Thermodynamic study of Cu-Tl-Te system using EMF technique with Cu<Subscript>4</Subscript>RbCl<Subscript>3</Subscript>I<Subscript>2</Subscript> solid electrolyte

The EMF method with a solid Cu⁺-conducting electrolyte of Cu₄RbCl₃I₂ was sued to study the Cu-Tl-Te system in the temperature range of 300–420 K. A diagram of solid-phase equilibriums of this system is constructed, partial molar functions of copper in alloys, standard thermodynamic functions of formation and standard entropies of CuTlTe₂, CuTl₄Te₃, Cu₂TlTe₂, Cu₃TlTe₂, Cu₉TlTe₅ triple compounds and Cu _x Tl_{5 − x} Te₃ solid solutions (0 < x < 1) are calculated. The obtained results confirmed the assumption as to the possibility of using this modification for the EMF technique for thermodynamic studies of copper-containing triple systems, even if they contain a less noble component than copper.     

Thermodynamic study of Ag<Subscript>8</Subscript>GeSe<Subscript>6</Subscript> by EMF with an Ag<Subscript>4</Subscript>RbI<Subscript>5</Subscript> solid electrolyte

The Ag–Ge–Se system was studied in the range of compositions Ag₂Se–GeSe₂–Se by measuring the EMF of the concentration (relative to the silver electrode) circuits with a solid electrolyte Ag₄RbI₅ in the temperature range 290–430 K. The polymorphic transition temperature of Ag₈GeSe₆ (320 K) was determined and the partial molar functions of silver were calculated for both crystal modifications of this compound based on the EMF measurements. The thermodynamic functions of formation and entropy of both modifications of Ag₈GeSe₆ and the thermodynamic functions of its polymorphic transition were calculated.     

Phase equilibria in the PbSe-Bi<Subscript>2</Subscript>Se<Subscript>3</Subscript>-Se system and thermodynamic properties of intermediate phases

The Pb-Bi-Se system in the PbSe-Bi₂Se₃-Se-Se composition region was studied by measurement of concentration circuits of the type (−) PbSe(solid) liquid electrolyte, Pb²⁺(Pb-Bi-Se)(solid) (+) in the temperature range 300–430 K and by X-ray powder diffraction. A solid-phase equilibrium diagram was constructed, and the formation was confirmed for the ternary compounds Pb₅Bi₆Se₁₄, Pb₅Bi₁₂Se₂₃, and Pb₅Bi₁₈Se₃₂, which belong to the homologous series [(PbSe)₅] _m · [(Bi₂Se₃)₃] _n . From the emf versus temperature equations, the partial thermodynamic functions [`(DG)]\overline {\Delta G}, [`(DH)]\overline {\Delta H}, [`(DS)]\overline {\Delta S} of PbSe in alloys were calculated. Based on the solid-phase equilibrium diagram from these partial molar quantities using the corresponding data for PbSe and Bi₂Se₃, the standard thermodynamic functions of formation and standard entropies of the above ternary compounds were calculated.     

Thermodynamic Properties of AgIn<Subscript>2</Subscript>Te<Subscript>3</Subscript>I and AgIn<Subscript>2</Subscript>Te<Subscript>3</Subscript>Br,Determined by EMF Method

Differential thermal analysis (DTA), X-ray diffraction (XRD), and electromotive force (EMF) are used to triangulate Ag–In–Te–I(Br) systems in the vicinity of compounds AgIn₂Te₃I and AgIn₂Te₃Br. The three-dimensional position of the AgIn₂Te₃I–InTe–Ag₂Te–AgI and AgIn₂Te₃Br–InTe–Ag₃TeBr phase areas with respect to the figurative points of silver is used to create equations of potential-determining chemical reactions. The potential-determining reactions are conducted in (?)C|Ag|Ag₃GeS₃I(Br) glass|D|C(+) electrochemical cells (ECCs), where C stands for inert (graphite) electrodes, Ag and D are ECC electrodes (D denotes alloys of one-, three-, and four-phase areas), and Ag₃GeS₃I and Ag₃GeS₃Br glasses are membranes with purely ionic Ag⁺ conductivity. Linear parts of the temperature dependences of the cell EMFs are used to calculate the standard integral thermodynamic functions of saturated solid solutions based on AgIn₂Te₃I and AgIn₂Te₃Br, and the relative partial thermodynamic functions of silver in the stoichiometric quaternary compounds.     

Thermodynamic study of the Ag-As-Se and Ag-S-I systems using the EMF method with a solid Ag<Subscript>4</Subscript>RbI<Subscript>5</Subscript> electrolyte

The EMF method with a solid Ag₄RbI₅ superionic conductor was used to study the Ag-As-Se and Ag-S-I systems in the composition ranges of Ag₂Se-As₂Se₃-Se and Ag₂S-AgI-S, accordingly. Their solid-phase equilibrium diagrams are constructed or specified. The existence of ternary AgAs₃Se₅, AgAsSe₂, Ag₃AsSe₃, Ag₇AsSe₆, Ag₃SI compounds is confirmed. The standard partial and integral thermodynamic formation functions and also standard entropies were calculated for these compounds for the first time.     

Thermal behaviour and properties of Na<Subscript>2</Subscript>O-TiO<Subscript>2</Subscript>-P<Subscript>2</Subscript>O<Subscript>5</Subscript> glasses

Differential scanning calorimetry (DSC) and thermomechanical analysis (TMA) were used to study the thermal behaviour of (50-x)Na₂O-xTiO₂-50P₂O₅ and 45Na₂O-yTiO₂-(55-y)P₂O₅ glasses. The addition of TiO₂ to the starting glasses (x=0 and y=5 mol% TiO₂) resulted in a nonlinear increase of glass transition temperature and dilatation softening temperature, whereas the thermal expansion coefficient decreased. All prepared glasses crystallize under heating within the temperature range of 300–610°C. The contribution of the surface crystallization mechanism over the internal one increases with increasing TiO₂ content. With increasing TiO₂ content the temperature of maximum nucleation rate is also gradually shifted from a value close to the glass transition temperature towards the crystallization temperature. X-ray diffraction measurements showed that the major compounds formed by glass crystallization were NaPO₃, TiP₂O₇ and NaTi₂(PO₄)₃. The chemical durability of the glasses without titanium oxide is very poor, but with the replacement of Na₂O or P₂O₅ by TiO₂, it increases sharply.     

Thermal analysis study of Bi<Subscript>2</Subscript>Sr<Subscript>2</Subscript>Ca<Subscript>2</Subscript>Cu<Subscript>3-x</Subscript>Er<Subscript>x</Subscript>O<Subscript>10+δ</Subscript> glass-ceramic system

Summary We have fabricated glasses in the Bi-2223 HT_c superconductor system with Bi₂Sr₂Ca₂Cu_3-xEr_xO_{10+ δ} nominal composition, where x=0.5 and 1.0, by the glass-ceramic technique. Using an analysis developed for non-isothermal crystallization studies, information on some aspects of crystallization temperature and thermal properties has been obtained. The crystallization studies were made using DTA with several uniform rates. The calculations of crystallization activation energies, E_a, and the Avrami parameters, n, were made based on the non-isothermal kinetic theory of Kissinger and the Ozawa’s equations. The DTA data of the samples showed that the first crystallization temperature, T_x1, increases and the second crystallization temperature, T_x2, decreases by increasing the Er concentration. This suggests that the Er substitution had significant effect on the glassification of the BSCCO material due to change on the surface nucleation and increased ionic activities at high temperature region. The activation energy for crystallization, E_a, of the samples was also showed an increase at high Er concentration case. However, the Avrami parameter, n, decreased from 2.5 to 1.7 for x=0.5 and 1.0 samples, respectively. This suggests that the growth mechanism is diffusion-controlled and three-dimensional parabolic growth takes place near the first crystallization temperature. The oxidization rates and the activation barrier for oxygen out-diffusion process, E, was calculated using the TG data. It was found that the total mass gain in the x=0.5 sample is comparably smaller than that of the x=1.0 sample. This shows that the oxygen absorption of the x=1.0 sample is faster than the x=0.5 sample, leading to increase in the oxidization rate in the x=1.0 material.     

Reactivity of triangular oxalate cluster complexes [M<Subscript>3</Subscript>Q<Subscript>7</Subscript>(C<Subscript>2</Subscript>O<Subscript>4</Subscript>)<Subscript>3</Subscript>]<Superscript>2−</Superscript> (M = Mo or W; Q = S or Se)

The reactions of the oxalate complexes [M₃Q₇(C₂O₄)₃]²⁻ (M = Mo or W; Q = S or Se) with Mn^II, Co^II, Ni^II, and Cu^II aqua and ethylenediamine complexes in aqueous and aqueous ethanolic solutions were studied. The previously unknown heterometallic complexes [Mo₃Se₇(C₂O₄)₃Ni(H₂O)₅]·3.5H₂O (1) and K₃{[Cu(en)₂H₂O]([Mo₃S₇(ox)₃]₂Br)}·5.5H₂O (2) were synthesized. In these complexes, the oxalate clusters serve as monodentate ligands. The K(H₂en)₂[W₃S₇(C₂O₄)₃]₂Br·4H₂O salt (3) was isolated from solutions containing Co^II, Ni^II, or Cu^II aqua complexes and ethylenediamine. The reaction of [Mo₃Se₇(C₂O₄)₃]²⁻ with HBr produced the bromide complex [Mo₃Se₇Br₆]²⁻, which was isolated as (Bu₄N)₂[Mo₃Se₇Br₆] (4). Complexes 1–3 were characterized by X-ray diffraction, IR spectra, and elemental analysis. The formation of 4 was detected by electrospray mass spectrometry. Dedicated to Academician G. A. Abakumov on the occasion of his 70th birthday. Published in Russian in Izvestiya Akademii Nauk. Seriya Khimicheskaya, No. 9, pp. 1645–1649, September, 2007.     

Synthesis of nonequilibrium Ir<Subscript>x</Subscript>Re<Subscript>1-x</Subscript> solid solutions. Crystal structure of [Ir(NH<Subscript>3</Subscript>)<Subscript>5</Subscript>Cl]<Subscript>2</Subscript>[ReCl<Subscript>6</Subscript>]Cl<Subscript>2</Subscript>

Synthesis of five binary complex salts with an [Ir(NH₃)₅Cl]²⁺ complex cation is described. The counterions are [ReCl₆]^2–, [IrCl₆]^2–, [ReBr₆]^2–, and Cl^–. A polycrystal X-ray diffraction study has been performed for [Ir(NH₃)₅Cl]₂[ReCl₆]Cl₂, and its crystal structure has been determined. A series of Ir _x Re_1–x phases (0.5 x > 1) were obtained by reductive thermolysis. For the Ir-Re system, the history of the V/Z(x) dependence has been refined.Original Russian Text Copyright © 2004 by S. A. Gromilov, S. V. Korenev, I. V. Korolkov, K. V. Yusenko, and I. A. BaidinaTranslated from Zhurnal Strukturnoi Khimii, Vol. 45, No. 3, pp. 508–515, May–June 2004.     

Nano-composites SnO(VO<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>) as anodes for lithium ion batteries

Nano-composites of SnO(V₂O₃) _x (x = 0, 0.25, and 0.5) and SnO(VO)_0.5 are prepared from SnO and V₂O₃/VO by high-energy ball milling (HEB) and are characterized by X-ray diffraction (XRD), scanning electron microscopy, and high-resolution transmission electron microscopy techniques. Interestingly, SnO and SnO(VO)_0.5 are unstable to HEB and disproportionate to Sn and SnO₂, whereas HEB of SnO(V₂O₃) _x gives rise to SnO₂.VO _x . Galvanostatic cycling of the phases is carried out at 60 mA g⁻¹ (0.12 C) in the voltage range 0.005–0.8 V vs. Li. The nano-SnO(V₂O₃)_0.5 showed a first-charge capacity of 435 (±5) mAh g⁻¹ which stabilized to 380 (±5) mAh g⁻¹ with no noticeable fading in the range of 10–60 cycles. Under similar cycling conditions, nano-SnO (x = 0), nano-SnO(V₂O₃)_0.25, and nano-SnO(VO)_0.5 showed initial reversible capacities between 630 and 390 (±5) mAh g⁻¹. Between 10 and 50 cycles, nano-SnO showed a capacity fade as high as 59%, whereas the above two VO _x -containing composites showed capacity fade ranging from 10% to 28%. In all the nano-composites, the average discharge potential is 0.2–0.3 V and average charge potential is 0.5–0.6 V vs. Li, and the coulombic efficiency is 96–98% after 10 cycles. The observed galvanostatic cycling, cyclic voltammetry, and ex situ XRD data are interpreted in terms of the alloying–de-alloying reaction of Sn in the nano-composite “Sn-VO _x -Li₂O” with VO _x acting as an electronically conducting matrix.     

Phase formation in the Ag<Subscript>2</Subscript>MoO<Subscript>4</Subscript>-MgMoO<Subscript>4</Subscript>-Al<Subscript>2</Subscript>(MoO<Subscript>4</Subscript>)<Subscript>3</Subscript> system

The subsolidus region of the Ag₂MoO₄-MgMoO₄-Al₂(MoO₄)₃ ternary salt system has been studied by X-ray phase analysis. The formation of new compounds Ag_{1 ? x} Mg_{1 ? x} Al_{1 + x} (MoO₄)₃ (0 ≤ x ≤ 0.4) and AgMg₃Al(MoO₄)₅ has been determined. The Ag_{1 ? x} Mg_{1 ? x} Al_{1 + x} (MoO₄)₃ variable-composition phase is related to the NASICON type structure (space group R \(\bar 3\) c). AgMg₃Al(MoO₄)₅ is isostructural to sodium magnesium indium molybdate of the same formula unit and crystallizes in triclinic system (space group P \(\bar 1\), Z = 2) with the following unit cell parameters: a = 9.295(7) Å, b = 17.619(2) Å, c = 6.8570(7) Å, α = 87.420(9)°, β = 101.109(9)°, γ = 91.847(9)°. The compounds Ag_{1 ? x} Mg_{1 ? x} Al_{1 + x} (MoO₄)₃ and AgMg₃Al(MoO₄)₅ are thermally stable up to 790 and 820°C, respectively.     

Cu<Subscript>4</Subscript>RbCl<Subscript>3</Subscript>I<Subscript>2</Subscript> solid superionic conductor in thermodynamic study of three-component copper chalcogenides

The Cu-B-Se (B = In, As, Sb, Bi) systems are studied by measurement of EMF for concentration circuits vs. a copper electrode in the temperature range of 300–430 K. A solid superionic Cu₄RbCl₃I₂ conductor is used as an electrolyte. Diagrams of solid-phase equilibriums in the studied systems are constructed. Partial molar functions of alloyed copper are calculated on the basis of the equations of the temperature dependences of EMF. Potential-forming reactions corresponding to the measured EMF values are determined on the basis of the phase diagrams and standard thermodynamic formation functions and standard entropies of ternary compounds are calculated.     

Character of interaction and glass formation in the TlAs<Subscript>2</Subscript>Se<Subscript>4</Subscript>-Tl<Subscript>3</Subscript>As<Subscript>2</Subscript>S<Subscript>3</Subscript>Se<Subscript>3</Subscript> system

The TlAs₂Se₄-Tl₃As₂S₃Se₃ system was investigated by physicochemical methods (DTA, X-ray powder diffraction, microstructural analysis), and its phase diagram was constructed. The TlAs₂Se₄-Tl₃As₂S₃Se₃ join is a quasi-binary internal section of the As-Tl-S-Se quaternary system. The solubility range of TlAs₂Se₄-based solid solutions is extended to 7 mol %, and the region of Tl₃As₂S₃Se₃-based solid solutions is extended to 15 mol %.     

NaF-CaF<Subscript>2</Subscript>-YbF<Subscript>3</Subscript> phase diagram

Vertical sections CaF₂-Na_0.4Yb_0.6F_2.2 and NaF-Ca_0.75Yb_0.25F_2.25 of the system NaF-CaF₂-YbF₃ were studied by differential thermal analysis. A fluorite solid solution belt between phases of variable composition Ca_1?x Yb _x F_2+x and Na_0.5?x Yb_0.5+x F_2+2x was discovered. A liquidus-surface projection was constructed. The solidification character of the solid solution is unfavorable for growth of optical-quality ternary mixed crystals.     

Glass transition and crystallization study of chalcogenide Se<Subscript>70</Subscript>Te<Subscript>15</Subscript>In<Subscript>15</Subscript> glass

Differential scanning calorimetry data at different heating rates (5, 10, 15 and 20 °C min⁻¹) of Se₇₀Te₁₅In₁₅ chalcogenide glass is reported and discussed. The crystallization mechanism is explained in terms of recent analyses developed for use under non-isothermal conditions. The value of Avrami exponent (n) indicates that the glassy Se₇₀Te₁₅In₁₅ alloy has three-dimensional growth. The average values of the activation energy for glass transition, E _g, and crystallization process, E _c, are (154.16 ± 4.1) kJ mol⁻¹ and (98.81 ± 18.1) kJ mol⁻¹, respectively. The ease of glass formation has also been studied. The reduced glass transition temperature (T _rg), Hruby’ parameter (K _gl) and fragility index (F _i) indicate that the prepared glass is obtained from a strong glass forming liquid.     

Synthesis,crystal structure,and biological properties of the complex [Co(DmgH)<Subscript>2</Subscript>(Seu)<Subscript>1.4</Subscript>(Se-Seu)<Subscript>0.5</Subscript>(Se<Subscript>2</Subscript>)<Subscript>0.1</Subscript>][BF<Subscript>4</Subscript>]

A new Co(III) dioxime complex with selenocarbamide was obtained by the reaction of Co(BF₄)₂ ? 6H₂O, DmgH₂, and Seu (DmgH2 = dimethylglyoxime, Seu = selenocarbamide). According to X-ray diffraction (CIF file CCDC no. 1485732), the product was an ionic coordination compound with unusual composition, [Co(DmgH)₂(Seu)_1.4(Se-Seu)_0.5(Se₂)_0.1][BF₄] (I). Apart from two monodeprotonated DmgH￣ molecules, the central atom coordinates neutral Seu, Se-Seu, and Se₂ molecules. Thus, the crystal contains the complex cations [Co(DmgH)₂(Seu)₂]⁺, [Co(DmgH)₂(Seu)(Se-Seu)]⁺, and [Co(DmgH)₂(Seu)(Se₂)]⁺. Each [BF₄]￣ anion is linked to the cations not only by electrostatic forces but also by intermolecular N–H···F hydrogen bonds (H-bonds). The complex cations are combined by intermolecular N–H···O H-bonds. The new coordination compound was found to possess biological activity. Treatment of the garlic (Allium sativum L.) foliage with an aqueous solution of I optimizes the content of selenium in the leaves and cloves and enhances the growth and plant productivity. The organs of treated plants are characterized by enhanced antioxidant protection owing to increasing activity of antioxidant enzymes and contents of proline and assimilation pigments, and decreasing lipid peroxidation.     

Effects of Cr doping on the electrochemical performance of Li<Subscript>3</Subscript>V<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript> cathode material for lithium ion batteries

A series of Cr-doped Li₃V_2???x Cr _x (PO₄)₃ (x?=?0, 0.1, 0.25, and 0.5) samples are prepared by a sol–gel method. The effects of Cr doping on the physical and chemical characteristics of Li₃V₂(PO₄)₃ are investigated. Compared with the XRD pattern of the undoped sample, the XRD patterns of the Cr-doped samples have no extra reflections, which indicates that Cr enters the structure of Li₃V₂(PO₄)₃. As indicated by the charge–discharge measurements, the Cr-doped Li₃V_2???x Cr _x (PO₄)₃ (x?=?0.1, 0.25, and 0.5) samples exhibit lower initial capacities than the undoped sample at the 0.2 C rate. However, both the discharge capacity and cycling performance at high rates (e.g., 1 and 2 C) are enhanced with proper amount of Cr doping (x?=?0.1). The highest discharge capacity and capacity retention at the rates of 1 and 2 C are obtained for Li₃V_1.9Cr_0.1(PO₄)₃. The improvement of the electrochemical performance can be attributed to the higher crystal stability and smaller particle size induced by Cr doping.     

LiMn<Subscript>2</Subscript>O<Subscript>4</Subscript> and LiCoO<Subscript>2</Subscript> composite cathode materials obtained by mechanical activation

New composite cathode materials xLiMn₂O₄/(1 ? x) LiCoO₂(x = 0.7, 0.6, 0.5 и 0.4) were obtained by mechanical activation. According to scanning electron microscopy data, the process was accompanied by pronounced dispersion and fine mixing of the initial components. In the course of the preparation and electrochemical cycling of the composites, LiMn₂O₄ and LiCoO₂ partially reacted, leading to the replacement of manganese with cobalt in the structure of spinel, which was detected by powder X-ray diffraction (XRD), IR and X-ray photoelectron spectroscopy (XPS), and cyclic chronopotentiometry. The specific discharge capacity of composites was ～100 mAh/g.     

Synthesis and crystal structure of new double mercury silver phosphide iodide Hg<Subscript>12</Subscript>Ag<Subscript>41</Subscript>P<Subscript>88</Subscript>I<Subscript>41</Subscript>

New double mercury silver phosphide iodide Hg₁₂Ag₄₁P₈₈I₄₁ (1) was synthesized and its crystal structure was established. Compound 1 crystallizes in the cubic system. The characteristic feature of the crystal structure 1 is the presence of the anionic cage clusters P₁₁ ³⁻, which have been previously found in alkali metal compounds only. The well-ordered P₁₁ ³⁻ clusters form a system of polyhedra, which encapsulate various disordered α-AgI-type fragments. Published in Russian in Izvestiya Akademii Nauk. Seriya Khimicheskaya, No. 10, pp. 1882–1886, October, 2007.     

Obtaining of Ni<Subscript>0.65</Subscript>Zn<Subscript>0.35</Subscript>Fe<Subscript>2</Subscript>O<Subscript>4</Subscript>/SiO<Subscript>2</Subscript> nanocomposites by thermal decomposition of complex compounds embedded in silica matrix

This article presents the results of our investigation on the obtaining of Ni_0.65Zn_0.35Fe₂O₄ ferrite nanoparticles embedded in a SiO₂ matrix using a modified sol–gel synthesis method, starting from tetraethylorthosilicate (TEOS), metal (Fe^III,Ni^II,Zn^II) nitrates and ethylene glycol (EG). This method consists in the formation of carboxylate type complexes, inside the silica matrix, used as forerunners for the ferrite/silica nanocomposites. We prepared gels with different compositions, in order to obtain, through a suitable thermal treatment, the nanocomposites (Ni_0.65Zn_0.35Fe₂O₄)_x–(SiO₂)_100–x (where x=10, 20, 30, 40, 50, 60 mass%). The synthesized gels were studied by differential thermal analysis (DTA), thermogravimetry (TG) and FTIR spectroscopy. The formation of Ni–Zn ferrite in the silica matrix and the behavior in an external magnetic field were studied by X-ray diffraction (XRD) and quasi-static magnetic measurements (50 Hz).