| 载银羟基磷灰石抗菌粉体和陶瓷的制备及抗菌性能 |
| Preparation and Antibacterial Property of Ag-doped Hydroxyapatite Antibacterial Powders and Antibacterial Ceramic |
|
| 摘要: 采用水热法一步合成载银羟基磷灰石抗菌粉体(Ag-HA),并将其应用于抗菌陶瓷的制备。研究结果表明水热条件下HA实际载银量与AgNO3加入量存在较好的线性关系。XRD和TEM分析结果显示Ag-HA与HA具有相同的晶体结构,水热条件下Ag 取代Ca2 在HA晶体中的位置,生成AgxCa10-x(PO4)6(OH)2。Ag-HA长度随Ag 掺入量的增加而增大,当Ag 掺入量增加至1.50%时,Ag-HA由棒状生长为晶须状。选择4.50%Ag-HA作为抗菌粉体,其掺入量为9wt%时,陶瓷的抗菌率＞99.9%,此时釉料中Ag3PO4含量为0.56%,低于目前研究中釉料中Ag3PO4添加量(2-4wt%),不但在一定程度上解决了抗菌陶瓷产品成本较高的问题,而且满足JC/T 897-2002(抗菌陶瓷制品抗菌性能)对抗菌陶瓷抗菌性能的要求。 |
| 关键词: 银 羟基磷灰石 水热合成 抗菌 陶瓷 |
| 基金项目: 国家自然科学基金 |
| Abstract: Silver doped hydroxyapatite antimicrobial powders were synthesized by one-step reaction, then it was used for preparing antibacterial ceramic. The experimental results show that there was a significant linear correlation between silver content of HA and quantity of silver nitrate at hydrothermal condition. The XRD patterns and TEM photos indicate that HA and Ag-HA have the same crystal structure, and Ca2 in HA crystals is displaced by Ag and AgxCa10-x(PO4)6(OH)2 was produced at hydrothermal condition. The length of Ag-HA antimicrobial powders increases with the increase of content of Ag in Ag-HA. Ag-HA antimicrobial powders went from sticks to whisker when the contents of Ag in Ag-HA exceeds 1.5%. 4.50%Ag-HA was selected as antimicrobial powders, an antibacterial rate of antibacterial ceramic is above 99.9%. and at this point, the mass fraction of Ag3PO4 in antimicrobial tglazes is 0.56%, which was far below 2-4% of Ag3PO4 in antimicrobial tglazes of ongoing research. This technology can not only reduce the cost of producing antibacterial ceramic, but also meet JC/T 897-2002 demands for antibacterial properties of antibacterial ceramic. |
| Keywords: Ag HA hydro-thermal method Antibacterial property Ceramic |
| 投稿时间：2013-01-04 修订日期：2013-06-26 |
| 摘要点击次数: 14 |
| 全文下载次数: 1 |
|
| 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|