating was only slightly affected by the alumina content of the deposits prepared in present investigation, the alumina content effect on the tribological characteristic of Ni-W/Al₂O₃ composite coatings is significant. The friction coefficient was lowered to 0.25 and the wear loss was reduced to 1.05 mg by setting the control factors according to the values mentioned above for obtaining the coating with the highest micro-hardness.     

Ultra-hard ceramic coatings fabricated through microarc oxidation on aluminium alloy

Ultra-hard ceramic coatings with microhardness of 2535 Hv have been synthesized on the Al alloy substrate by microarc oxidation (MAO) technique. The effects of anodic current density (j_a) and the ratio of cathodic to anodic current density (j_c/j_a) on the mechanical and corrosion resistance properties of MAO coatings have been studied by microhardness and pitting corrosion tests, respectively. In addition, the phase composition and microstructure of the coatings were analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The results show that the coatings prepared at high anodic current density consist mainly of α-Al₂O₃, while those fabricated at low anodic current density are almost composed of γ-Al₂O₃. Microhardness test shows that the coatings have high microhardness, and the highest one is found in the coating formed at j_a = 15 A/dm² and j_c/j_a = 0.7. Pitting corrosion test shows that the structure of coatings is strongly influenced by the varying j_c/j_a.     

Effect of Ni-to-Fe ratio on structure and properties of Ni-Fe-B-Si-Nb coatings fabricated by laser processing

Ni-Fe-B-Si-Nb coatings have been deposited on mild steel substrates using high power laser cladding process followed by laser remelting. The influence of Ni-to-Fe concentration ratio in (Ni_100−xFe_x)₆₂B₁₈Si₁₈Nb₂ (x = 55, 50, 45 and 40) powders on the phase composition and microstructure is analyzed by X-ray diffraction, scanning- and transmission-electron microscopies. The microhardness and corrosion resistance properties of the coatings are also measured. The results reveal that amorphous matrix layers are obtained for all coatings. The increase of the Ni-to-Fe ratio can promote the formation of γ(Fe-Ni) phase and decrease the formation of Fe₂B phase and α-Fe phase. The coating with 1:1 ratio of Ni-to-Fe exhibits the highest microhardness of 1200 HV_0.5 and superior corrosion resistance property due to its largest volume fraction of amorphous phase in the coating. Higher or lower than 1:1 ratio of Ni-to-Fe may result in lower amorphous forming ability. However, even that the coating with ratio of 3:2, shows a minimum of microhardness, it shows a better corrosion resistance than other two coatings.     

Microstructure and corrosion resistance behavior of ceramic coatings on biomedical NiTi alloy prepared by micro-arc oxidation

In this paper, ceramic coatings were prepared on biomedical NiTi alloys by micro-arc oxidation (MAO) in constant voltage mode. The current density-time response was recorded during the MAO process. The microstructure, element distribution and phase composition of the coatings prepared at different MAO treatment times were investigated by scanning electron microscopy (SEM), energy dispersive X-ray spectrometer (EDS), thin-film X-ray diffraction (TF-XRD) and X-ray photoelectron spectroscopy (XPS). The corrosion behavior of the coatings in 0.9% NaCl solution was evaluated by the potentiodynamic polarization test. It is found that the coatings become more compact with increasing the MAO treatment time, and the growth rate of coating decreases. The results of TF-XRD, EDS and XPS indicate that the coatings are composed of a large amount of γ-Al₂O₃ and a little α-Al₂O₃, TiO₂ and Ni₂O₃. The Ni content of the coatings is about 3 at.%, which is greatly lower than that of NiTi substrate. The bonding strength of coating-substrate is higher than 40 MPa for all the samples in this study. The corrosion resistance of the coatings is about two orders of magnitude higher than that of the uncoated NiTi alloy.     

Effects of duty ratio at low frequency on growth mechanism of micro-plasma oxidation ceramic coatings on Ti alloy

The aim of this work is to study the effects of duty ratio on the growth mechanism of the ceramic coatings on Ti-6Al-4V alloy prepared by pulsed single-polar MPO at 50 Hz in NaAlO₂ solution. The phase composition of the coatings was studied by X-ray diffraction, and the morphology and the element distribution in the coating were examined through scanning electron microscopy and energy dispersive spectroscopy. The thickness of the coatings was measured by eddy current coating thickness gauge. The corrosion resistance of the coated samples was examined by linear sweep voltammetry technique in 3.5% NaCl solution. The changes of the duty ratio (D) of the anode process led to the changes of the mode of the spark discharge during the pulsed single-polar MPO process, which further influenced the structure and the morphology of the ceramic coatings. The coatings prepared at D = 10% were composed of a large amount of Al₂TiO₅ and a little γ-Al₂O₃ while the coatings prepared at D = 45% were mainly composed of α-Al₂O₃ and γ-Al₂O₃. The coating thickness and the roughness were both increased with the increasing D due to the formation of Al₂O₃. The formation of Al₂TiO₅ resulted from the spark discharge due to the breakdown of the oxide film, while the formation of Al₂O₃ resulted from the spark discharge due to the breakdown of the vapor envelope. The ceramic coatings improved the corrosion resistance of Ti-6Al-4V alloy. And the surface morphology and the coating thickness determined the corrosion resistance of the coated samples prepared at D = 45% was better than that of the coated samples prepared at D = 10%.     

Preparation and characterization of nickel nano-Al2O3 composite coatings by sediment co-deposition

Ni-Al₂O₃ composite coatings were prepared by using sediment co-deposition (SCD) technique and conventional electroplating (CEP) technique from Watt's type electrolyte without any additives. The microstructure, hardness, and wear resistance of resulting composites were investigated. The results show that the incorporation of nano-Al₂O₃ particles changes the surface morphology of nickel matrix. The preferential orientation is modified from (2 0 0) plane to (1 1 1) plane. The microhardness of Ni-Al₂O₃ composite coatings in the SCD technique are higher than that of the CEP technique and pure Ni coating and increase with the increasing of the nano-Al₂O₃ particles concentration in plating solution. The wear rate of the Ni-Al₂O₃ composite coating fabricated via SCD technique with 10 g/l nano-Al₂O₃ particles in plating bath is approximately one order of magnitude lower than that of pure Ni coating. Wear resistance for SCD obtained composite coatings is superior to that obtained by the CEP technique. The wear mechanism of pure Ni and nickel nano-Al₂O₃ composite coatings are adhesive wear and abrasive wear, respectively.     

Morphological, mechanical, corrosion and hydrogen permeation characteristics of Ni-nano-TiO2 composite coating compared to Ni electrodeposited on low carbon steel

Ni and Ni-nano-TiO₂ composite coatings with various amounts of TiO₂ in electrolyte, on low carbon steel, have been prepared from Watts-bath using electrodeposition process. The morphological, mechanical, corrosion and hydrogen permeation characteristics of Ni and Ni-nano-TiO₂ coatings were studied and compared with each other. The results revealed that, existence of nano-TiO₂ particles in Ni matrix improved the microstructure as well as microhardness, whereas increasing particle incorporation from 4.33 to 7.62 vol % concluded to microhardness enhancement. The corrosion behavior of Ni and Ni-nano-TiO₂ composite coatings with various amount of particle content was studied by the anodic polarization curves in 5% H₂SO₄ solution at room temperature. It was seen Ni-nano-TiO₂ composite coatings exhibited higher corrosion resistances comparing to pure Ni coating and corrosion protection improved with increasing nano-TiO₂ in coatings. In addition to the corrosion and engineering properties, comparison of hydrogen permeation characteristics of the Ni coating was made with Ni-nano-TiO₂ composite coating through Devanthan-Stachurski hydrogen permeation test. From the resulting data analysis, Ni-nano-TiO₂ composite coating was seen not only to provide longer life under corroding media, but also reduces greatly the risk of the substrate being exposed to hydrogen permeation when compared to electrodeposited Ni coating.     

Preparation and high-temperature properties of Au nano-particles doped α-Al2O3 composite coating on TiAl-based alloy

Au nano-particles doped α-Al₂O₃ composite coatings were successfully prepared on TiAl-based alloy by electrodeposition, using the Al₂O₃ sols with minor addition of HAuCl₄ solution. The even distribution of Au nano-particles (<2.0 wt.%) in the α-Al₂O₃ matrix has been observed. Isothermal oxidation tests of the samples coated with the as-prepared novel coatings at 900 °C in static air for 200 h shown that the oxygen inward diffusion can be effectively suppressed to a low level. The results of high-temperature cyclic oxidation test at 900 °C in air revealed that the oxidation and spallation resistance of TiAl-based alloy were improved significantly under thermal cycling. In the as-prepared coatings, cracks were shielded by means of crack bridging and the fracture resistance of the formed scales can be improved by toughening effects of the composite structure. Surface scratching tests after the cyclic oxidation exhibited that the adhesion of the formed composite scale on TiAl-based alloy was remarkably improved by the Au nano-particles doped α-Al₂O₃ composite coating.