Characterization of MoO3 nanorods for lithium battery using PVP as a surfactant

We synthesized MoO₃ nanorods using poly (vinyl pyrrolidone) (PVP) as a surfactant through the hydrothermal route for making a cathode for a lithium battery. Scanning electron microscopy images reveal the structures to have dimensions on the order of 1–10 μm in length and 50–200 nm in diameter. Analytical techniques such as X-ray diffractometry, Fourier transformation infrared spectroscopy, thermogravimetric analysis, and cyclic voltammetry were used to characterize the nanorods. The measured specific charge of MoO₃ nanorods prepared through a 15-day hydrothermal reaction was 156 mAhg⁻¹ during the initial discharge process.     

Preparation of nanocrystalline Fe-doped TiO<Subscript>2</Subscript> powders as a visible-light-responsive photocatalyst

Nanocrystalline Fe-doped TiO₂ powders were prepared using TiOSO₄, urea, and Fe(NO₃)₃ · 9H₂O as precursors through a hydrothermal method. The as-synthesized yellowish-colored powders are composed of anatase TiO₂, identified by X-ray diffraction (XRD). The grain size ranged from 9.7 to 12.1 nm, calculated by Scherrer’s method. The specific surface area ranged from 141 to 170 m²/g, obtained by the Brunauer–Emmett–Teller (BET) method. The transmission electron microscopy (TEM) micrograph of the sample shows that the diameter of the grains is uniformly distributed at about 10 nm, which is consistent with that calculated by Scherrer’s method. Fe³⁺ and Fe²⁺ have been detected on the surface of TiO₂ powders by X-ray photoelectron spectroscopy (XPS). The UV–Vis diffuse reflection spectra indicate that the light absorption thresholds of the Fe-doped TiO₂ powders have been red-shifted into the visible light region. The photocatalytic activity of the Fe-doped TiO₂ was evaluated through the degradation of methylene blue (MB) under visible light irradiation. The Fe-doped TiO₂ powders have shown good visible-light photocatalytic activities and the maximum degradation ratio is achieved within 4.5 h.     

Synthesis,characterization of B-doped TiO<Subscript>2</Subscript> nanotubes with high photocatalytic activity

B-doped TiO₂ nanotubes (B/TiO₂ NTs) were prepared by the combination of sol–gel process with hydrothermal treatment. The prepared catalysts were characterized by XRD, TEM and XPS. The photocatalytic activity of B/TiO₂ NTs was evaluated through the photodegradation of aqueous methyl orange. The results demonstrated that the 1.5% B/TiO₂ NTs calcined at 300 °C possessed the best photocatalytic activity. Compared with pure TiO₂ nanotubes, the doping with B significantly enhanced the photocatalytic efficiency.     

The first rare-earth fluoride one-dimensional nanostructures: template synthesis of LnF<Subscript>3</Subscript> (Ln = Eu,La) nanotubes

Uniformly ordered crystal EuF₃ and LaF₃ nanotubes were prepared using alumina film as a nanochannel reactor, and characterized by scanning electron microscope (SEM), transmission electron microscope (TEM), and X-ray powder diffraction (XRD). These nanotubes have outer diameters in the range of 200–350 nm, inner diameters of 100–250 nm and length up to 30 μm. The fabrication method is simple, efficient and easy to control. It can be used to prepare a wide range of inorganic nanomaterials.     

Rational synthesis of alpha-MnO2 single-crystal nanorods

alpha-MnO2 single-crystal nanorods with diameters 20-80 nm and lengths up to 6 microns have been prepared through a low-temperature liquid-phase comproportionation method, which involves no catalysts or templates and may be adjusted to prepare alpha-MnO2 single-crystal nanorods in large scale.     

Hydrothermal synthesis of (Fe,N) co-doped TiO<Subscript>2</Subscript> powders and their photocatalytic properties under visible light irradiation

(Fe, N) co-doped titanium dioxide powders have been prepared by a quick, low-temperature hydrothermal method using TiOSO₄, CO(NH₂)₂, Fe(NO₃)₃, and CN₃H₅ · HCl as starting materials. The synthesized powders were characterized by XRD, TEM, BET, XPS, and UV–Vis spectroscopy. Experimental results show that the as-synthesized TiO₂ powders are present as the anatase phase and that the N and Fe ions have been doped into the TiO₂ lattice. The specific surface area of the powders is 167.8 m²/g by the BET method and the mean grain size is about 11 nm, calculated by Scherrer’s formula. UV–Vis absorption spectra show that the edge of the photon absorption has been red-shifted up to 605 nm. The doped titanium dioxide powders had excellent photocatalytic activity during the process of photo-degradation of formaldehyde and some TVOC gases under visible light irradiation.     

Comparison of different soft chemical routes synthesis of submicro-LiMn<Subscript>2</Subscript>O<Subscript>4</Subscript> and their influence on its electrochemical properties

A comparative study of submicro-crystalline spinel LiMn₂O₄ powders prepared by two different soft chemical routes such as hydrothermal and sol–gel methods is made. The dependence of the physicochemical properties of the spinel LiMn₂O₄ powder has been extensively investigated by using X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscope, cyclic voltammogram, charge–discharge test, and electrochemical impedance spectroscopy (EIS). The results show that the electrochemical performances of spinel LiMn₂O₄ depend strongly upon the synthesis method. The LiMn₂O₄ powder prepared by hydrothermal route has higher specific capacity and better cycling performance than the one synthesized from sol–gel method. The former has the max discharge capacity of 114.36 and 99.78 mAh g⁻¹ at the 100th cycle, while the latter has the max discharge capacity of 98.67 and 60.25 mAh g⁻¹ at the 100th cycle. The selected equivalent circuit can fit well the EIS results of synthesized LiMn₂O₄. For spinel LiMn₂O₄ from sol–gel method and hydrothermal route in the first charge process R _SEI remain almost invariable, R _e and R _ct first decreasing and then increasing with the increase of polarization potential.     

Ru/Ni/MgAl<Subscript>2</Subscript>O<Subscript>4</Subscript> catalysts for steam reforming of methane: effects of Ru content on self-activation property

The effects of Ru on the self-reducibility of Ru-doped Ni/MgAl₂O₄ catalysts, which do not need pre-reduction treatment with H₂, were investigated in the steam reforming of methane (SRM). The Ru-promoted Ni/MgAl₂O₄ catalysts with various amounts of Ru (0–0.5 wt%) were prepared by stepwise impregnation and co-impregnation methods using hydrotalcite-like MgAl₂O₄ support. For comparison, Ru/MgAl₂O₄ catalysts with the same amount of Ru were also prepared by the impregnation method. The catalysts were characterized by the N₂-sorption, XRD, H₂-TPR, H₂-chemisorption, and XPS methods. Ni/MgAl₂O₄ catalyst in the presence of even the trace amount of Ru (Ru content ≥0.05 wt%) showed higher conversion without pre-reduction as compared to Ru/MgAl₂O₄ catalysts in SRM under the same conditions. The self-activation of Ru–Ni/MgAl₂O₄ catalysts is mainly attributed to the spillover of hydrogen, which is produced on Ru at first and then reduces NiO species under reaction conditions. Besides, Ru doping makes the reduction of NiO easier. The stepwise impregnated Ru/Ni/MgAl₂O₄ catalyst produced superior performance as compared to co-impregnated Ru–Ni/MgAl₂O₄ catalyst for SRM.     

Structural evolution and magnetic properties of SrFe<Subscript>12</Subscript>O<Subscript>19</Subscript> nanofibers by electrospinning

The SrFe₁₂O₁₉/poly (vinyl pyrrolidone) (PVP) composite fiber precursors were prepared by the sol-gel assisted electrospinning with ferric nitrate, strontium nitrate and PVP as starting reagents. Subsequently, the M-type strontium ferrite (SrFe₁₂O₁₉) nanofibers were derived from calcination of these precursors at 750–1,000 °C.The composite precursors and strontium ferrite nanofibers were characterized by Fourier transform infrared spectroscopy, X-ray diffraction, scanning electron microscopy and vibrating sample magnetometer. The structural evolution process of strontium ferrite consists of the thermal decomposition and M-type strontium ferrite formation. After calcined at 750 °C for 2 h the single M-type strontium ferrite phase is formed by reactions of iron oxide and strontium oxide produced during the precursor decomposition process. The nanofiber morphology, diameter, crystallite size and grain morphology are mainly influenced by the calcination temperature and holding time. The SrFe₁₂O₁₉ nanofibers characterized with diameters of around 100 nm and a necklace-like structure obtained at 900 °C for 2 h, which is fabricated by nanosized particles about 60 nm with the plate-like morphology elongated in the preferred direction perpendicular to the c-axis, show the optimized magnetic property with saturation magnetization 59 A m² kg⁻¹ and coercivity 521 kA m⁻¹. It is found that the single domain critical size for these M-type strontium ferrite nanofibers is around 60 nm.     

Gold catalysts supported on ZnO/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> for low-temperature CO oxidation

Gold catalysts with loadings ranging from 0.5 to 7.0 wt% on a ZnO/Al₂O₃ support were prepared by the deposition–precipitation method (Au/ZnO/Al₂O₃) with ammonium bicarbonate as the precipitation agent and were evaluated for performance in CO oxidation. These catalysts were characterized by inductively coupled plasma-atom emission spectrometry, temperature programmed reduction, and scanning transmission electron microscopy. The catalytic activity for CO oxidation was measured using a flow reactor under atmospheric pressure. Catalytic activity was found to be strongly dependent on the reduction property of oxygen adsorbed on the gold surface, which related to gold particle size. Higher catalytic activity was found when the gold particles had an average diameter of 3–5 nm; in this range, gold catalysts were more active than the Pt/ZnO/Al₂O₃ catalyst in CO oxidation. Au/ZnO/Al₂O₃ catalyst with small amount of ZnO is more active than Au/Al₂O₃ catalyst due to higher dispersion of gold particles.     

Synthesis of electrospun BaSrTiO<Subscript>3</Subscript>/PVP nanofibers

Ba_1−x Sr _x TiO₃(x = 0–0.5, BST) nanofibers with diameters of 150–210 nm were prepared by using electrospun BST/polyvinylpyrrolidone (PVP) composite fibers by calcination for 2 h at temperatures in the range of 650–800 °C in air. The morphology and crystal structure of calcined BST/PVP nanofibers were characterized as functions of calcination temperature and Sr content with an aid of XRD, FT-IR, and TEM. Although several unknown XRD peaks were detected when the fibers were calcined at temperatures less than 750 °C, they disappeared with increasing the temperature (above 750 °C) due to its thermal decomposition and complete reaction in the formation of BST. In addition, the FT-IR studies of BST/PVP fibers revealed that the intensities of the O–H stretching vibration bands (at 3430 and 1425 cm⁻¹) became weaker with increasing the calcination temperature and a broad band at 540 cm⁻¹, Ti–O vibration, appeared sharper and narrower after calcination above 750 °C due to the formation of metal oxide bonds. However, no effect of Sr content on the crystal structure of the composites was detected.     

Low Temperature Hydrothermal Synthesis of MnO<Subscript>2</Subscript> Nanoclusters as Positive Material of RAM Batteries

MnO₂ nanoclusters were synthesized by a low temperature hydrothermal method. In the presented procedure, MnO₂ was precipitated by oxidation of manganese sulfate solution upon addition of ammonium persulfate solution. The synthesized sample was characterized by SEM and XRD. Optimized nanoclusters with needle diameters of 30 nm were synthesized by mixing of manganese sulfate solution (0.8 M) with ammonium persulfate solution (0.7 M) in sulfuric acid media (0.8 M) at constant temperature of 80 °C. Effect of solid state lithium sulfate treatment on the phase composition, particle size and morphology of the obtained MnO₂ nanoclusters was studied at different temperatures. The obtained results showed that lithium salt can changes MnO₂ nanoclusters morphology without any intercalation. Discharge capacity and cycle life of the synthesized MnO₂ nanoclusters as positive materials of RAM battery (Zn–MnO₂ battery), before and after treatment with lithium sulfate were studied. MnO₂ nanopowder showed average discharge capacity of 190 mA.h/g (with respect to MnO₂ weight) during 3 first discharges. Lithium sulfate-treated powder showed higher discharge capacity (160 mA.h/g) and shorter cycle life than the untreated powder.     

Template-based electrophoretic growth of PbZrO<Subscript>3</Subscript> nanotubes

Lead zirconate (PbZrO₃) nanotubes have been grown using porous anodic alumina templates. Sol–gel electrophoresis technique was utilized to form the nanotubes on the pore walls. The alumina templates were prepared using various anodizing voltages and times to achieve different pore diameters and lengths. Phosphoric acid solution was employed as the anodizing electrolyte. Stabilized lead zirconate sols were prepared using lead acetate trihydrate and an alkoxide precursor of zirconium. Acetic acid was used as the modifier. The prepared sols were driven into the template channels under various electrophoretic voltages and times, and the effect of the electrophoresis parameters on the formation of nanotubes was investigated. The filled templates were dried at 100 °C and sintered at 700 °C. Scanning and transmission electron microscopy (SEM and TEM) investigations demonstrated the tubular form of the lead zirconate arrays. The SEM investigations also showed the nanotubes have been efficiently grown in the template pores. The TEM studies further confirmed the polycrystalline nature of the tubes.     

Synthesis of LiNi<Subscript>1/3</Subscript>Co<Subscript>1/3</Subscript>Mn<Subscript>1/3</Subscript>O<Subscript>2</Subscript> nanoparticles by modified Pechini method and their enhanced rate capability

Layered LiNi_1/3Co_1/3Mn_1/3O₂ nanoparticles were prepared by modified Pechini method and used as cathode materials for Li-ion batteries. The pyrolytic behaviors of the foamed precursors were analyzed by use of simultaneous thermogravimetric and differential thermal analysis (TG-DTA). Structure, morphology and electrochemical performance characterization of the samples were investigated by X-ray diffraction (XRD), field emission scanning electron macroscopy(SEM), Brunauer-Emmett-Teller (BET) specific surface area and charge–discharge tests. The results showed that the samples prepared by modified Pechini method caclined at 900 °C for 10 h were indexed to pure LiNi_1/3Co_1/3Mn_1/3O₂ with well hexagonal structure. The particle size was in a range of 100–300 nm. The specific surface area was larger than that of the as-obtained sample by Pechini method. Initial discharge capacity of 163.8 mAh/g in the range 2.8–4.4 V (vs. Li/Li⁺) and at 0.1C for LiNi_1/3Co_1/3Mn_1/3O₂ prepared by modified Pechini method was obtained, higher than that of the sample prepared by Pechini method (143.5 mAh/g). Moreover, the comparison of electrochemical results at different current rates indicated that the sample prepared by modified Pechini method exhibited improved rate capability.     

Some studies on the phase formation and kinetics in TiO<Subscript>2</Subscript> containing lithium aluminum silicate glasses nucleated by P<Subscript>2</Subscript>O<Subscript>5</Subscript>

Lithium aluminum silicate (LAS) glasses of compositions (wt%) 10.6Li₂O–71.7SiO₂–7.1Al₂O₃–4.9K₂O–3.2B₂O₃–1.25P₂O₅–1.25TiO₂ were prepared by the melt quench technique. Crystallization kinetics was investigated by the method of Kissinger and Augis–Bennett using differential thermal analysis (DTA). Based on the DTA data, glass ceramics were prepared by single-, two-, and three-step heat treatment schedules. The interdependence of different phases formed, microstructure, thermal expansion coefficient (TEC) and microhardness (MH) was investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), thermo-mechanical analysis (TMA), and microhardness (MH) measurements. Crystallization kinetics revealed that Li₂SiO₃ is the kinetically favored phase with activation energy of 91.10 kJ/mol. An Avrami exponent of n = 3.33 indicated the dominance of bulk crystallization. Based upon the formation of phases, it was observed that the two-stage heat treatment results in highest TEC glass ceramics. The single-step heat treatment yielded glass ceramics with the highest MH.     

Preparation of highly active photocatalyst anatase TiO<Subscript>2</Subscript> by mixed template method

TiO₂ nanocrystals with diameters 8–10 nm have been prepared through sol–gel method using a mixed template of polyethylene glycol (PEG) and cetytrimethylammonium bromide (CTAB) at low temperature. The samples were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution (HR) TEM and fourier transform infrared spectroscopy (FT-IR) etc. XRD analysis showed the TiO₂ photocatalysts prepared with mixed template are pure anatase. FTIR spectrum revealed that the cationic surfactant provides CTA⁺ molecules and bonds to Ti–O to prevent the condensation reaction. PEG plays a dispersant role in controlling the structure of nano-TiO₂ particles. CTAB and PEG incorporated with each other to restrain the growth of crystal nucleus and control the size of grain. The self-assembling process has been confirmed by HRTEM. PEG played different role in mixed template from the single template. The photocatalytic activity of samples was determined by using as a model reaction. The results showed that TiO₂ photocatalysts with mixed template have higher photocatalytic activity than P25.     

MoO3−δ nanorods: Synthesis,characterization and magnetic properties

A novel preparation method of MoO_2.987 nanorods and the thorough investigation of their structural and magnetic properties by means of X-ray diffraction and infrared spectroscopy as well as by scanning and transmission electron microscopy are reported. MoO_3−δ nanorods were prepared via hydrothermal treatment of a mixture made from molybdenum peroxide solution and oxalic acid. The presented synthesis approach is very simple, of low-cost and can be a perspective for industrial manufacturing. The resulting single crystalline nanorods exhibit diameters of 60–90 nm and lengths up to several micrometers. The crystal structure was found to be orthorhombic as in α-MoO₃. This agrees with our magnetization data which imply non-magnetic Mo⁶⁺ ions but show only a small amount of magnetic impurities giving rise to a weak paramagnetic response.     

Non-isothermal decomposition kinetics of NiFe<Subscript>2</Subscript>O<Subscript>4</Subscript> nanoparticles synthesized using egg white solution route

The thermal decomposition kinetics of nickel ferrite (NiFe₂O₄) precursor prepared using egg white solution route in dynamical air atmosphere was studied by means of TG with different heating rates. The activation energy (E _α) values of one reaction process were estimated using the methods of Flynn–Wall–Ozawa (FWO) and Kissinger–Akahira–Sunose (KAS), which were found to be consistent. The dependent activation energies on extent of conversions of the decomposition reaction indicate “multi-step” processes. XRD, SEM and FTIR showed that the synthesized NiFe₂O₄ precursor after calcination at 773 K has a pure spinel phase, having particle sizes of ~54 ± 29 nm.     

Mechanism of the nanocrystals formation of the spinel structure in the MgO-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-H<Subscript>2</Subscript>O system under the hydrothermal conditions

Using the method of hydrothermal synthesis,the nanoparticles of magnesium-aluminum spinel were obtained with a crystallite size of 40–50 nm. The sequence was determined of the chemical transformations under hydrothermal conditions of the initial magnesium-aluminum hydroxides obtained by co-precipitation, leading to the formation of nanoparticles MgAl₂O₄.     

Facile synthesis of CeO2 nanoplates and nanorods by [1 0 0] oriented growth

This study demonstrated a facile method for the synthesis of CeO₂ nanoplates and nanorods via the thermal decomposition of a mixture of cerium acetate, oleic acid, oleyamine and 1-octadecene under controlled atmospheres. Morphologies of the produced cerium oxides were controlled by the adding procedures of activators. Activators added at room temperature and heated with the reaction mixture result in the formation of nanoplates. Injection of activators at high temperature leads to the formation of nanorods. Both the nanoplates and nanorods are achieved via the [1 0 0] oriented assembly of smaller particles. A blue-shifting of the UV absorption threshold edge are observed for the cerium oxide nanoplates and nanorods, contrasting with the bulk commercial powders.