Carbon‐Coated LiTi2(PO4)3: An Ideal Insertion Host for Lithium‐Ion and Sodium‐Ion Batteries |
| |
| Authors: | Dr Vanchiappan Aravindan Dr Wong Chui Ling Steffen Hartung Nicolas Bucher Prof Srinivasan Madhavi |
| |
| Affiliation: | 1. Energy Research Institute @ NTU (ERI@N), Nanyang Technological University, 637553 (Singapore);2. Technische Universit?t München, 85748 Garching (Germany);3. TUM‐CREATE, 1 Create Way, #10‐02 CREATE Tower, 138602 (Singapore);4. School of Materials Science and Engineering, Nanyang Technological University, 639798 (Singapore) |
| |
| Abstract: | We report the extraordinary performance of carbon‐coated sodium super ion conductor (NASICON)‐type LiTi2(PO4)3 as an ideal host matrix for reversible insertion of both Li and Na ions. The NASICON‐type compound was prepared by means of a Pechini‐type polymerizable complex method and was subsequently carbon coated. Several characterization techniques such as XRD, thermogravimetric analysis (TGA), field‐emission (FE) SEM, TEM, and Raman analysis were used to study the physicochemical properties. Both guest species underwent a two‐phase insertion mechanism during the charge/discharge process that was clearly evidenced from galvanostatic and cyclic voltammetric studies. Unlike that of Li (≈1.5 moles of Li), Na insertion exhibits better reversibility (≈1.59 moles of Na) while experiencing a slightly higher capacity fade (≈8 % higher than Li) and polarization (780 mV) than Li. However, excellent rate capability profiles were noted for Na insertion relative to its counterpart Li. Overall, the Na insertion properties were found to be superior relative to Li insertion, which makes carbon‐coated NASICON‐type LiTi2(PO4)3 hosts attractive for the development of next‐generation batteries. |
| |
| Keywords: | alkali metals carbon conducting materials electrodes insertion |
|
|