离子液体凝胶聚合物电解质PP13TFSI-LiTFSI-P(VdF-HFP)的电化学性能 (cited: 1)
引用本文:杨培霞,Lei Liu,Jun Hou,Jin-qiu Zhang.离子液体凝胶聚合物电解质PP13TFSI-LiTFSI-P(VdF-HFP)的电化学性能 (cited: 1)[J].化学物理学报,2013,26(4):439-444.
作者姓名:杨培霞  Lei Liu  Jun Hou  Jin-qiu Zhang
作者单位:哈尔滨工业大学化工学院,哈尔滨150001;哈尔滨工业大学化工学院,哈尔滨150001;哈尔滨工业大学化工学院,哈尔滨150001;哈尔滨工业大学化工学院,哈尔滨150001
摘    要:采用溶液浇铸法将N-甲基-N-丙基哌啶二(三氟甲基磺)亚胺(PP13TFSI)、二(三氟甲基磺)亚胺锂与偏氟乙烯-六氟丙烯共聚物(P(VdF-HFP))混合制备离子液体凝胶聚合物电解质(ILGPEs). 通过扫描电子显微镜观察发现,这种离子液体凝胶聚合物电解质由于液体相的均匀分布而具有疏松的结构. 采用电化学阻抗、计时电流法、线性扫描伏安法测试了电解质的离子电导率、锂离子迁移数和电化学窗口. 室温下离子液体凝胶聚合物电解质的离子电导率和锂离子迁移数分别是0.79 mS/cm和0.71,电化学窗口为0~5.1 Vvs. Li+/Li. 电池性能测试表明,这种离子液体凝胶聚合物电解质在Li/LiFePO4电池中是稳定的,放电容量在30、75和150mA/g倍率下分别为135、117和100 mAh/g,电池经100个循环后容量保持在100%而几乎没有衰减.

关 键 词:PP13TFSI,P(VdF-HFP),锂离子电池,离子液体,聚合物电解质
收稿时间:4/7/2013 12:00:00 AM

Electrochemical Properties of PP13TFSI-LiTFSI-P(VdF-HFP) Ionic Liquid Gel Polymer Electrolytes (cited: 1)
Pei-xia Yang,Lei Liu,Jun Hou and Jin-qiu Zhang.Electrochemical Properties of PP13TFSI-LiTFSI-P(VdF-HFP) Ionic Liquid Gel Polymer Electrolytes (cited: 1)[J].Chinese Journal of Chemical Physics,2013,26(4):439-444.
Authors:Pei-xia Yang  Lei Liu  Jun Hou and Jin-qiu Zhang
Affiliation:School of Chemical Engineering and Technology, Harbin Institute of Technology, Harbin 150001, China;School of Chemical Engineering and Technology, Harbin Institute of Technology, Harbin 150001, China;School of Chemical Engineering and Technology, Harbin Institute of Technology, Harbin 150001, China;School of Chemical Engineering and Technology, Harbin Institute of Technology, Harbin 150001, China
Abstract:N-Methyl-N-propylpiperidiniumbis(trifluoromethanesulfonyl)imide (PP13TFSI), bis(triflu-oromethanesulfonyl)imide lithium salt (LiTFSI), and poly(vinylidene difluoride-co-hexafluoropropylene) (P(VdF-HFP)) were mixed and made into ionic liquid gel polymer electrolytes (ILGPEs) by solution casting. The morphology of ILGPEs was observed by scanning electron microscopy. It was found that the ILGPE had a loosened structure with liquid phase uniformly distributed. The ionic conductivity, lithium ion transference num- ber and electrochemical window were measured by electrochemical impedance spectroscopy, chronoamperometric and linear sweep voltammetry. The ionic conductivity and lithium ion transference number of this ILGPE reached 0.79 mS/cm and 0.71 at room temperature, and the electrochemical window was 0 to 5.1 V vs. Li+/Li. Battery tests indicated that the ILGPE is stable when being operated in Li/LiFePO4 batteries. The discharge capacity maintained at about 135, 117, and 100 mAh/g at 30, 75, and 150 mA/g rates, respectively. The capacity retentions were almost 100% after 100 cycles without little capacity fading.
Keywords:Lithium ion battery  Ionic liquid  Polymer electrolyte  N-Methyl-N-propylpiperidiniumbis(trifluoromethanesulfonyl)imide  Poly(vinylidene difluoride-co-hexa fluoropropylene)
点击此处可从《化学物理学报》浏览原始摘要信息
点击此处可从《化学物理学报》下载全文
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司    京ICP备09084417号-23

京公网安备 11010802026262号