高速电弧喷涂NiCrBMoFe/BaF2·CaF2涂层的摩擦磨损性能研究

利用高速电弧喷涂技术制备了NiCrBMoFe和NiCrBMoFe/BaF₂·CaF₂两种复合涂层.两种涂层均含非晶相与纳米晶相,非晶相质量百分数分别达45%和33%.NiCrBMoFe涂层中纳米晶相弥散分布在非晶母相中;NiCrBMoFe/BaF₂·CaF₂涂层纳米晶相以团聚形态存在.检测了两种涂层的摩擦磨损性能.在常温下,NiCrBMoFe和NiCrBMoFe/BaF₂·CaF₂两种涂层的摩擦系数分别为0.5和0.375,后者比基体18Cr₂Ni₄WA的摩擦系数下降了25%,耐磨性能优异.在高温摩擦磨损条件下,NiCrBMoFe/BaF₂·CaF₂涂层也具有良好的耐磨性能.在450 ℃左右,涂层中BaF₂·CaF₂固体润滑相会析出涂层表面,形成一层低摩擦系数的润滑转化膜,使涂层具有良好的减摩润滑作用.     

离子液体作为Si3N4-Ti3SiC2摩擦副润滑剂的摩擦学性能研究

采用SRV摩擦磨损试验机在室温及100 ℃下考察了两种离子液体（L-B106 和L-P106）、丙三醇、水作为Si₃N₄-Ti₃SiC₂摩擦副润滑剂的摩擦学行为,利用扫描电子显微镜（SEM）及X光电子能谱（XPS）对磨损表面进行了分析.结果表明：室温、20 N条件下,两种离子液体和丙三醇抗磨和减摩性能相当,室温、100 ℃条件下,L-P106相较于L-B106具有更好的润滑性能,且其抗磨和减摩性能均优于丙三醇,作为Si₃N₄-Ti₃SiC₂摩擦副润滑剂具有在苛刻环境条件下使用的应用前景. XPS分析结果表明：Ti₃SiC₂材料在摩擦过程中在摩擦热作用下生成了SiO_x、TiO₂,进而有效提高了Ti₃SiC₂摩擦副材料的抗磨损性能;此外,离子液体中的活性元素在Si₃N₄-Ti₃SiC₂摩擦副表面发生了复杂的摩擦化学反应,生成了由氟化钛、磷酸钛及硼酸钛等组成的具有减摩和抗磨性能的边界润滑膜.     

γ-TiAl合金激光熔覆高温自润滑耐磨复合材料涂层研究

以NiCr-Cr₃C₂-40%CaF₂(wt.%)复合合金粉末为原料,采用Nd:YAG激光熔覆技术,在γ-TiAl合金基体表面成功制备出了高温自润滑耐磨复合材料涂层,在复合粉体准备时,采用Ni-P化学镀包覆原始CaF₂颗粒,以减少其在激光熔覆过程中的分解?蒸发和上浮.采用XRD?SEM和EDS等手段对所制备复合材料涂层的显微组织进行了分析,并测试了TiAl合金及所制备的复合材料涂层的室温滑动磨损性能.结果表明:该复合材料涂层由初生发达树枝状TiC和次生块状Al ₄C₃碳化物增强相以及细小弥散分布的CaF₂润滑颗粒均匀分布在塑韧性良好的NiCrAlTi(γ)基体中,其平均显微硬度是基体TiAl合金的2倍以上. CaF₂颗粒由于采用Ni-P化学镀包覆而大部分得以保留,并且增强了其与NiCrAlTi(γ)金属基体的相容性,使得该复合材料涂层具有良好的自润滑和耐磨效果     

Ti_3SiC_2的加入对Ag-MoS_2-graphite复合材料力学及摩擦磨损性能的影响

采用热压烧结技术制备了Ag-Mo S2-graphite和Ag-Mo S2-graphite-Ti3Si C2两种银基自润滑复合材料,考察了两种材料的致密度、硬度、弯曲强度及其在不同环境(大气和低真空)中的摩擦磨损性能.结果表明:低润湿性使得Ti3Si C2与基体界面处的孔隙增多,降低了致密度和弯曲强度,但对硬度影响不明显;摩擦过程中Ti3Si C2颗粒易于从基体材料表面剥落,阻碍了润滑膜的形成,造成Ag-Mo S2-graphite-Ti3Si C2复合材料的摩擦系数高于Ag-Mo S2-graphite复合材料;但Ti3Si C2的添加能够明显提高复合材料在大气中的耐磨性能,这主要与摩擦过程中的材料转移和摩擦化学反应有关.     

微弧氧化陶瓷层对AZ31合金板料渐进成形的影响

利用数控试验机床(CNC)和微弧氧化处理技术,对AZ31镁合金板材热渐进成形和多孔陶瓷层润滑机理进行了研究.结果表明:镁合金表面微弧氧化多孔陶瓷层吸附固体二硫化钼颗粒,形成多孔陶瓷-二硫化钼润滑膜.在摩擦初始阶段,多孔陶瓷固体MoS ₂润滑膜的室温摩擦系数约为0.08,满足镁合金板材热渐进成形润滑和减摩条件.多孔陶瓷层为固体Mo S ₂润滑剂提供了良好润滑平台,加工件内表面光滑,且没有任何缺陷.由于陶瓷层孔中吸附大量固体Mo S ₂粉末,所研究的润滑陶瓷层在渐进成形中具有自润滑作用.与无微弧氧化处理相比,多孔陶瓷润滑层具有更好的润滑效果.     

中频磁控溅射制备不同S/W原子比WSx薄膜的结构和摩擦学性能研究

采用中频磁控溅射制备了WS_x薄膜,通过X射线衍射 (XRD)、场发射扫描电子显微镜(FESEM)、原子力显微镜(AFM)和X射线光电子能谱 (XPS)对其结构进行了分析,采用纳米压入仪(Triboindenter)和真空球-盘摩擦试验机分别考察了薄膜的力学性能和摩擦磨损性能.结果表明:改变溅射功率密度和气压,将引起选择性溅射与薄膜氧化程度的变化,致使薄膜S/W原子比随之变化,薄膜的S/W原子比随着溅射功率密度的增加先减小后增大,而随着溅射气压的增大逐渐增大.薄膜S/W原子比较低时,薄膜W含量较高,薄膜结构较致密、硬度较高,但摩擦系数较大、耐磨性能较差;随着S/W原子比的增大,薄膜中WS₂含量显著增加,W含量明显下降,摩擦系数降低,耐磨性能明显改善.     

DZ125高温合金表面激光熔覆Co基合金的组织和冲蚀性能研究

利用激光熔覆技术在DZ125高温合金表面制备了Co基合金熔覆层,采用光学显微镜、扫描电镜(SEM)、X射线衍射仪及HV-1000型显微硬度计测试了Co基合金熔覆层的组织结构,截面显微硬度.利用自制冲蚀设备对其耐冲蚀性能进行研究.结果表明:熔覆层与基体形成良好的冶金结合,交界处组织具有定向凝固特征且晶粒生长方向垂直于界面;在不同角度下熔覆层耐冲蚀性能各异,熔覆层的硬度是材料抗冲蚀性能影响因素之一.     

HVOF制备的微纳米结构WC-12Co涂层组织结构与抗空蚀性能

本文中采用HVOF工艺制备了二种微纳米结构及一种普通微米WC-12Co金属陶瓷复合涂层,并采用SEM、XRD等分析了涂层的显微形貌和组织结构;测量了涂层的显微硬度、孔隙率及开裂韧性;采用超声振动空蚀装置研究了涂层的抗空蚀性能,探讨了涂层空蚀机理.结果表明:由亚微米与纳米WC-12Co组成的微纳米结构涂层孔隙率最低,组织最细小;虽然HVOF制备的微米WC-12Co涂层中WC基本上没有产生氧化脱碳,但是在二种微纳米结构WC-12Co涂层中WC不同程度地产生氧化脱碳,生成W₂C、W及Co₆W₆C等物相;由亚微米与纳米WC-12Co组成的微纳米结构涂层显示了最优异的抗空蚀性能,空蚀率仅为微米涂层的1/3,其涂层抗空蚀性能提高的根本原因在于涂层中同时存在亚微米和纳米尺寸的WC、W₂C、Co₆W₆C高硬度颗粒及一定量的Co、W韧性金属,由此提高了涂层的硬度和开裂韧性,延缓了微裂纹的产生与扩展.     

Nano-WC/PTFE-Ni复合电刷镀层的磨损性能研究

采用电刷镀技术在Q235钢基材上制备含纳米WC和PTFE的镍基复合镀层,采用S-2700型扫描电子显微镜观察镀层表面形貌及其显微组织,采用HX-1型显微硬度计测定镀层的显微硬度,采用WS-2005型涂层附着力自动划痕仪测定镀层与基体的结合强度,采用HT-500型销-盘高温摩擦磨损试验机测量镀层的滑动磨损性能.结果表明:镀液中同时加入纳米WC和PTFE可以得到表面形貌平整、纳米粒子分布均匀的纳米复合镍镀层;复合镀层的硬度随WC含量的增加而增大,随PTFE含量的增加而减小;含有2种纳米粒子的复合镍镀层的耐磨性比镍镀层和含单一WC或PTFE的镍镀层的耐磨性优良;当镀液中WC和PTFE含量分别为3.0 g/L和7.5 mL/L时,复合镍镀层的显微硬度较镍镀层提高约30%,耐磨性较镍镀层提高7倍.     

电刷镀镍/镍包纳米Al_2O_3颗粒复合镀层微动磨损性能研究

应用电刷镀技术制备了含有镍包纳米 Al2 O3颗粒的镍基复合镀层 .与快速镍镀层对比考察了该复合镀层高温硬度的变化 ,同时还从微动磨损角度考察了该复合镀层耐磨性和摩擦系数的变化 .结果表明 :与快镍镀层相比 ,镍 /镍包纳米 Al2 O3复合镀层具有更高的高温硬度和更好的抗微动磨损性能 ;复合镀层在 40 0℃左右表现出较明显的强化趋势 ,具有较好的综合性能 ;纳米 Al2 O3颗粒使复合镀层的结构致密和细化 ,在磨损过程中起到了一定的减轻粘着和降低摩摩的作用 ;复合镀层的微动磨损机理主要为粘着磨损 .     

Mo/Al2O3复合材料的耐磨性

无压烧结制备了不同组分的Mo/Al2O3复合材料样品,对样品的磨损行为和磨损机理进行了研究,并用电子探针分析了其磨损形貌.结果表明:Mo/Al2O3复合材料的磨损率随Mo含量的增加呈上升趋势,在30vol.%Mo时出现峰值;摩擦系数随着Mo含量的增加而增大,20vol.%Mo样品的摩擦系数较小;Mo含量不超过60%时,当出现Mo的连续相或者Al2O3的连续相时复合材料表现出较好的耐磨性;Mo含量较低时磨损机理表现为脆性脱落,而Mo含量较高时材料的磨损机理主要为磨粒磨损.     

Spatiotemporal variations of PM2.5 and PM10 concentrations between31 Chinese cities and their relationships with SO2,NO2,CO and O3

The variations of mass concentrations of PM_2.5,PM₁₀,SO₂,NO₂,CO,and O₃ in 31 Chinese provincial capital cities were analyzed based on data from 286 monitoring sites obtained between March 22,2013 and March 31,2014.By comparing the pollutant concentrations over this length of time,the characteristics of the monthly variations of mass concentrations of air pollutants were determined.We used the Pearson correlation coefficient to establish the relationship between PM_2.5,PM₁₀,and the gas pollutants.The results revealed significant differences in the concentration levels of air pollutants and in the variations between the different cities.The Pearson correlation coefficients between PMs and NO₂ and SO₂ were either high or moderate(PM_2.5 with NO₂:r=0.256-0.688,mean r=0.498;PM₁₀ with NO₂:r = 0.169-0.713,mean r = 0.493;PM2.5 with SO₂:r= 0.232-0.693,mean r=0.449;PM₁₀ with SO₂:r = 0.131-0.669,mean r=0.403).The correlation between PMs and CO was diverse(PM_2.5:r = 0.156-0.721,mean r=0.437;PM₁₀:r=0.06-0.67,mean r= 0.380).The correlation between PMs and O₃ was either weak or uncorrelated(PM_2.5:r--0.35 to 0.089,mean r=-0.164;PM₁₀:r=-0.279 to 0.078,mean r=-0.127),except in Haikou(PM2.5:r=0.500;PM₁₀:r-0.509).     

Evaporation heat transfer coefficient in single circular small tubes for flow natural refrigerants of C3H8, NH3, and CO2

An experimental study of evaporation heat transfer coefficients for single circular small tubes was conducted for the flow of C₃H₈, NH₃, and CO₂ under various flow conditions. The test matrix encompasses the entire quality range from 0.0 to 1.0, mass fluxes from 50 to 600 kg m⁻² s⁻¹, heat fluxes from 5 to 70 kW m⁻², and saturation temperatures from 0 to 10 °C. The test section was made of circular stainless steel tubes with inner diameters of 1.5 mm and 3.0 mm, and a length of 2000 mm in a horizontal orientation. The test section was uniformly heated by applying electric power directly to the tubes. The effects of mass flux, heat flux, saturation temperature, and inner tube diameter on the heat transfer coefficient are reported. Among the working refrigerants considered in this study, CO₂ has the highest heat transfer coefficient. Laminar flow was observed in the evaporative small tubes, and was considered in the modification of boiling heat transfer coefficients and pressure drop correlations.     

氧化铝/石墨-硫酸钡层状复合材料的摩擦学性能及润滑机理

将石墨和硫酸钡按一定比例复合作为弱界面层，通过铺层-冷压-放电等离子烧结工艺制备了Al₂O₃/Graphite-BaSO₄层状复合材料. 考察了复配润滑剂的组分对层状复合陶瓷在室温至800 ℃连续加热过程中自润滑性能的影响规律，并通过磨损表面分析探讨了其在宽温域下的协同润滑机制. 结果表明:通过复配在室温和中高温度段具有优异自润滑性能的固体润滑剂，并借助仿贝壳材料独特的层状结构特征，可有效改善氧化铝陶瓷在不同温度段的摩擦学性能，进而实现材料在较宽温度范围内的连续润滑. 基于润滑相组分优化的复合材料在室温至800 ℃温度范围内与Al₂O₃栓对摩时的摩擦系数可保持在0.28~0.48之间，比块体Al₂O₃陶瓷/Al₂O₃栓摩擦副的摩擦系数降低了近60%.      

High-frequency dielectric properties of BSTO ceramic prepared with hydrothermal synthesized SrTiO3 and BaTiO3 powders

BSTO dielectric ceramic was prepared from SrTi03 and BaTi03 powders synthesized by hydrothermal method, as well as from Bao.sSro.4TiO3 powder synthesized by conventional solid-state reaction. The former can be sintered at a relatively low temperature of 1120 ℃. Characterization by SEM showed that the grain shapes of both ceramics are cubical, though the grain size of the former is much smaller. Dielectric constants measured at 20℃ were shown to vary with frequency in the range from I kHz to 2 MHz and dc bias field, and further that the dielectric loss of the former to be less than 2 × 10^- 3 in the frequency range of 20 kHz to 1 MHz, much smaller than that of the latter sample. For the former, temperature dependence of dielectric constant is much flatter and there exists an extended phase transition diffusion covering a wide temperature range of Curie temperature To. The smaller grain size of the former depresses the dc bias electrical field dependence of dielectric constant. The tunability is 7% under a bias field of 0.6 kV/mm dc.     

Fe_3Al/WS_2复合材料的真空摩擦学性能研究

采用热压烧结的方法制备了添加WS2质量百分数为10%、20%和30%的Fe-28Al-5Cr基复合材料,通过XRD和SEM等手段分析了样品的相组成和组织结构.利用自制的真空摩擦试验机测试了样品在4×10-4Pa真空下的摩擦学性能.研究结果显示:通过与WS2的复合能够显著降低Fe3Al基金属间化合物在真空条件下的摩擦系数,但三种不同WS2含量复合材料的摩擦系数差别不大.随着WS2含量增加,复合材料的磨损率逐渐降低,特别是30%复合材料的磨损率较纯Fe-28Al-5Cr的磨损率低约1个数量级.滑动速度和载荷对三种材料的摩擦系数和磨损率均有一定的影响.纯Fe3Al的磨损表面较为粗糙,出现严重的剥落坑和剥落痕迹,磨损机理为严重的疲劳磨损.添加质量百分数为10%WS2的复合材料的磨损机理为磨粒磨损和疲劳磨损;添加WS2质量百分数为20%和30%的复合材料,其磨损表面相对较为光滑平整,磨损机理为轻微剥落.因此,在复合材料制备中添加WS2能够显著提高Fe3Al金属间化合物的真空摩擦学性能.     

等离子喷涂Al2O3/TiO2纳米复合涂层的制备、结构及摩擦学性能

采用喷雾干燥法对溶胶-凝胶法合成的系列A l2O3/TiO2纳米复合粉体进行造粒,使用等离子喷涂技术制备系列A l2O3/TiO2纳米复合涂层.对涂层结构和形貌分析表明所制备的A l2O3/TiO2纳米复合涂层形成了具有熔融区和半熔融区的双区形态的纳米复合结构.使用UMT-2MT试验机研究了复合涂层的摩擦磨损性能,结果表明复合涂层的磨损率随TiO2含量的增加表现出先降低而后增大的趋势,TiO2质量百分数为10%的纳米复合涂层的磨损率最低;而涂层的摩擦系数随TiO2含量的增加变化不大.复合涂层的磨损机制为裂纹扩展导致的磨损剥落.     

Ti_3SiC_2/Cu摩擦副的载流摩擦学性能

本文中考察了Ti3SiC2/Cu摩擦副在干摩擦和微量离子液体润滑条件下的载流摩擦学特性.在干摩擦条件下,Ti3SiC2/Cu摩擦副的摩擦系数值为0.6~0.75.当滑动速度从0.11增至0.33 m/s时,接触电阻降低小,在Ti3SiC2栓磨损表面有Cu的转移膜形成.当滑动速度为0.44和0.56 m/s时,栓/盘接触不稳定并且产生电火花,表明在机械磨损和电磨损共同作用下Ti3SiC2栓发生了严重磨损.在微量离子液体润滑条件下,Ti3SiC2/Cu摩擦副处于边界润滑状态,随着滑动速度的提高,摩擦系数由0.08增至0.2.当滑动速度高于0.33 m/s时,产生长约数厘米、平均直径53μm的弯曲缠绕的铜丝,这是相对较硬的Ti3SiC2对Cu盘犁削作用的结果.铜丝将离子液体"扫离"了摩擦表面,并且对摩擦学性能和电性能造成不利影响.