Oxygen permeability of La2Cu(Co)O4+δ solid solutions

Formation of the La₂Cu_1−xCo_xO_4+δ solid solutions with orthorhombic K₂NiF₄-type structure was found to be in the range of 0≤x≤0.30 at temperatures above 1270 K. Incorporating cobalt into the copper sublattice of lanthanum cuprate leads to increasing oxygen hyperstoichiometry and decreasing electrical conductivity. Thermal expansion coefficients of the La₂Cu_1−xCo_xO_4+δ (x=0.02–0.30) ceramics at 470–1100 K were calculated from the dilatometric data to vary in the range (12.2–13.2)×10⁻⁶ K⁻¹. Studying the dependence of oxygen permeation fluxes through La₂Cu(Co)O_4+δ on the membrane thickness demonstrated that the oxygen transport at the thickness values below 1 mm is limited by both surface exchange rate and bulk ionic conductivity. Oxygen permeability of the La₂Cu_1−xCo_xO_4+δ solid solutions was ascertained to increase with cobalt concentration at x=0.02–0.10 and to decrease with further dopant additions, indicating a participation of interstitial oxygen in the ionic transport.     

Perovskite-like system (Sr,La)(Fe,Ga)O3−δ: structure and ionic transport under oxidizing conditions

The maximum solid solubility of gallium in the perovskite-type La_1−xSr_xFe_1−yGa_yO_3−δ (x=0.40–0.80; y=0–0.60) was found to vary in the approximate range y=0.25–0.45, decreasing when x increases. Crystal lattice of the perovskite phases, formed in atmospheric air, was studied by X-ray diffraction (XRD) and neutron diffraction and identified as cubic. Doping with Ga results in increasing unit cell volume, while the thermal expansion and total conductivity of (La,Sr)(Fe,Ga)O_3−δ in air decrease with gallium additions. The average thermal expansion coefficients (TECs) are in the range (11.7–16.0)×10⁻⁶ K⁻¹ at 300–800 K and (19.3–26.7)×10⁻⁶ K⁻¹ at 800–1100 K. At oxygen partial pressures close to atmospheric air, the oxygen permeation fluxes through La_1−xSr_xFe_1−yGa_yO_3−δ (x=0.7–0.8; y=0.2–0.4) membranes are determined by the bulk ambipolar conductivity; the limiting effect of the oxygen surface exchange was found negligible. Decreasing strontium and gallium concentrations leads to a greater role of the exchange processes. As for many other perovskite systems, the oxygen ionic conductivity of La_1−xSr_xFe_1−yGa_yO_3−δ increases with strontium content up to x=0.70 and decreases on further doping, probably due to association of oxygen vacancies. Incorporation of moderate amounts of gallium into the B sublattice results in increasing structural disorder, higher ionic conductivity at temperatures below 1170 K, and lower activation energy for the ionic transport.     

Study of superconducting state parameters of alkali–alkali binary alloys by a pseudopotential

A detailed study of the superconducting state parameters (SSP) viz. electron–phonon coupling strength λ, Coulomb pseudopotential μ^*, transition temperature T_C, isotope effect exponent and effective interaction strength N_OV of ten alkali–alkali binary alloys i.e. Li_1−xNa_x, Li_1−xK_x, Li_1−xRb_x, Li_1−xCs_x, Na_1−xK_x, Na_1−xRb_x, Na_1−xCs_x, K_1−xRb_x, K_1−xCs_x and Rb_1−xCs_x are made within the framework of the model potential formalism and employing the pseudo-alloy-atom (PAA) model for the first time. We use the Ashcroft’s empty core (EMC) model potential for evaluating the superconducting properties of alkali alloys. Five different forms of local field correction functions viz. Hartree (H), Taylor (T), Ichimaru–Utsumi (IU), Farid et al. (F) and Sarkar et al. (S) are used to incorporate the exchange and correlation effects. A considerable influence of various exchange and correlation functions on λ and μ^* is found from the present study. Reasonable agreement with the theoretical values of the SSP of pure components is found (corresponding to the concentration x = 0 or 1). It is also concluded that nature of the SSP strongly depends on the value of the atomic volume Ω₀ of alkali–alkali binary alloys.     

Trapping mechanism of superconductivity suppression induced by Pr substitution in the Ho1−xPrxBa2Cu3O7−δ system

Pr concentration dependence of the superconducting transition temperature T_c in the Ho_1−xPr_xBa₂Cu₃O_7−δ system is determined from measurements of DC electrical resistance. This dependence coincides with that for the parallely studied Y_1−xPr_xBa₂Cu₃O_7−δ reference system. Both systems have the same value of the critical concentration x_c=0.58, in accordance with nearly equal ionic radii of Ho³⁺ and Y³⁺ ions. It has been shown that the T_c(x) curve can be described with a single mechanism based on a decreasing number of sheet holes trapped by Pr^IV-ions, if one takes also into account that the number of these ions changes with x.     

Structural study and magnetoresistance effect of epitaxial La0.67Sr0.33MnO3–δ and Pr0.7Ca0.3MnO3−δ multilayer films

La_0.67Sr_0.33MnO_3−δ (LSMO) and Pr_0.7Ca_0.3MnO_3−δ (PCMO) multilayer epitaxial films, which were fabricated with different LSMO and PCMO layer thickness on LaAlO₃ single crystal substrates of (0 0 1) orientation by a direct current magnetron sputtering technique, were studied further, after the structure, magnetoresistance effect and magnetic properties of LSMO/PCMO/LSMO (LPL) trilayer epitaxial films were systemically studied. The superlattice structures of multilayer films were observed according to the diffraction peaks of X-ray diffraction patterns at small angles. The metal–insulator transition temperature (T_P) and peak resistivity (ρ_max) obviously changed when we altered the thickness of PCMO middle layer and the intra-field related with the thickness of those layers and their interaction. Considering the effect of the distribution of electrical field and current, and the interaction among the layers of LSMO and PCMO, an effective fact n* was introduced to replace n (the number of layer). All the calculated values of ρ (the resistivity of multilayer films) accorded with the experimental values.     

Dielectric and magnetic properties of xNiFe2O4+(1−x)Ba0.9Sr0.1TiO3 composites

Magnetoelectric composites, namely, xNiFe₂O₄+(1−x)Ba_0.9Sr_0.1TiO₃ were prepared by standard double sintering ceramic method. The X-ray diffraction analysis was carried out to check the phases formed during sintering and to calculate the lattice parameters. Scanning electron microscope (SEM) micrographs were taken to understand the microstructure of the samples. The dielectric constant (ε′) and loss tangent (tan δ) were measured as a function of frequency in the frequency range 100 Hz–1 MHz. Variation of dielectric constant and loss tangent with temperature and composition has been reported. The hysteresis measurements were done to determine saturation magnetization (M_S) and coersivity (H_c). The variation of saturation magnetization and magnetic moment is interpreted in terms of composition.     

Ferromagnetic Zr1−xMnxCo2 laves phase compounds

Structure and magnetic properties of the Zr_1−xMn_xCo_2+δ alloys were studied for 0 x <0.7, δ=0, 0.45. The cubic C15 Laves phase structure shows Mn solubility up to x≈0.4. The other Laves phase with the hexagonal C36 structure found for x0.5 apparently has a small region of Mn solubility in the vicinity of Zr_0.4Mn_0.6Co₂. Though the parent Mn-free compounds are known to be paramagnetic, the Mn-substituted alloys show ferromagnetic behavior with the Curie temperatures up to 625 K and the room-temperature saturation magnetization of about 100 emu/g. The onset of ferromagnetism with the Mn substitution for Zr may be caused by polarization of itinerant 3d electrons, like it was earlier supposed for the off-stoichiometric ZrCo_2+δ. The universal composition dependencies of the intrinsic magnetic properties for different δ can be obtained, if plotted against the amount of zirconium atoms missing in its sublattice. The room-temperature anisotropy with the noticeable anisotropy field of 24 kOe and the 1 1 0 easy magnetization direction laying in a basal plane was found in the hexagonal Zr_0.5Mn_0.5Co₂.     

Characterization of nonstoichiometric nickel manganite spinels NixMn3−x□3δ/4O4+δ by temperature programmed reduction

Cation deficient spinels Ni_xMn_3−x□_3δ/4O_4+δ (0≤x≤1) have been prepared by thermal decomposition of mixed oxalates Ni_x/3Mn_(3−x)/3(C₂O₄)·nH₂O in air at 623 K. They have been characterised by temperature programmed reduction (TPR) under H₂, the reaction being followed by gravimetric and powder X-ray diffraction measurements. It has been shown that TPR proceeds in several steps. The first steps correspond to the loss of nonstoichiometric oxygen leading to the formation of a stoichiometric oxide. During the following stages the manganese cations are reduced, causing the spinel structure to be destroyed, and the formation of solid solution of NiO in a cubic MnO. Subsequently, Ni²⁺ cations undergo a reduction to metallic nickel, and, finally, a mixture of nonstoichiometric MnO_1−δ and metallic nickel is formed. These oxides contain a high level of vacancies which vary with the nickel content with a maximum of δ≈1 near x=0.6. This nonstoichiometry is ascribed both to the presence of Ni³⁺ and excess of Mn⁴⁺.     

Nax/2Bi1−x/2MoxV1−xO4 and Bi1−x/3MoxV1−xO4 New Scheelite-related phases

New Scheelite-related solid solutions of the compositions Na_x/2Bi_1−x/2Mo_xV_1−xO₄ (0≤x≤1) and Bi_1−x/3 Mo_xV_1−xO₄(0≤x≤0.2) have been synthesised by the substitution of Na and Mo at the A and B sites respectively of the ABO₄ type ferroelastic BiVO₄. The phases were characterised using chemical analysis, powder X-ray diffraction, scanning electron microscopy, EDAX, and Raman spectroscopy. While almost a continuous solid solution is obtained for the series Na_x/2Bi_1−x/2Mo_xV_1−xO₄, the absence of Na at the A-site results only in a narrow stability region for the other series, Bi_1−x/3 Mo_xV_1−xO₄ where 0≤x≤0.2. Raman spectra of selected samples at room temperature also suggest that vanadium and molybdenum atoms are disordered at the tetrahedral sites.     

Oxygen diffusion and surface exchange in La1−xSrxFe0.8Cr0.2O3−δ (x=0.2, 0.4 and 0.6)

Oxygen tracer diffusion (D*) and surface exchange rate constant (k*) have been measured, using isotopic exchange and depth profiling by secondary ion mass spectrometry (SIMS), in La_1−xSr_xFe_0.8Cr_0.2O_3−δ (x=0.2, 0.4 and 0.6). Measurements were made as a function of temperature (700–1000 °C) and oxygen partial pressure (0.21–10⁻²¹ atm) in dry oxygen, water vapour and water vapour/hydrogen/nitrogen mixtures. At high oxygen activity, D* was found to increase with increasing temperature and Sr content. The activation energies for D* in air are 2.13 eV (x=0.2), 1.53 eV (x=0.4) and 1.21 eV (x=0.6). As the oxygen activity decreases, D* increases as expected qualitatively from the increase in oxygen vacancy concentration. Under strongly reducing conditions, the measured values of D* at 1000 °C range from 10⁻⁸ cm² s⁻¹ for x=0.2 to 10⁻⁷ cm² s⁻¹ for x=0.4 and 0.6. The activation energies determined at constant H₂O/H₂ ratio are 1.21 eV (x=0.2), 1.59 eV (x=0.4) and 0.82 eV (x=0.6).

The surface exchange rate constant of oxygen for the H₂O molecule is similar in magnitude to that for the O₂ molecule and both increase with increasing Sr concentration.     

Structural and compositional analysis of InBixAsySb(1−x−y) films grown on GaAs(0 0 1) substrates by liquid phase epitaxy

The growth of epitaxial InBi_xAs_ySb_(1−x−y) layers on highly lattice mis-matched semi-insulating GaAs substrates has been successfully achieved via the traditional liquid phase epitaxy. Orientation and single crystalline nature of the film have been confirmed by X-ray diffraction. Scanning electron micrograph shows abrupt interface at micrometer resolution. Surface composition of Bi(x) and As(y) in the InBi_xAs_ySb_(1−x−y) film was measured using energy dispersive X-ray analysis and found to be 2.5 and 10.5 at.%, respectively, and was further confirmed with X-ray photoelectron spectroscopy. Variation of the composition with depth of the film was studied by removing the layers with low current (20 μA) Ar⁺ etching. It was observed that with successive Ar⁺ etching, In/Sb ratio remained the same, while the As/Sb and Bi/Sb ratios changed slightly with etching time. However after about 5 min etching the As/Sb and Bi/Sb ratios reached constant values. The room temperature band gap of InBi_0.025As_0.105Sb_0.870 was found to be in the range of 0.113–0.120 eV. The measured values of mobility and carrier density at room temperature are 3.1×10⁴ cm² V⁻¹ s⁻¹ and 8.07×10¹⁶ cm⁻³, respectively.     

A spectroscopic ellipsometric investigation of new critical points of Zn1−xMnxS epilayers

Zn_1−xMn_xS epilayers were grown on GaAs (1 0 0) substrates by hot-wall epitaxy. X-ray diffraction (XRD) patterns revealed that all the epilayers have a zincblende structure. The optical properties were investigated using spectroscopic ellipsometry at 300 K from 3.0 to 8.5 eV. The obtained data were analyzed for determining the critical points of pseudodielectric function spectra, (E) = ₁(E) + i₂(E), such as E₀, E₀ + Δ₀, and E₁, and three E₂ (Σ, Δ, Γ) structures at a lower Mn composition range. These critical points were determined by analytical line-shapes fitted to numerically calculated derivatives of their pseudodielectric functions. The observation of new peaks, as well as the shifting and broadening of the critical points of Zn_1−xMn_xS epilayers, were investigated as a function of Mn composition by ellipsometric measurements for the first time. The characteristics of the peaks changed with increasing Mn composition. In particular, four new peaks were observed between 4.0 and 8.0 eV for Zn_1−xMn_xS epilayers, and their characteristics were investigated in this study.     

Phonon Raman scattering in Nd1+xBa2−xCu3O7−δ and Pr1+xBa2−xCu3O7−δ single crystals

The polarized Raman spectra of Nd_1+xBa_2−xCu₃O_7−δ (−0.023≤x≤0.107) and Pr_1+xBa_2−xCu₃O_7−δ (0.01≤x≤0.15) single crystals have been investigated. It was found that the Cu(2) A_g mode softens by 6 cm⁻¹ in Nd 1:2:3 and 4 cm⁻¹ in Pr 1:2:3 as x increases. These frequency shifts cannot be explained by the change in the relevant bond lengths due to Nd(Pr)-substitution for Ba. The variations with x of the two low frequency modes may be affected by change of their hybridization and/or change of their force constants. The linewidths of Ba mode in Pr 1:2:3 are broader than those in Y 1:2:3. This result suggests that the Pr substitution on Ba sites occurred even in a very small value of x. In x(yy) geometry the relative intensity of the Ba and O(4) modes in Nd 1:2:3 is greater than those in Pr 1:2:3. The difference between Nd 1:2:3 and Pr 1:2:3 in the relative intensity of the Ba and O(4) modes may be produced by the chains.     

Material design of new lithium ionic conductor, thio-LISICON, in the Li2S–P2S5 system

A new lithium ionic conductor of the thio-LISICON (LIthium SuperIonic CONductor) family was found in the binary Li₂S–P₂S₅ system; the new solid solution with the composition range 0.0≤x≤0.27 in Li_3+5xP_1−xS₄ was synthesized at 700 °C and characterized by X-ray diffraction measurements. Its electrical and electrochemical properties were studied by ac impedance and cyclic voltammetry measurements, respectively. The solid solution member at x=0.065 in Li_3+5xP_1−xS₄ showed the highest conductivity value of 1.5×10⁻⁴ S cm⁻¹ at 27 °C with negligible electronic conductivity and the activation energy of 22 kJ mol⁻¹ which is characteristic of high ionic conduction state. The extra lithium ions in Li₃PS₄ created by partial substitution of P⁵⁺ for Li⁺ led to the large increase in ionic conductivity. In the solid solution range examined, the minimum conductivity was obtained for the compositions, Li₃PS₄ (x=0.0 in Li_3+5xP_1−xS₄) and Li₄P_0.8S₄ (x=0.2 in Li_3+5xP_1−xS₄); this conductivity behavior is similar to other thio-LISICON family with the general formula, Li_xM_1−yM_y′S₄ (M=Si, Ge, and M′=P, Al, Zn, Ga, Sb). Conduction mechanism and the material design concepts are discussed based on the conduction behavior and the structure considerations.     

Disruption of antiferromagnetic order in Zn-doped La2CuO4

The magnetic phase diagram of La₂(Cu_1−xZn_x)O₄ has been determined from zero-field muon-spin-rotation (ZF-μSR) data taken at LAMPF for 0 ≤ x ≤ 0.10. Antiferromagnetic onset temperatures follow T_N(x) from susceptibility measurements on the same samples. However, the order becomes long range, as evidenced by a well-defined internal magnetic field, only at temperatures well below T_N. Extrapolation of our results yields T_N → 0 K at x = 0.11 for a single (Cu_1−xZn_x)O₂ plane, and comparison with YBa₂(Cu_1−xZn_x)₃O₆ implies identical disruption of magnetism by Zn doping in the single- and double-plane systems.     

Lithium insertion to ReO3-type metastable phase in the Nb2O5–WO3 system

Lithium insertion to distorted ReO₃-type metastable solid solution Nb_xW_1−xO_3−x/2 (0≤x<0.25) has been studied by chemical and electrochemical methods. In the course of lithium insertion into tetragonal compounds, transition to a cubic phase was found to occur in the region where values of y (in Li_yNb_xW_1−xO_3−x/2) fall between 0.2 and 0.3, and the phase transition was found to depend on the conditions of the reaction. Changes in OCV and lattice parameters in tetragonal region (y<0.2) were discussed from the viewpoint of the ordering of lithium ions. Also, the component diffusion coefficient of lithium in tetragonal compounds Li_0.1Nb_xW_1−xO_3−x/2 (0≤x≤0.23) was found to increase with niobium content when x≤0.10, and to saturate at 4×10⁻⁹ cm²/s.     

Study on the superconducting composite material formation in the system Bi2Sr2CaCu2O8+x/Al-containing phases

Phase evolution in the Bi---Sr---Ca---Cu---Al---O system was studied. Two Al-containing phases BiSr_1.5Ca_0.5Al₂O_z and (Sr_1−xCa_x)₃Al₂O₆ (x = 0.4 − 0.45) were determined to be chemically compatible with Bi_2.18Sr₂CaCu₂O_8+x (Bi-2212) at temperatures of the samples processing. The phase equilibria in the title system were investigated above the solidus temperature. The BiSr_1.5Ca_0.5Al₂O_z was found to be in equilibrium only with the melt and the (Sr_1−xCa_x)₃Al₂O₆ phase. This latter aluminate equilibrated with Ca,Sr cuprates, CaO, the Cu-free phase, and the liquid. The melting and solidification in Bi-2212, doped with the aluminate, corresponded to the reversible reaction Bi-2212 + BiSr_1.5Ca_0.5Al₂O_z ↔ (Sr_1−xCa_x)₃Al₂O₆ + liquid. Two sets of superconducting composite materials with initial compositions Bi-2212 + nBiSr_1.5Ca_0.5Al₂O_z and Bi-2212 + m(Sr_1−xCa_x)₃Al₂O₆ were prepared by solidification from the partial melt. The former material was composed mostly of large Bi-2212 lamellas separated by the BiSr_1.5Ca_0.5Al₂O_z phase, which destroyed superconducting links between Bi-2212 grains. The latter material consisted of a Bi-2212 polycrystalline matrix with high concentration of small (ca. 3 μm) grains of (Sr_1−xCa_x)₃Al₂O₆ imbedded in Bi-2212 lamellas. The Bi-2212 + m(Sr_1−xCa_x)₃Al₂O₆ materials displayed a trend to enhance flux pinning at T = 60 K with the increase of aluminate phase content.     

X-ray diffraction characterization of MBE grown Pr1−xSrxMnO3 thin films on NGO(1 1 0)

Oxygen plasma-assisted molecular beam epitaxial (MBE) growth of Pr_1−xSr_xMnO₃ (PSMO) thin films has been carried out on NdGaO₃(1 1 0) (NGO) substrates. The growth parameters have been optimized to realize 2D layer-by-layer growth. XRD results of the epilayers show that the PSMO/NGO(1 1 0) thin films are of high crystal quality, as clear diffraction peaks can be observed belonging to the film and the substrate, respectively. Based on analysis of the peaks, it was concluded that epitaxial relation is PSMO(1 1 0)//NGO(1 1 0), i.e., the c-axis being parallel to the surface. Both single scans (ω scan, 2θ/ω scan) and 2-axis reciprocal space mapping (RSM) were performed in an effort to assess the crystal structure, crystalline quality, surface and interface properties of the epitaxial layers. High temperature annealing effects on lattice structure and crystal quality have been studied and discussed. Transport property measurement of the PSMO thin film samples has been carried out and main features discussed.     

Higher-order elastic constants of La1.84Sr0.16CuO4 high-temperature superconductor

Finite deformation theory is used to obtain the strain energy density of a tetragonal 2–1–4-type single crystal of the high-temperature superconductor La_2−xSr_xCuO₄. The complete set of second and third-order elastic constants of the high-temperature superconductor La_2−xSr_xCuO₄ (x = 0.16) is calculated by taking into account the interactions between nine nearest-neighbour atoms in the lattice and using Mie–Grüneisen interatomic potential. For the sake of comparison we have also computed the values of these constants for x = 0.13–0.20. The values of third-order elastic constants of La_2−xSr_xCuO₄ (x = 0.13–0.20) are negative and their absolute magnitudes are one order higher than those of the second-order elastic constants.     

Spectroscopic study of BixEu1−xVO4 and BiyGd1−yVO4 mixed oxides

The mixed oxides Bi_xEu_1−xVO₄ and Bi_yGd_1−yVO₄ crystallize in a zircon-type structure, for 0 <x < 0.6 and 0 < y < 0.64, and in a fergusonite-type structure, for 0.94 < x < 1 and 0.93 < y < 1. A process of competition between the dominant and the constrained effects of the lone-pair 6s² of Bi³⁺ is discussed. The diffuse reflectance spectroscopic studies of these mixed oxides are presented. The observed broad bands are attributed to charge transfer processes and the sharp peaks in the Bi_xEu_1−xVO₄ spectra are ascribed to intra-configurational 4f – 4ftransitions of the Eu³⁺ ion. The broad absorption shift in BiLnVO₄ (Ln : Eu and Gd) compounds to the longer wavelengths range, when Bi is introduced in the LnVO₄ lattice, is ascribed to charge transfer processes in a Bi-VO₄ center and are interpreted assuming a Jahn-Teller effect in the excited state of Bi³⁺. The concept of an internal pressure of Bi³⁺ ions is also used to explain the broad A-band shifts.