Probing the tribological behaviors in water of novel poly(phthalazione ether sulfone ketone) and its composites based on the state of aggregation and the microstructure |
| |
| Authors: | Fengxiang Cao Jianzhang Wang Fengyuan Yan |
| |
| Affiliation: | 1. State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, China;2. University of Chinese Academy of Sciences, Beijing, China |
| |
| Abstract: | In this paper, novel poly(phthalazione ether sulfone ketone) (PPESK) and its composites reinforced with carbon fibers (CFs) were prepared, and their tribological behaviors in pure and sea water were comparatively investigated. Affected by the noncoplanar twisted aromatic structure in the molecular skeleton, the aggregation of the macromolecular chain in PPESK was amorphous, resulting in very high water absorption of PPESK matrix. The invading water molecules led to a sharp decrease in the hardness of PPESK surface, resulting in very high wear rate of PPESK in water. Although CF/PPESK composites had higher water absorption than pure PPESK, their wear processes in water were no longer dominated by high water absorption but by the load‐carrying effect of CFs, ascribed to the good CF/PPESK interfacial adhesion. Therefore, CF/PPESK composites exhibited very low wear rates in the order of 10?7 mm3/Nm in water, which decreased with the CF content increasing until the content of CFs reached 50%. The results revealed that the most critical factor determining the wear behavior of a fiber‐reinforced polymer composite sliding in water is the fiber/matrix interface but not the water absorption of the polymer matrix. Copyright © 2017 John Wiley & Sons, Ltd. |
| |
| Keywords: | fibers polymer‐matrix composites wear hardness testing |
|
|