| 非水溶剂中纳米结构SrTiO3薄膜电极平带电位研究 |
| |
| 引用本文： | 张惠惠,寇慧芝,汪海波.非水溶剂中纳米结构SrTiO3薄膜电极平带电位研究[J].人工晶体学报,2021,50(6):1070-1075. |
| |
| 作者姓名： | 张惠惠 寇慧芝 汪海波 |
| |
| 作者单位： | 武汉轻工大学化学与环境工程学院,武汉 430023 |
| |
| 基金项目： | 国家自然科学基金(21676208);湖北省自然科学基金(Q20181806) |
| |
| 摘 要： | 本文制备了纳米结构SrTiO3薄膜电极,并通过XRD、TEM和SEM对电极的结构和表面形貌进行表征。利用光谱电化学法,测定了纳米结构SrTiO3电极在非水溶剂中的平带电位。研究发现:SrTiO3电极在水中及非水质子溶剂(甲醇、乙醇)中的平带电位比在非水非质子溶剂(乙腈、四氢呋喃)中更正。在水及非水质子溶剂中,Li+的添加对 SrTiO3电极的平带电位影响较小,而在非水非质子溶剂中,Li+的加入对 SrTiO3电极的平带电位有较大影响,随着Li+浓度的增加,SrTiO3电极的平带电位向电位更正的方向移动。
|
| 关 键 词： | SrTiO3电极 光谱电化学 非水质子溶剂 非水非质子溶剂 平带电位 |
| 收稿时间： | 2021-02-25 |
Flatband Potentials for Nanostructured SrTiO3 Film Electrodes in Nonaqueous Solvents |
| |
| ZHANG Huihui,KOU Huizhi,WANG Haibo.Flatband Potentials for Nanostructured SrTiO3 Film Electrodes in Nonaqueous Solvents[J].Journal of Synthetic Crystals,2021,50(6):1070-1075. |
| |
| Authors: | ZHANG Huihui KOU Huizhi WANG Haibo |
| |
| Affiliation: | School of Chemical and Environmental Engineering, Wuhan Polytechnic University, Wuhan 430023, China |
| |
| Abstract: | Transparent nanostructured SrTiO3 film electrodes were prepared on conduction substrates and characterized by XRD, TEM and SEM. The flatband potential (Efb) of a nanostructured SrTiO3 electrode was determined with spectroelectrochemical measurement in a range of nonaqueous solvents (acetonitrile, tetrahydrofuran, methanol and ethanol). The results show that Efb is significantly more positive for water and nonaqueous protic solvents (methanol and ethanol) than for nonaqueous aprotic solvents (acetonitrile and tetrahydrofuran) due to establishment of a proton adsorption-desorption equilibrium. Further, addition of Li+ has no significant effect on Efb in water and nonaqueous protic solvents, but in nonaqueous aprotic solvents, the Efb shifts to more positive values following the increase of added Li+ concentration. |
| |
| Keywords: | SrTiO3 electrode spectroelectrochemical nonaqueous protic solvent nonaqueous aprotic solvent flatband potential |